Root resistant waterproof coiled material for plantation roofs and production method thereof

A waterproof membrane and root puncture-resistant technology, which is applied in the direction of chemical instruments and methods, hydraulic material layered products, layered products, etc. In order to avoid problems such as low tensile strength and cumbersome production process, it can achieve the effects of good mold resistance, enhanced chemical affinity, and increased lipophilicity.

Active Publication Date: 2018-05-22
GUANGXI WUXUAN JINPAI WATERPROOF MATERIAL SCI & TECH CO LTD
View PDF14 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the tensile strength of the waterproof membrane is not high; the integrity of the laying is also poor; after construction, there is a great risk of leakage; the construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Root resistant waterproof coiled material for plantation roofs and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] Example 1

[0027] A root puncture-resistant waterproofing membrane for planting roofs. The waterproofing membrane has a five-layer structure, from top to bottom: upper surface isolation layer, upper modified asphalt layer, tire base layer, lower modified asphalt layer and Lower surface isolation layer;

[0028] Both the upper surface isolation layer and the lower surface isolation layer are polyethylene film; the tire base layer is copper foil tire base;

[0029] The upper modified bitumen layer and the lower modified bitumen layer are made of modified bitumen, and the modified bitumen is made of the following parts by weight: 90# petroleum asphalt 70 parts; naphthenic oil 20 parts; SBS modified 10 parts of sex agent; 5 parts of SIS styrene-isoprene-styrene block copolymer; 10 parts of phenolic lignin; 1 part of polyvinyl alcohol; 2 parts of γ-ethylenediaminotriethoxysilane; Chemical root inhibitor copper oxide powder 1 part; tributyl citrate 1 part; antioxidant propyl gall...

Example Embodiment

[0038] Example 2

[0039] A root puncture-resistant waterproofing membrane for planting roofs. The waterproofing membrane has a five-layer structure, from top to bottom: upper surface isolation layer, upper modified asphalt layer, tire base layer, lower modified asphalt layer and Lower surface isolation layer;

[0040] The upper surface isolation layer is coated sand, the lower surface isolation layer is polyethylene film; the tire base layer is copper foil tire base;

[0041] The upper modified bitumen layer and the lower modified bitumen layer are made of modified bitumen, and the modified bitumen is made of the following parts by weight of raw materials: 90# petroleum asphalt 73 parts; naphthenic oil 22 parts; SBS modified 12 parts of sex agent; 9 parts of SIS styrene-isoprene-styrene block copolymer; 13 parts of phenolic lignin; 1.5 parts of polyvinyl alcohol; 3 parts of γ-ethylenediaminotriethoxysilane; Chemical root inhibitor copper oxide powder 2 parts; tributyl citrate 2 pa...

Example Embodiment

[0050] Example 3

[0051] A root puncture-resistant waterproofing membrane for planting roofs. The waterproofing membrane has a five-layer structure, from top to bottom: upper surface isolation layer, upper modified asphalt layer, tire base layer, lower modified asphalt layer and Lower surface isolation layer;

[0052] The upper surface isolation layer is a PET isolation film, the lower surface isolation layer is a polyethylene film; the tire base layer is a copper foil tire base;

[0053] The upper modified bitumen layer and the lower modified bitumen layer are made of modified bitumen. The modified bitumen is made of the following raw materials by weight: 90# petroleum asphalt 75 parts; naphthenic oil 25 parts; SBS modified 15 parts of sex agent; 10 parts of SIS styrene-isoprene-styrene block copolymer; 15 parts of phenolic lignin; 2 parts of polyvinyl alcohol; 4 parts of γ-ethylenediaminotriethoxysilane; Chemical root inhibitor copper oxide powder 3 parts; tributyl citrate 3 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a root resistant waterproof coiled material for plantation roofs and a production method thereof. The waterproof coiled material comprises five layers from top to bottom: an upper surface isolation layer, an upper modified asphalt layer, a base layer, a lower modified asphalt layer, and a lower surface isolation layer. The upper modified asphalt layer and the lower modified asphalt layer are prepared from modified asphalt. The properties of provided root resistant waterproof coiled material such as root resistant performance, tear resistant performance, caking property, waterproof property, anti-aging property, and the like, are largely improved. The elongation at break is high. The manufacturing technology is simple. The shortages that the manufacturing of waterproof coiled materials is tedious and the bonding performance is weak are overcome. The provided waterproof coiled material is used for buildings. The adhesive force between the waterproof coiled material and the surface of buildings is great. The waterproof effect and root resistant performance are good. The water leakage phenomenon is prevented effectively. The coiled material has the waterproof and root resistant functions.

Description

technical field [0001] The invention relates to a building waterproof material, in particular to a root puncture-resistant waterproof coiled material for planting roofs and a production method thereof, belonging to the field of waterproof chemical materials. Background technique [0002] With the improvement of construction technology, the demand for waterproof materials for construction projects is also increasing, and the quality requirements are also getting higher and higher. With the progress of various engineering constructions, the problem of water seepage and leakage in roofs, floors, and basements has always troubled people. As a result, waterproof projects have emerged as the times require. Various waterproof materials emerge in endlessly. The waterproof industry is booming, and waterproof membranes are widely used in the construction industry. Among them, it is one of the important building materials. [0003] With the development of the city, both commercial bui...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B13/12B32B13/06B32B15/20B32B27/06B32B27/36B32B27/32C08L95/00C08L91/00C08L53/02C08L29/04C08L1/28C08L97/00C08K13/06C08K9/04C08K3/26C08K5/11C08K5/544C08K5/132C08K3/22
CPCB32B13/06B32B13/12B32B15/20B32B27/06B32B27/32B32B27/36B32B2307/558B32B2307/5825B32B2307/73B32B2419/06C08K2003/2248C08K2003/265C08K2201/011C08L95/00C08L2205/035C08L91/00C08L53/02C08L29/04C08L1/286C08L97/00C08K13/06C08K9/04C08K3/26C08K5/11C08K5/544C08K5/132C08K3/22
Inventor 刘拥军刘永刚郑新国郑爱彬候尚春
Owner GUANGXI WUXUAN JINPAI WATERPROOF MATERIAL SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap