Harmonic and stray electromagnetic radiation restraining material and preparation method thereof
An electromagnetic radiation and stray technology, applied in chemical instruments and methods, other chemical processes, etc., can solve the problems of reducing the operation stability of neighboring electronic equipment, unfavorable working performance, electronic device interference, etc., to meet the requirements of harmonic and electromagnetic The need for radiation suppression, the impact of reduced operating performance, the effect of large conformity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0028] Example 1
[0029] Embodiments of the present invention provide a harmonic and stray electromagnetic radiation suppression material and a preparation method thereof, which specifically include:
[0030] In parts by weight, 25 parts of polyurethane rubber, 2 parts of vulcanizing agent, 1 part of antifungal agent, 2 parts of anti-aging agent and 25 parts of mixed solvent of xylene, butyl acetate, n-butanol and cyclohexanone were added to In the beaker, heat and stir in a water bath until the mixture is uniform, and then add 70 parts of iron-silicon-aluminum powder to fully mix the iron-silicon aluminum powder in the glue solution, then grind the material to a fineness of less than 100 μm, cast and dry to obtain a thickness of 0.08 μm. The thin green embryos with a thickness of mm are superimposed and placed in the mold and are heated and pressurized by a flat vulcanizer to obtain a harmonic and stray electromagnetic radiation suppression material with a thickness of 1.6mm...
Example Embodiment
[0031] Example 2
[0032] Embodiments of the present invention provide a harmonic and stray electromagnetic radiation suppression material and a preparation method thereof, which specifically include:
[0033] In parts by weight, 20 parts of polyurethane rubber, 3 parts of vulcanizing agent, 2 parts of antifungal agent, 2 parts of anti-aging agent and 27 parts of mixed solvent of xylene, butyl acetate, n-butanol and cyclohexanone were added to In the beaker, heat and stir in a water bath until the mixture is uniform, and then add 68 parts of iron-silicon-aluminum powder to fully mix the iron-silicon aluminum powder in the glue solution, and then grind the material to a fineness of less than 100 μm, cast and dry to obtain a thickness of 0.08mm. Thick and thin green embryos are superimposed and placed in the mold and heated and pressurized by a flat vulcanizer to obtain a harmonic and stray electromagnetic radiation suppression material with a thickness of 1.6mm. The processing ...
Example Embodiment
[0034] Example 3:
[0035] Embodiments of the present invention provide a harmonic and stray electromagnetic radiation suppression material and a preparation method thereof, which specifically include:
[0036] In parts by weight, a total of 22 parts of polyurethane rubber and EPDM rubber, 4 parts of vulcanizing agent, 1 part of mildew inhibitor, 3 parts of anti-aging agent and 27 parts of xylene, butyl acetate, n-butanol, cyclic The mixed solvent of hexanone is added to the beaker, heated and stirred in a water bath until the mixture is uniform, and then 75 parts of iron-silicon-aluminum powder are added to fully mix the iron-silicon aluminum powder in the glue solution, and then the material is ground to a fineness of less than 100 μm, and casting is carried out. , drying to obtain a thin green embryo with a thickness of 0.08mm, superimposed and placed in a mold, and heated and pressurized by a flat vulcanizer to obtain a harmonic and stray electromagnetic radiation suppress...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap