Self-drying waterborne ceramic coating and preparation method thereof

A ceramic coating, self-drying technology, applied in fireproof coatings, alkali metal silicate coatings, coatings, etc., can solve the problems of acid resistance, weather resistance, human body damage, etc., and achieve strong non-stickiness and good weather resistance , good self-cleaning effect

Inactive Publication Date: 2018-07-27
GUANGDONG FRUTO NEW MATERIALS CO LTD
View PDF0 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are generally three types of ceramic coatings. The first is general zinc-rich coatings. This type of coating has low temperature resistance and loses its protective effect when exposed to high temperatures. Dark color, the second is PTFE fluorocarbon coating, this kind of coating is not environmentally friendly, once the coating is heated, it will produce a poisonous gas, which changes color quickly and is not safe. It will produce open flames and smoke when exposed to high temperatures of 300°C, which will harm the environment and human body. The damage is great, and it is not energy-saving. The sintering temperature must be above 380 ° C, and it takes more than 30 minutes, and the self-cleaning property is poor, and it is not anti-fouling. It is not environmentally friendly, pollutes the environment, is easy to oxidize, and is not weather-resistant, acid-resistant, salt-resistant, and energy-saving. It is usually expensive to maintain, and it is not temperature-resistant and flame-retardant. Open flames, dense smoke, easy to change color, crack and peel off when the temperature is above 50°C, and the surface hardness is low, easy to scratch

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] Specific embodiments of the present invention will be further described in detail below.

[0032] The present invention includes A solution and B solution, wherein,

[0033] A solution is made up of the component of following percentage by weight:

[0034] Silicate solution 40-50%, powder filler 10-20%, pigment filler 5-15%, anti-rust powder 1-10%, additive 1-5%, and the rest is solvent;

[0035] Solution B consists of the following components:

[0036] Siloxane 20-40%, silica gel solution 40-60%, and the rest are solvents.

[0037] The silicate solution is one or more mixtures of lithium silicate, potassium silicate, potassium titanate, sodium silicate, zinc silicate and titanate.

[0038] The powder filler is one or more mixtures of whisker silicon, kaolin, mica powder, precipitated barium sulfate and alumina fiber.

[0039] The pigment filler is one or more of titanium dioxide, mica red iron oxide, titanium yellow, iron blue, cadmium red, cadmium yellow, iron bla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a self-drying waterborne ceramic coating and a preparation method thereof. The self-drying waterborne ceramic coating is characterized by comprising a solution A and a solutionB, wherein the solution A is prepared from the following components in percentage by weight: 40-50% of silicate solution, 10-20% of powder filler, 5-15% of pigment filler, 1-10% of antirust powder, 1-5% of auxiliary and the balance of solvent; and the solution B is prepared from the following components: 20-40% of siloxane, 40-60% of silica gel solution and the balance of solvent.

Description

technical field [0001] The invention relates to the field of chemical industry, in particular to a self-drying water-based ceramic coating and a preparation method thereof. Background technique [0002] At present, there are generally three types of ceramic coatings. The first is general zinc-rich coatings. This type of coating has low temperature resistance and loses its protective effect when exposed to high temperatures. Its hardness is soft, its protection ability is poor, and its appearance is not good. Dark color, the second is PTFE fluorocarbon coating, this kind of coating is not environmentally friendly, once the coating is heated, it will produce a toxic gas, change color quickly, and is not safe, it will produce open flames and smoke when exposed to high temperatures of 300 ° C, which will harm the environment and human body The damage is great, and it is not energy-saving. The sintering temperature must be above 380°C, and it takes more than 30 minutes, and the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/04C09D1/00C09D7/61
CPCC09D1/04C09D1/00C09D5/18
Inventor 韩勇敢钟志敏李蕴雯
Owner GUANGDONG FRUTO NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products