A kind of method utilizing modified polysaccharide to prepare copper nanoparticles

A technology of copper nanoparticles and particles, which is applied in the direction of nanotechnology, nanotechnology, nanotechnology, etc. for materials and surface science, can solve the problems of large environmental hazards, reaction time, easy oxidation of copper nanoparticles, high price, etc., to achieve cost Inexpensive, mild reaction, good biocompatibility effect

Active Publication Date: 2019-07-16
UNIV OF SCI & TECH BEIJING
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to aim at the currently reported preparation method of copper nanoparticles, the reaction process requires the use of reagents that are harmful to the environment or expensive, the reaction process requires high temperature, long reaction time and the prepared copper nanoparticles are easy to oxidize To provide a method for preparing copper nanoparticles with low cost, environmental friendliness, easy operation and excellent oxidation resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method utilizing modified polysaccharide to prepare copper nanoparticles
  • A kind of method utilizing modified polysaccharide to prepare copper nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Modification of starch

[0025] Take a 250 ml round bottom flask, add 10 g of starch, 5 g of sodium periodate and 100 ml of deionized water in sequence, and stir for 12 hours in an oil bath at 37°C. Filter and wash with water 4 times, then place in a vacuum freeze dryer for 72 hours to obtain dry dialdehyde starch powder.

[0026] (2) Dissolution of dialdehyde starch

[0027] Get 2 grams of dialdehyde starch prepared in step (1) and place it in a beaker, add 90 milliliters of sodium hydroxide-urea solutions with mass fractions of 6% and 4%, respectively. After stirring at room temperature for 1 hour, freeze in a -20°C refrigerator for 12 hours, and then slowly thaw at room temperature to obtain a dialdehyde starch solution.

[0028] (3) Preparation of copper nanoparticles

[0029] The dialdehyde starch solution that 5 milliliters of steps (2) process obtains is added in the glass vial, then add 1 milliliter of 1 mg / ml polyethyleneimine solution, 1 milliliter conc...

Embodiment 2

[0031] (1) Modification of cellulose

[0032] Take a 250 ml round bottom flask, add 10 g of cellulose, 5 g of sodium periodate and 100 ml of deionized water in sequence, and stir for 12 hours in an oil bath at 37°C. Filter and wash 4 times with water, then place in a vacuum freeze dryer for 72 hours to obtain dry dialdehyde cellulose powder.

[0033] (2) Dissolution of dialdehyde cellulose

[0034] Take 1 gram of dialdehyde cellulose prepared in step (1) and place it in a beaker, and add 90 milliliters of sodium hydroxide-urea solutions with mass fractions of 7% and 12%, respectively. After stirring at room temperature for 1 hour, freeze in a -20°C refrigerator for 12 hours, and then slowly thaw at room temperature to obtain a dialdehyde starch solution.

[0035] (3) Preparation of copper nanoparticles

[0036] Add the dialdehyde cellulose solution obtained in milliliter step (2) into the glass vial, then add 1 milliliter of 5 mg / ml polyethyleneimine solution, 1 milliliter ...

Embodiment 3

[0038] (1) Modification of starch

[0039] Take a 250 ml round bottom flask, add 10 g of starch, 5 g of sodium periodate and 100 ml of deionized water in sequence, and stir for 12 hours in an oil bath at 37°C. Filter and wash with water 4 times, then place in a vacuum freeze dryer for 72 hours to obtain dry dialdehyde starch powder.

[0040] (2) Dissolution of dialdehyde starch

[0041] Get 3 grams of dialdehyde starch prepared in step (1) and place it in a beaker, add 90 milliliters of sodium hydroxide-urea solutions with mass fractions of 6% and 4%, respectively. After stirring at room temperature for 1 hour, freeze in a -20°C refrigerator for 12 hours, and then slowly thaw at room temperature to obtain a dialdehyde starch solution.

[0042] (3) Preparation of copper nanoparticles

[0043] The dialdehyde starch solution that 5 milliliters of steps (2) process obtains is added in the glass vial, then add the polyethylenimine solution of 1 milliliter 5 mg / ml, 1 milliliter c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to a method for preparing metallic copper nanoparticles, and particularly relates to a method for preparing copper nanoparticles with excellent oxidation resistance by using modified natural polysaccharides as reducing agents and amino-containing polymers as protective agents in a liquid phase. The aldehyde group is introduced into the starch chain skeleton through the oxidation of sodium periodate, and then the starch is dissolved in sodium hydroxide-urea solution to obtain a dialdehyde starch solution. The dialdehyde starch solution, copper sulfate pentahydrate and polyethyleneimine are sequentially added into the container, stirred and argon gas is introduced, and reacted for a period of time to obtain copper nanoparticles. The invention is simple in operation, low in cost, does not need high temperature conditions, does not need to use any toxic reagents, and is energy-saving and environment-friendly. At the same time, the as-prepared nanoparticles can be stored under ambient conditions for at least three months in dry powder form.

Description

technical field [0001] The invention relates to a method for preparing metal nanoparticles, in particular to a method for preparing copper nanoparticles with excellent oxidation resistance by using modified natural polysaccharides as reducing agents and amino-containing polymers as protective agents. Background technique [0002] Due to their nano-effects, metal nanoparticles exhibit special physical and chemical properties that traditional metal bulk materials do not have, so they are widely used in catalysis, sensing, optoelectronics, biomedicine and other fields. At present, the research on metal nanoparticles mainly focuses on gold, silver, platinum and other noble metal nanoparticles. Compared with gold, silver and other nanoparticles, copper nanoparticles also have excellent catalytic, optical, electrical, thermal and bactericidal properties, and have important applications in catalytic materials, electronic displays, light-transmitting conductive films, and bactericid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/24B22F1/00B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00B22F9/24B22F1/054
Inventor 李立东唐馥唐亮珍
Owner UNIV OF SCI & TECH BEIJING
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com