High strength light-weight concrete and preparation method thereof

A light-weight concrete and high-strength technology, applied in the field of building materials, can solve the problems of difficulty in meeting the performance index requirements of the construction industry for ceramsite concrete, poor thermal insulation effect, and insufficient light weight, etc., to achieve light weight, thermal insulation The effect of good performance and low equipment requirements

Inactive Publication Date: 2018-08-17
合肥金云新材料有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the high-strength ceramsite concrete on the market still has problems such as low strength, poor weather resistance, insufficient weight, poor thermal insulation effect, etc., and it is difficult to meet the performance requirements of the construction industry for ceramsite concrete.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A high-strength lightweight concrete, comprising the following components in parts by weight: 50 parts of cement, 30 parts of ceramsite, 25 parts of fly ash, 15 parts of fine sand, 10 parts of calcium carbonate, 20 parts of light-burned magnesium oxide, polypropylene 5 parts of fiber, 10 parts of micro silica fume, 5.5 parts of calcium monofluorophosphate, 10 parts of nano silicon dioxide, 12 parts of desulfurized gypsum, 7 parts of quartz sand, 4 parts of expanded vermiculite, 7 parts of sodium dodecyl sulfonate, 5 parts of functional aids and 90 parts of deionized water;

[0027] The functional auxiliary agent includes the following components in parts by weight: 3 parts of water reducer, 2 parts of thickener, 3 parts of foaming agent and 1 part of expansion agent.

[0028] Wherein, the ceramsite is a mixture of shale ceramsite and clay ceramsite, and its particle size is 5-15mm.

[0029] Wherein, the polypropylene fiber is a superfine fiber filament with a length of...

Embodiment 2

[0039] A high-strength lightweight concrete, comprising the following components in parts by weight: 40 parts of cement, 20 parts of ceramsite, 20 parts of fly ash, 10 parts of fine sand, 5 parts of calcium carbonate, 15 parts of light-burned magnesium oxide, polypropylene 2 parts of fiber, 5 parts of micro silica fume, 3 parts of calcium monofluorophosphate, 5 parts of nano silicon dioxide, 8 parts of desulfurized gypsum, 5 parts of quartz sand, 2 parts of expanded vermiculite, 4 parts of sodium dodecyl sulfonate, 2 parts of functional aids and 80 parts of deionized water.

[0040] The functional auxiliary agent includes the following components in parts by weight: 1 part of water reducer, 1 part of thickener, 2 parts of foaming agent and 0.4 part of expansion agent.

[0041] Wherein, the ceramsite is a mixture of gangue ceramsite and fly ash ceramsite, and its particle size is 5-15mm.

[0042] Wherein, the polypropylene fiber is a superfine fiber filament with a length of 1...

Embodiment 3

[0052]A high-strength lightweight concrete, comprising the following components in parts by weight: 60 parts of cement, 40 parts of ceramsite, 30 parts of fly ash, 20 parts of fine sand, 15 parts of calcium carbonate, 25 parts of light-burned magnesium oxide, polypropylene 8 parts of fiber, 15 parts of micro silica fume, 8 parts of calcium monofluorophosphate, 15 parts of nano silicon dioxide, 15 parts of desulfurized gypsum, 10 parts of quartz sand, 7 parts of expanded vermiculite, 10 parts of sodium dodecyl sulfonate, 8 parts of functional aids and 100 parts of deionized water.

[0053] The functional auxiliary agent includes the following components in parts by weight: 5 parts of water reducer, 3 parts of thickener, 4 parts of foaming agent and 1.6 parts of expansion agent.

[0054] Wherein, the ceramsite is a mixture of clay ceramsite and coal gangue ceramsite, and its particle size is 5-15mm.

[0055] Wherein, the polypropylene fiber is a superfine fiber filament with a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses high strength light-weight concrete, the concrete is prepared from the following components in parts by weight: 40 to 60 parts of cement, 20 to 40 parts of ceramsite, 20 to 30parts of coal ash, 10 to 20 parts of fine sand, 5 to 15 parts of calcium carbonate, 15 to 25 parts of light calcined magnesia, 2 to 8 parts of polypropylene fiber, 5 to 15 parts of microsilica fume, 3to 8 parts of calcium monofluorophosphate, 5 to 15 parts of nano silicon dioxide, 8 to 15 parts of desulphurization gypsum, 5 to 10 parts of quartz sand, 2 to 7 parts of expanded vermiculite, 4 to 10parts of sodium dodecyl sulfate, 2 to 8 parts functional agent and 80 to 100 parts of deionized water. The high strength light-weight concrete provided by the invention has the characteristics of light weight, high strength, good weather resistance, good heat-insulating property and the like, can meet index requirements of construction industry to ceramsite concrete performance and has better application prospect.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a high-strength lightweight concrete and a preparation method thereof. Background technique [0002] High-strength ceramsite concrete is a kind of light aggregate concrete. The strength range currently used is LC5.0-LC60. Due to its high strength, light bulk density, not easy to crack due to temperature difference, small self-shrinkage, good freeze-thaw resistance, after forming concrete Being able to form self-maintenance and other characteristics, it is one of the main energy-saving and environmental protection materials that are currently being promoted in the new century. Ceramsite concrete began to develop in my country in the 1960s, mainly used for thermal insulation materials and non-load-bearing structures. In the late 1990s, with the rapid development of foreign technology, it also gradually developed rapidly and has C50 grade high-strength ceramsite concrete....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/02C04B38/10
CPCC04B28/02C04B18/027C04B18/08C04B14/06C04B14/28C04B14/30C04B22/066C04B16/0633C04B18/146C04B22/16C04B14/062C04B22/145C04B14/204C04B24/20C04B2103/302C04B22/064C04B22/14C04B24/34C04B2103/0068C04B38/10C04B18/023C04B14/108
Inventor 谭群英
Owner 合肥金云新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap