A kind of lignin-filled foam slippers and preparation method thereof

A technology of lignin and slippers, applied in footwear, clothing, applications, etc., can solve the problems of poor comfort and hard materials, and achieve the effects of reducing plasticizer content, low equipment requirements, and stable cell size

Active Publication Date: 2020-11-13
NANJING TECH UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to provide a kind of lignin-filled foam slippers to solve the problems of relatively hard materials and poor comfort in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lignin-filled foam slippers and preparation method thereof
  • A kind of lignin-filled foam slippers and preparation method thereof
  • A kind of lignin-filled foam slippers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A kind of foamed slipper filled with lignin and its preparation method:

[0035] 32 parts of polyvinyl chloride resin,

[0036] 8 parts neoprene,

[0037] Hardwood lignin 15 parts,

[0038] 6 parts of calcium zinc stabilizer,

[0039] 2 parts polyethylene wax,

[0040] 1 part stearic acid,

[0041] 20 parts of epoxy soybean oil,

[0042] AC blowing agent 1 part,

[0043] 1 copy of ACR,

[0044] 6 parts of talcum powder,

[0045] Antioxidant 1010 5 parts,

[0046] 3 copies of color masterbatch.

[0047] Its preparation method comprises the following steps:

[0048] (1) take each raw material according to parts by weight;

[0049] (2) First, polyvinyl chloride resin, lignin and other fillers and additives are added to the kneader, and kneaded at 95 ° C for 12 minutes;

[0050] (3) The kneaded material is injection-molded at 180° C. through a single-screw injection molding machine.

Embodiment 2

[0052] A kind of foamed slipper filled with lignin and its preparation method:

[0053] 27 parts of polyvinyl chloride resin,

[0054] 9 parts of natural rubber,

[0055] 18 parts of cork lignin,

[0056] 6 parts of calcium zinc stabilizer,

[0057] 2 parts polyethylene wax,

[0058] 1 part stearic acid,

[0059] 17 parts of tributyl citrate,

[0060] AC blowing agent 1 part,

[0061] 1 copy of ACR,

[0062] Calcium carbonate 10 parts

[0063] Antioxidant 1010 5 parts,

[0064] 3 copies of color masterbatch.

[0065] Its preparation method comprises the following steps:

[0066] (1) take each raw material according to parts by weight;

[0067] (2) First, polyvinyl chloride resin, lignin and other fillers and additives are added to the kneader, and kneaded at 105 ° C for 15 minutes;

[0068] (3) The kneaded material is injection-molded at 195° C. through a single-screw injection molding machine.

Embodiment 3

[0070] A kind of foamed slipper filled with lignin and its preparation method:

[0071] 27 parts of polyvinyl chloride resin,

[0072] Butadiene rubber 9 parts,

[0073] 21 parts of herbal lignin,

[0074] 6 parts of organotin stabilizer,

[0075] 2 parts polyethylene wax,

[0076] 1 part stearic acid,

[0077] Dioctyl phthalate 16 parts,

[0078] AC blowing agent 1 part,

[0079] 1 copy of ACR,

[0080] 8 parts of talcum powder,

[0081] Antioxidant 1010 5 parts,

[0082] 3 copies of color masterbatch.

[0083] Its preparation method comprises the following steps:

[0084] (1) take each raw material according to parts by weight;

[0085] (2) First, polyvinyl chloride resin, lignin and other fillers and additives are added to the kneader, and kneaded at 105 ° C for 15 minutes;

[0086] (3) The kneaded material is injection-molded at 200° C. through a single-screw injection molding machine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses lignin-filled foaming slippers and a producing method thereof. The slippers contain 20 to 60 parts of polyvinyl chloride resin, 5 to 20 parts of rubber, 5 to 40 parts of lignin, 4 to 15 parts of a stabilizer, 1 to 7 parts of an external lubricant, 1 to 5 parts of an internal lubricant, 10 to 32 parts of a plasticizer, 1 to 9 parts of a foaming agent, 1 to 7 parts of a foaming regulator, 0 to 80 parts of a filler, 0 to 12 parts of an antioxidant, and 0 to 10 parts of color masterbatch. Compared with the prior art, the lignin-added polyvinyl chloride is subjected to foaming treatment so as to not only effectively decrease the content of the plasticizerbut also make the product soft and comfortable in texture, and possess good resilience and wear resistance. The methodprovided by the invention has an easy producing process, has low requirements for instruments, can save cost, and has good market expectation.

Description

technical field [0001] The invention belongs to the field of daily necessities, and in particular relates to a lignin-filled foamed slipper and a preparation method thereof. Background technique [0002] Slippers are a necessity in people's daily life. With the increasing pursuit of quality of life by consumers, the requirements for wearing comfort and antibacterial and deodorizing effects of slippers are becoming higher and higher. At the same time, more and more people pay attention to environmental protection and sustainability. The problem of sustainable development has brought new challenges to the research and development of sole materials. [0003] Lignin is the second largest biomass resource in the world after cellulose, but it has long been used as waste in the biorefinery industry and paper industry, which not only has a low recycling rate, but also causes serious environmental pollution. Lignin molecules have a unique hyperbranched polyphenol structure, which is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L11/00C08L7/00C08L9/00C08L97/00C08L91/00C08K5/09C08K3/34C08K5/134C08K13/02C08J9/10C08J9/00A43B1/14
CPCA43B1/14C08J9/0061C08J9/103C08J2203/04C08J2327/06C08J2407/00C08J2409/00C08J2411/00C08J2497/00C08K3/34C08K5/09C08K5/1345C08K13/02
Inventor 朱晨杰朱时祥李明应汉杰唐成伦陈勇柳东牛欢青高南吴菁岚
Owner NANJING TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap