A glass fiber cloth and a production method technology, applied in the field of materials, can solve the problems of insufficient strength, increased cost, easy burrs, etc., and achieve the effects of light and thin texture, material saving, and thin texture

Inactive Publication Date: 2018-10-02
孙福春
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glass fiber cloth is a commonly used industrial auxiliary product, which can be widely used in occasions where matting is required. However, the currently used glass fiber cloth is easy to burr, easy to break, and generally not strong enough. If the thickness is increased, the cost will increase

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] A method for making glass fiber cloth, comprising the following main steps: the raw materials used are: 1-3 parts of aluminum oxide, 5-8 parts of zinc oxide, 12 parts of sodium benzoate, 12 parts of methyl butyrate, 6 parts of sodium methyl phosphate 12 parts of castor oil, 11 parts of ethylene oxide, 18 parts of diethanolamine, 17 parts of sodium lauryl sulfate, 19 parts of sunflower oil, 11 parts of sodium aluminate, 8 parts of alanine, dipropylene glycol butyl ether 8 parts of dipropylene glycol monoalkyl, 12 parts of aluminum nitrate, 4 parts of rutile titanium dioxide, 3 parts of sunset yellow, 6 parts of vitamin C ethyl ether, 1 part of cocamidopropyl betaine, 10 parts of lactic acid and corn starch 8 servings.

[0010] The above raw materials are mixed and heated to 120 degrees Celsius, reacted under normal pressure for 12 minutes, then injected into the injection molding machine, and extruded according to the specified thickness to obtain glass fiber cloth.

Embodiment 2

[0012] A method for making glass fiber cloth, comprising the following major steps: the raw materials used are: 3 parts of aluminum oxide, 8 parts of zinc oxide, 12 parts of sodium benzoate, 12 parts of methyl butyrate, 6 parts of sodium methyl phosphate, castor oil 12 parts, 11 parts of ethylene oxide, 18 parts of diethanolamine, 17 parts of sodium lauryl sulfate, 19 parts of sunflower oil, 11 parts of sodium aluminate, 8 parts of alanine, dipropylene glycol butyl ether and other dipropylene glycol mono 8 parts of alkyl, 12 parts of aluminum nitrate, 7 parts of rutile titanium dioxide, 8 parts of sunset yellow, 11 parts of vitamin C ethyl ether, 10 parts of cocamidopropyl betaine, 19 parts of lactic acid and 10 parts of corn starch.

[0013] After the above-mentioned raw materials are mixed, they are heated to 146 degrees Celsius, reacted under normal pressure conditions for 19 minutes, then injected into an injection molding machine, and extruded according to the specified th...

Embodiment 3

[0015] A method for making glass fiber cloth, comprising the following main steps: raw materials used are: 2 parts of aluminum oxide, 6 parts of zinc oxide, 9 parts of sodium benzoate, 5 parts of methyl butyrate, 5 parts of sodium methyl phosphate, castor oil 11 parts, 8 parts of ethylene oxide, 17 parts of diethanolamine, 12 parts of sodium lauryl sulfate, 12 parts of sunflower oil, 10 parts of sodium aluminate, 3 parts of alanine, dipropylene glycol butyl ether and other dipropylene glycol mono 4 parts of alkyl, 11 parts of aluminum nitrate, 5 parts of rutile titanium dioxide, 5 parts of sunset yellow, 7 parts of vitamin C ethyl ether, 2 parts of cocamidopropyl betaine, 12 parts of lactic acid and 9 parts of corn starch.

[0016] After the above-mentioned raw materials are mixed, they are heated to 141 degrees Celsius, reacted under normal pressure conditions for 13 minutes, then injected into an injection molding machine, and extruded according to the specified thickness to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Provided is a producing method of glass fiber cloth. The producing method comprises the following main steps that raw materials which include aluminium oxide, zinc oxide, sodium benzoate, methyl butyrate, methyl sodium phosphate, castor oil, ethylene oxide, diethanol amine, lauryl sodium sulfate, sunflower seed oil, sodium aluminate, alanine, dipropylene glycol butyl ether dipropylene glycol monoalkyl, aluminium nitrate, rutile titanium dioxide, sunset yellow, vitamin C ethyl ether, cocamidopropyl betaine, lactic acid and corn starch are adopted; the raw materials are mixed and heated, react under an atmospheric condition, and then are injected into an injection molding machine and squeezed out according to specified thickness, and thus the glass fiber cloth is obtained. The glass fiber cloth is light, thin, good in paving effect, suitable for wide application and small in thickness, and saves material.

Description

technical field [0001] The invention belongs to the field of materials, in particular to a method for making glass fiber cloth. Background technique [0002] Glass fiber cloth is a commonly used industrial auxiliary product, which can be widely used in occasions that require bedding. However, the currently used glass fiber cloth is easy to burr, easy to break, and generally not strong enough. If the thickness is increased, the cost will increase. Contents of the invention [0003] The object of the present invention is to provide a method for making glass fiber cloth. The glass fiber cloth is light and thin, has good bedding effect and is suitable for wide use. [0004] A method for making glass fiber cloth, comprising the following main steps: the raw materials used are: 1-3 parts of aluminum oxide, 5-8 parts of zinc oxide, 3-12 parts of sodium benzoate, 4-12 parts of methyl butyrate, methyl 3-6 parts of sodium phosphate, 2-12 parts of castor oil, 3-11 parts of ethylene ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L91/00C08L3/02C08K13/02C08K3/22C08K5/098C08K3/28C08K5/41C08K5/17
CPCC08L91/00C08L2205/025C08L2205/03C08L3/02C08K13/02C08K2003/2227C08K5/098C08K3/28C08K5/41C08K5/17
Inventor 孙福春
Owner 孙福春
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap