Preparation method for automobile instrument board with high impact strength

A car dashboard, high impact resistance technology, applied in building components, building insulation materials, buildings, etc., can solve the problems affecting the appearance and use of car interiors, low impact strength, etc., and achieve excellent low temperature impact strength and impact strength High, good mutual compatibility effect

Inactive Publication Date: 2018-05-15
QUANJIAO XIANGRUI PLASTIC
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, the plastic material used for the car dashboard body has a technical problem of low impact strength, which affects the appearance and use of the car interior, which needs to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing a high-impact-strength automobile instrument panel, comprising the steps of:

[0021] S1. After pulverizing 15kg of quartz sand, add 18kg of rosin-modified phenolic resin, heat up to 65°C and stir for 25 minutes, continue to add 4kg of epoxy soybean oil-modified phenolic resin, heat up to 165°C and stir for 10 minutes to obtain a quartz sand composite;

[0022] S2. Mix 15kg of quartz sand compound, 2kg of zirconia microspheres, 5kg of sepiolite powder, 4kg of calcined kaolin, 8kg of asphalt granules, 1kg of sodium lignosulfonate, and 2kg of cocamidopropyl betaine, and heat up to 85°C for stirring 10min, stirring speed is 5000r / min, obtains premix b;

[0023] S3. Mix 100kg of acrylonitrile-butadiene-styrene copolymer and 15kg of polypropylene, heat up to 140°C and stir for 5min at a stirring speed of 1800r / min, then add 10kg of premix b and 2kg of dicumyl peroxide , 1kg1,3-bis(tert-butylperoxyisopropyl)benzene, 2kg titanate coupling agent, heated ...

Embodiment 2

[0025] A method for preparing an automobile instrument panel with high impact resistance, comprising the steps of:

[0026] S1. After crushing 35kg of quartz sand, add 10kg of rosin-modified phenolic resin, heat up to 85°C and stir for 15 minutes, continue to add 8kg of epoxy soybean oil-modified phenolic resin, heat up to 125°C and stir for 20 minutes to obtain a quartz sand composite;

[0027] S2. Mix 5kg of quartz sand compound, 5kg of zirconia microspheres, 1kg of sepiolite powder, 10kg of calcined kaolin, 2kg of asphalt granules, 2kg of sodium lignosulfonate, and 1kg of cocamidopropyl betaine, and heat up to 95°C for stirring 5min, stirring speed is 5400r / min, obtains premix b;

[0028] S3. Mix 60kg of acrylonitrile-butadiene-styrene copolymer and 25kg of polypropylene, heat up to 130°C and stir for 12min at a stirring speed of 1500r / min, then add 20kg of premix b and 1kg of dicumyl peroxide , 2kg of 1,3-bis(tert-butylperoxyisopropyl)benzene, 1kg of titanate coupling age...

Embodiment 3

[0030] A method for preparing an automobile instrument panel with high impact resistance, comprising the steps of:

[0031] S1. After pulverizing 20kg of quartz sand, add 16kg of rosin-modified phenolic resin, heat up to 70°C and stir for 22 minutes, continue to add 5kg of epoxy soybean oil-modified phenolic resin, heat up to 155°C and stir for 12 minutes to obtain a quartz sand composite;

[0032] S2, mix 12kg quartz sand compound, 3kg zirconia microspheres, 4kg sepiolite powder, 6kg calcined kaolin, 6kg pitch granules, 1.2kg sodium lignosulfonate, 1.7kg cocamidopropyl betaine, heat up to 88 Stir at ℃ for 8 minutes, and the stirring speed is 5100r / min, to obtain premix b;

[0033] S3. Mix 90kg of acrylonitrile-butadiene-styrene copolymer and 18kg of polypropylene, heat up to 137°C and stir for 8min at a stirring speed of 1700r / min, then add 12kg of premix b and 1.8kg of diisopropyl peroxide Benzene, 1.3kg of 1,3-bis(tert-butylperoxyisopropyl)benzene, and 1.6kg of titanate co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Bending strengthaaaaaaaaaa
Flexural modulusaaaaaaaaaa
Densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for an automobile instrument board with high impact strength. The preparation method comprises the following steps of crushing quartz sand, then adding rosin modified phenolic resin, carrying out heating and stirring, continuously adding epoxidized soybean oil modified phenolic resin and carrying out heating and stirring so as to obtain a quartz sand compound; mixing the quartz sand compound, zirconium oxide microspheres, sepiolite powder, calcined kaolin, asphalt particles, sodium lignin sulfonate and cocamidopropyl betaine and carrying out heatingand stirring so as to obtain premix b; and mixing ABS resin and polypropylene, carrying out heating and stirring, then adding the premix b, dicumyl peroxide, 1,3-bis[3-(tert-butylperoxy)propyl]benzene and a titanate coupling agent, carrying out heating and stirring, heating a mixture to a molten state, carrying out extrusion and carrying out hot-press forming so as to obtain the automobile instrument board with high impact strength. The preparation method for the automobile instrument board with high impact strength has the advantages of being environment-friendly in process and less in pollution, and the obtained automobile instrument board is high in structural strength, high in impact strength, good in low-temperature brittleness and good in anti-aging effect.

Description

technical field [0001] The invention relates to the technical field of automobile instrument panels, in particular to a method for preparing an automobile instrument panel with high impact resistance. Background technique [0002] The dashboard is one of the most important parts of a car's body, located directly in front of the driver. Dashboards can be divided into hard plastic dashboards, blister dashboards and semi-rigid foam soft dashboards according to comfort. The dashboard body is made of hard plastic dashboards by injection molding because of its advantages of simple process and low investment. It is widely used, especially in low-end cars. However, at present, the plastic material used for the car dashboard body has a technical problem of low impact strength, which affects the aesthetics and use of the car interior, and needs to be solved urgently. Contents of the invention [0003] Based on the technical problems existing in the background technology, the prese...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L55/02C08L23/12C08L61/14C08L95/00C08L97/00C08K13/06C08K9/04C08K3/36C08K7/18C08K3/34C08K5/14
CPCC08L55/02C08K2201/011C08L2201/08C08L2205/025C08L2205/035C08L23/12C08L61/14C08L95/00C08L97/005C08K13/06C08K9/08C08K3/36C08K7/18C08K3/346C08K5/14
Inventor 刘仕明
Owner QUANJIAO XIANGRUI PLASTIC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products