Graphene superconducting far infrared heating paste

A far-infrared heating and graphene technology, applied in the field of graphene, can solve problems such as insufficient lifespan, achieve high heating power, ensure service life, and ensure safety

Inactive Publication Date: 2018-07-06
山东中亿烯创新材料科技有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the slurry generated by graphene has insufficient life span

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The present invention proposes a graphene superconducting far-infrared heating paste, whose raw materials are formulated as follows by weight: 50 parts of graphene, 20 parts of graphite, 20 parts of organic carrier, 12 parts of synthetic resin, 12 parts of magnetic rubber, metal mixed 12 parts of powder, 5 parts of environmentally friendly high temperature resistant conductive adhesive, 3 parts of corrosion resistant agent, 3 parts of antistatic agent, 3 parts of catalyst, and 1 part of bishydroxyethyl bishydroxypropyl stearyl ammonium chloride.

[0020] The metal mixed powder is a mixture of copper powder, aluminum powder, nickel powder and silver powder, and the molar mass ratio of copper powder, aluminum powder, nickel powder and silver powder is 5:2:1:0.2.

[0021] The organic vehicle is a mixture of methylstyrene resin, nano-silica cellulose acetate butyrate and additives, and the molar mass ratio of methylstyrene resin, nano-silica cellulose acetate butyrate and ad...

Embodiment 2

[0023] The present invention proposes a graphene superconducting far-infrared heating paste, whose raw materials are formulated as follows by weight: 55 parts of graphene, 23 parts of graphite, 23 parts of organic carrier, 13 parts of synthetic resin, 13 parts of magnetic rubber, metal mixed 13 parts of powder, 6 parts of environmentally friendly high temperature resistant conductive adhesive, 3.5 parts of corrosion resistant agent, 3.5 parts of antistatic agent, 3.5 parts of catalyst, and 1.5 parts of bishydroxyethyl bishydroxypropyl stearyl ammonium chloride.

[0024] The metal mixed powder is a mixture of copper powder, aluminum powder, nickel powder and silver powder, and the molar mass ratio of copper powder, aluminum powder, nickel powder and silver powder is 5:2:1:0.2.

[0025] The organic vehicle is a mixture of methylstyrene resin, nano-silica cellulose acetate butyrate and additives, and the molar mass ratio of methylstyrene resin, nano-silica cellulose acetate butyra...

Embodiment 3

[0027] The present invention proposes a graphene superconducting far-infrared heating paste. The formula of its raw materials by weight is as follows: 60 parts of graphene, 25 parts of graphite, 25 parts of organic carrier, 14 parts of synthetic resin, 14 parts of magnetic rubber, metal mixed 14 parts of powder, 7 parts of environmentally friendly high temperature resistant conductive adhesive, 4 parts of corrosion resistant agent, 4 parts of antistatic agent, 4 parts of catalyst, and 3 parts of bishydroxyethyl bishydroxypropyl stearyl ammonium chloride.

[0028] The metal mixed powder is a mixture of copper powder, aluminum powder, nickel powder and silver powder, and the molar mass ratio of copper powder, aluminum powder, nickel powder and silver powder is 5:2:1:0.2.

[0029] The organic vehicle is a mixture of methylstyrene resin, nano-silica cellulose acetate butyrate and additives, and the molar mass ratio of methylstyrene resin, nano-silica cellulose acetate butyrate and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses graphene superconducting far infrared heating paste. The graphene superconducting far infrared heating paste is prepared from, by weight, 50-70 parts of graphene, 20-30 parts of graphite, 20-30 parts of organic carrier, 12-16 parts of synthetic resin, 12-16 parts of magnetic rubber, 12-16 parts of metal mixed powder, 5-9 parts of environment-friendly high-temperature-resistant conductive binder, 3-5 parts of anticorrosion agent, 3-5 parts of antistatic agent, 3-5 parts of catalyst and 1-3 parts of dihydroxyethyl dihydroxypropyl stearin ammonium chloride. The graphene serves as the raw material, and the graphite is properly added, so that the heating paste is good in comprehensive performance, the resistance is moderate, the heating power is high, the conductivity ofthe heating paste can be effectively enhanced, and therefore the service life of the paste is guaranteed.

Description

technical field [0001] The invention relates to the technical field of graphene, in particular to a graphene superconducting far-infrared heating paste. Background technique [0002] The manufacture and application of graphene is an emerging industry. This new material has excellent mechanical, electrical, and thermal properties, and will have important applications in energy storage, electrical conduction, heat conduction, and mechanical enhancement. The company is mainly engaged in the development of large-scale production and preparation of high-quality thin-layer graphene, as well as a series of products such as powders, slurries, coatings, and inks based on high-quality thin-layer graphene for electrical conduction, heat conduction, and energy storage applications. The main customers are concentrated in lithium batteries, super capacitors and other energy storage companies, conductive and antistatic polymer composite material development and processing companies, mobile...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H05B3/14
CPCH05B3/14
Inventor 黄治鸿夏有良
Owner 山东中亿烯创新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap