Hard alloy tool

A cemented carbide and tool technology, applied in the field of tool processing, can solve problems such as unstable tool performance, and achieve the effects of avoiding grain aggregation, improving strength and fracture toughness, and being easy to form.

Inactive Publication Date: 2018-03-13
无锡市锦润合金工具有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In view of this, a cemented carbide cutting tool provided by the present invention can effectively solve the problem of unstable performance of the cutting tool produced by the existing cemented carbide cutting tool, and effectively improve the hardness and toughness of the cutting tool

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A cemented carbide cutting tool is composed of the following raw materials in parts by weight: 65-78 parts of hard phase, 10-12 parts of binder phase, 6-8 parts of inhibiting phase, and 2-4 parts of hardening phase;

[0023] The hard phase is composed of the following raw materials in mass percentage: 16-18% tungsten carbide, 3-5% tantalum carbide, 0.8-1.2% niobium carbide, 2.5-3.0% titanium carbide, 0.6-0.8% neodymium, and the balance is silicon carbide;

[0024] The binder phase is composed of the following raw materials in mass percentage: 4-8% aluminum nickel oxide, 24-32% cobalt, and the balance is hydroxyl iron powder;

[0025] The inhibiting phase is composed of the following raw materials in mass percentage: 3-6% niobium carbide, 10-15% thallium carbide, 10-15% graphene, and the balance is vanadium carbide;

[0026] The hardening phase is composed of the following raw materials in mass percentage: 60-70% chromium carbide, 12-18% titanium dioxide, and the balanc...

Embodiment 2

[0032] A cemented carbide cutting tool is composed of the following raw materials in parts by weight: 65-78 parts of hard phase, 10-12 parts of binder phase, 6-8 parts of inhibiting phase, and 2-4 parts of hardening phase;

[0033] The hard phase is composed of the following raw materials in mass percentage: 16-18% tungsten carbide, 3-5% tantalum carbide, 0.8-1.2% niobium carbide, 2.5-3.0% titanium carbide, 0.6-0.8% neodymium, and the balance is silicon carbide;

[0034] The binder phase is composed of the following raw materials in mass percentage: 4-8% aluminum nickel oxide, 24-32% cobalt, and the balance is hydroxyl iron powder;

[0035] The inhibiting phase is composed of the following raw materials in mass percentage: 3-6% niobium carbide, 10-15% thallium carbide, 10-15% graphene, and the balance is vanadium carbide;

[0036] The hardening phase is composed of the following raw materials in mass percentage: 60-70% chromium carbide, 12-18% titanium dioxide, and the balanc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

A cemented carbide cutting tool provided by the present invention is mainly characterized in that it consists of the following raw materials in parts by weight: 65-78 parts of hard phase, 10-12 parts of binder phase, 6-8 parts of inhibiting phase, 2-4 parts hardened phase. The cemented carbide cutter provided by the invention overcomes the defects of the prior art, has a simple manufacturing process, and effectively improves the hardness, strength and toughness of the cemented carbide cutter.

Description

technical field [0001] The invention belongs to the technical field of tool processing, and in particular relates to a cemented carbide tool. Background technique [0002] Because of its high hardness and wear resistance, cemented carbide is widely used to make wear-resistant parts, cutting tools, molds, mining tools, geological drilling tools, oil extraction tools, structural parts, high temperature and high pressure cylinders Body and mechanical seal parts, etc. At present, the cutting speed of cemented carbide cutting tools is hundreds of times higher than that of carbon steel, and 4-7 times higher than that of high-speed steel. However, they generally have the problems of low bending strength, poor impact toughness, high brittleness and easy wear. To solve the above problems, most of the cemented carbide tools are heat treated. The heat treatment of an existing cemented carbide tool adopts salt bath quenching or oil quenching, and then tempering treatment process, alth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C29/02C22C1/05C22C1/10B22F5/00
CPCC22C29/02B22F5/00B22F2005/001C22C1/051C22C29/005
Inventor 罗跃进
Owner 无锡市锦润合金工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products