Concrete slurry suitable for high temperature construction environment
A technology of concrete slurry and high temperature construction, applied in the field of concrete, can solve the problems of fast evaporation of water, affecting the application of concrete, and unusable concrete.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0017] The present invention also provides a method for preparing concrete slurry suitable for high temperature construction environment, comprising the following steps:
[0018] (1) After ball milling bentonite and kaolin evenly, calcinate at 300-450°C for 2-4h, then mix them with diethylenetriaminepentamethylenephosphonic acid in water, and react with microwave at 100-120°C for 5-10h, Obtain modified mineral powder;
[0019] (2) After mixing polymethacrylic acid, unsaturated glycerol, starch and polyphosphate in water, react at 80-120°C for 2-4h to obtain an intermediate, and then mix the intermediate, chitosan, polyphosphate Alcohol and polyethylene polyamine are mixed uniformly in water, and then reacted under microwave at 60-90°C for 30-90min to obtain retarded intermediate;
[0020] (3) After uniformly dispersing the retarder intermediate, cement, fine sand, pumice, modified mineral powder, and additives in water, continue stirring for 60-150s to obtain a concrete slurr...
Embodiment 1
[0024] A concrete slurry suitable for high-temperature construction environments, made of the following raw materials in parts by weight: 26kg of cement, 32kg of fine sand, 16kg of pumice, 6kg of bentonite, 8kg of kaolin, 2kg of diethylenetriaminepentamethylenephosphonic acid, 10kg chitosan, 6kg glycidyl methacrylate, 3kg starch, 3kg polyethylene adipate, 2kg N,N-diethylbutane-1,4-diamine, 5kg triallyl phosphate , 3kg polymethacrylic acid, 0.5kg polycarboxylate superplasticizer (model PASP-Ca, purchased from Shandong Yuanlian Chemical Co., Ltd.), 1kg sodium dodecylbenzenesulfonate, 0.5kg calcium stearate, 0.5kg Hydroxyethyl methyl reinforced cellulose ether, 0.5kg sodium aluminate.
[0025] The preparation steps of the concrete slurry applicable to the high-temperature construction environment are as follows:
[0026] (1) After ball milling bentonite and kaolin evenly, calcinate at 400°C for 2.5h, then mix them with diethylenetriaminepentamethylenephosphonic acid in water, th...
Embodiment 2
[0030]A concrete slurry suitable for high-temperature construction environments, made of the following raw materials in parts by weight: 30kg of cement, 28kg of fine sand, 12kg of pumice, 8kg of bentonite, 12kg of kaolin, 4kg of diethylenetriaminepentamethylenephosphonic acid, 8kg chitosan, 5kg 2-glycidyl methacrylate, 5kg starch, 1kg polyoxypropylene glycol, 3kg N-hydroxyethylbutylene diamine, 3kg allyl diethyl phosphate, 6kg polymethacrylic acid, 1kg polycarboxylate superplasticizer (model PASP-Ca, purchased from Shandong Yuanlian Chemical Co., Ltd.), 1kg sodium dodecylbenzenesulfonate, 1kg calcium stearate, 1kg hydroxyethyl methyl reinforced cellulose ether, 1kg of anhydrous sodium sulfate.
[0031] The preparation steps of the concrete slurry applicable to the high-temperature construction environment are as follows:
[0032] (1) After ball milling bentonite and kaolin evenly, calcinate at 350°C for 3.5h, then mix them with diethylenetriaminepentamethylenephosphonic acid ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com