Poured salt core for casting and preparation method thereof
The technology of salt core and edible salt is applied in the fields of salt core casting, casting salt core and preparation thereof, which can solve the problems of variability of salt core, simple and single shape, difficulty in pressurization, etc., and achieves simplified preparation process and molding effect. good, productive results
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0029] Example 1: A casting salt core for casting, which is composed of edible salt, reinforcing agent, binder, auxiliary agent and filler; the reinforcing agent includes aluminum oxide, mullite, short asbestos wool, and glass fiber; Binders include kaolin, calcium carbonate, glass water; supplements include potassium chloride, sodium fluorosilicate; filler is sodium carbonate, the above ingredients are 50kg of edible salt, aluminum oxide, mullite, short asbestos wool, 5kg each of glass fiber, kaolin, calcium carbonate, glass water, potassium chloride and sodium silicate, and 6kg of sodium carbonate.
[0030] A method for preparing a cast salt core for casting, including the following steps: putting 80 mesh edible salt into a ceramic crucible and heating it to melt; mixing 5 kg each of aluminum oxide, mullite, short asbestos wool, and glass fiber uniformly , Pour into the ceramic crucible; mix 5kg each of kaolin, calcium carbonate, and glass water into the ceramic crucible; mix 5...
Example Embodiment
[0032] Embodiment 2: A casting salt core for casting, which is composed of edible salt, reinforcing agent, binder, auxiliary agent and filler. The reinforcing agent includes aluminum oxide, mullite, short asbestos wool, and glass fiber; Binders include kaolin, calcium carbonate, glass water; supplements include potassium chloride, sodium fluorosilicate; filler is sodium carbonate, the above ingredients are 50kg of edible salt, aluminum oxide, mullite, short asbestos wool, The amount of glass fiber is 6kg each, the amount of kaolin, calcium carbonate, and glass water is 4kg, potassium chloride and sodium silicate are each 5kg, and sodium carbonate is 7kg.
[0033] A method for preparing a cast salt core for casting, including the following steps: putting 50 kg of 80 mesh edible salt into a ceramic crucible and heating it to melt; each 6 kg of alumina, mullite, short asbestos wool and glass fiber Mix well and pour into the ceramic crucible; mix 4kg each of kaolin, calcium carbonate...
Example Embodiment
[0035] Example 3: A castable salt core for casting, consisting of edible salt, reinforcing agent, binder, auxiliary agent and filler. The reinforcing agent includes aluminum oxide, mullite, short asbestos wool, and glass fiber; Binders include kaolin, calcium carbonate, glass water; supplements include potassium chloride, sodium fluorosilicate; filler is sodium carbonate, the above ingredients are 50kg of edible salt, aluminum oxide, mullite, short asbestos wool, The amount of glass fiber is 4.5kg each, the amount of kaolin, calcium carbonate, glass water is 6kg each, potassium chloride, sodium silicate are each 6kg, and sodium carbonate is 6kg.
[0036] A method for preparing a cast salt core for casting, including the following steps: putting 50 kg of 80 mesh edible salt into a ceramic crucible and heating it to melt; each 4.5 of alumina, mullite, short asbestos wool and glass fiber Kg mixed uniformly, pour into the ceramic crucible; mix 6kg each of kaolin, calcium carbonate, a...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap