Highway concrete with thermal insulation effect and good durability

A durability and concrete technology, applied in the field of concrete, can solve the problems of insufficient heat insulation and durability, and achieve the effects of improving impermeability, enhancing load-bearing capacity, and good heat insulation

Inactive Publication Date: 2018-10-19
来安县塔鑫建材有限公司
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the complexity of the road environment, there are certain requirements for the material and quality of the concrete. At present, the heat insulation and durability of road concrete are still slightly insufficient, and urgently need to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] The invention proposes a concrete with good heat insulation and durability for road use. The raw materials include: 200 parts of Portland cement, 480 parts of gravel, 80 parts of ceramsite, 350 parts of pumice, 60 parts of expanded perlite, vitrified 10 parts of microbeads, 10 parts of fish bone meal, 2 parts of carbon fiber, 4 parts of polyimide fiber, 10 parts of neoprene emulsion, 4 parts of epoxy resin, 4 parts of sulfur, 0.2 parts of sodium alkylbenzene sulfonate, polycarboxylic acid 0.2 parts of water reducer, 20 parts of modified lignin fiber.

Embodiment 2

[0017] The invention proposes a concrete with good heat insulation and durability for road use. The raw materials include: 250 parts of Portland cement, 550 parts of gravel, 40 parts of ceramsite, 450 parts of pumice, 120 parts of expanded perlite, vitrified 20 parts of microbeads, 15 parts of fish bone powder, 4 parts of carbon fiber, 8 parts of polyimide fiber, 5 parts of neoprene emulsion, 8 parts of epoxy resin, 2 parts of sulfur, 0.5 parts of sodium alkylbenzene sulfonate, polycarboxylic acid 0.5 parts of water reducer, 35 parts of modified lignin fiber.

[0018] Among them, the polycarboxylate water reducer is prepared according to the following process: mix methoxypolyethylene glycol, prenol polyoxyethylene ether and p-toluenesulfonic acid, then add benzoyl peroxide, methacrylic acid, 3-mercaptopropionic acid and sodium styrene sulfonate are stirred and reacted to obtain polycarboxylate water reducer;

[0019] The modified lignin fiber is prepared according to the foll...

Embodiment 3

[0021] The invention proposes a concrete with good heat insulation and durability for road use. The raw materials include, by weight, 220 parts of Portland cement, 510 parts of gravel, 60 parts of ceramsite, 400 parts of pumice, 90 parts of expanded perlite, vitrified 15 parts of microbeads, 12 parts of fish bone meal, 3 parts of carbon fiber, 6 parts of polyimide fiber, 8 parts of neoprene emulsion, 6 parts of epoxy resin, 3 parts of sulfur, 0.4 parts of sodium alkylbenzene sulfonate, polycarboxylic acid 0.3 parts of water reducing agent, 28 parts of modified lignin fiber.

[0022] Among them, the polycarboxylate water reducer is prepared according to the following process: 16 parts of methoxypolyethylene glycol, 27 parts of prenol polyoxyethylene ether and 0.3 part of p-toluenesulfonic acid are mixed in parts by weight, and the Stir under temperature conditions, then add 0.3 parts of benzoyl peroxide, 8 parts of methacrylic acid, 6 parts of 3-mercaptopropionic acid, and 5 pa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses highway concrete with thermal insulation effect and good durability. Raw materials of the highway concrete comprise: Portland cement, gravel, ceramsite, pumice, expanded perlite, glazed hollow beads, fishbone dust, carbon fiber, polyimides fiber, a polychloroprene emulsion, epoxy resin, sulphur, sodium alkyl benzene sulfonate, a polycarboxylate superplasticizer and modifiedlignin fibre. The invention brings forward highway concrete with thermal insulation effect and good durability. The highway concrete with thermal insulation effect and good durability has a certain thermal insulation effect and good durability.

Description

technical field [0001] The invention relates to the technical field of concrete, in particular to a concrete with good heat insulation and durability for road use. Background technique [0002] Concrete refers to the collective name of engineering composite materials that use cementitious materials (cement) to bond aggregates into a whole. Since its inception, concrete has quickly become one of the most popular and widely used building materials, which greatly accelerates the construction of national infrastructure projects. development, especially the development of road construction. Due to the complexity of the road environment, there are certain requirements for the material and quality of concrete. At present, the heat insulation and durability of road concrete are still slightly insufficient, and urgently need to be improved. Contents of the invention [0003] Based on the technical problems existing in the background technology, the present invention proposes a con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/08C04B28/04
CPCC04B28/04C04B2111/20C04B2111/40C04B14/06C04B18/027C04B14/16C04B14/185C04B14/24C04B18/18C04B16/0691C04B14/386C04B24/005C04B24/281C04B22/02C04B24/16C04B18/26C04B2103/302C04B38/08
Inventor 宋忠亭
Owner 来安县塔鑫建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com