Chromotropic paint used for medical instrument and preparation method and application thereof

A technology of medical devices and color-changing coatings, applied in the field of coatings, can solve the problems of affecting user comfort and safety, high VOCs content, easy discoloration of coatings, etc., achieve good environmental protection characteristics, low VOCs content, and prolong shelf life Effect

Pending Publication Date: 2018-10-23
HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems of high VOCs content in existing coatings for medical devices, the temperature of medical devices affects the comfort and safety of users, and the coating is prone to discoloration, aging, bacteria breeding and abrasion, the present invention provides a color-changing coating for medical devices

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chromotropic paint used for medical instrument and preparation method and application thereof
  • Chromotropic paint used for medical instrument and preparation method and application thereof
  • Chromotropic paint used for medical instrument and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] And, the embodiment of the present invention also provides a method for preparing a color-changing coating for medical devices, and the preparation method at least includes the following steps:

[0035] Step a. Weigh each raw material component according to the raw material formula of the above-mentioned color-changing coating for medical devices, and disperse 1 / 2 to 2 / 3 of the deionized water of the formula, 1 / 2 to 2 / 3 of the pH regulator, and Agent, 1 / 2~2 / 3 formula amount of defoamer, nano-alumina, nano-zirconia, nano-zinc oxide, temperature-sensitive color-changing powder, titanium dioxide, silica sol, organic silicone powder, and negative ion powder are mixed evenly;

[0036] Step b. Add water-based hydroxyacrylic acid emulsion, film-forming aids, remaining deionized water, remaining pH regulator, remaining defoamer and substrate wetting agent to the mixing container in turn under stirring, pre-mix evenly and add to In the mixture obtained in step a, mix evenly, add...

Embodiment 1

[0044] An embodiment of the present invention provides a color-changing coating for medical devices, including the following raw materials in parts by weight:

[0045]

[0046]

[0047] Among them, the titanium dioxide is a mixture of DuPont R-103 and R706 in a mass ratio of 1:1, and the defoamer is a mixture of 941PL from MOUSSEX and BYK-028 from BAK in a mass ratio of 1.2:1. The auxiliary agent is a mixture of environmentally friendly and odor-free film-forming auxiliary agent AF of Guangzhou Yutai Chemical Technology Co., Ltd. and alcohol ester-12 of American Eastman with a mass ratio of 1:1.

[0048] Prepare as follows:

[0049] Step a. Weigh each raw material component according to the raw material formula of the above-mentioned color-changing coating for medical devices, and mix 1 / 2 of the formula amount of deionized water, 1 / 2 of the formula amount of pH regulator, dispersant, 1 / 2 of the formula Mix a certain amount of defoamer, nano-alumina, nano-zirconia, nano-...

Embodiment 2

[0054] An embodiment of the present invention provides a color-changing coating for medical devices, including the following raw materials in parts by weight:

[0055]

[0056] Among them, the titanium dioxide is a mixture of JHNM-W of Jianghu Titanium Dioxide Company and R-980 of TPIAQUE Company with a mass ratio of 4:1, and the defoamer is a mass ratio of 941PL of MOUSSEX Company and BYK-024 of BAK Company It is a mixture of 1:1, and the film-forming aid is a mixture of the environmentally friendly and odor-free film-forming aid AF of Guangzhou Yutai Chemical Technology Co., Ltd. and the alcohol ester-12 of American Eastman with a mass ratio of 1:2.

[0057] Prepare as follows:

[0058] Step a. Weigh each raw material component according to the raw material formula of the above-mentioned color-changing coating for medical devices, and mix 1 / 2 of the formula amount of deionized water, 1 / 2 of the formula amount of pH regulator, dispersant, 1 / 2 of the formula Mix a certain ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a chromotropic paint used for a medical instrument and a preparation method and an application thereof. The chromotropic paint comprises the following raw materials in parts by weight: 25-50 parts of an aqueous hydroxyl acrylic emulsion, 5-20 parts of a curing agent, 2-5 parts of a cosolvent, 1-5 parts of organic silicone powder, 1-5 parts of nano alumina, 0.05-0.5 parts of nano zirconia, 0.1-3 parts of nano negative ion powder, 4-8 parts of titanium dioxide, 0.05-0.5 parts of nano zinc oxide, 1-6 parts of temperature-sensitive color-changing powder, 0.1-1 part of silica sol, 0.1-0.2 parts of a pH conditioning agent, 0.1-0.2 parts of an antifoaming agent, 2-5 parts of a film-forming auxiliary agent, 0.3-0.5 parts of a dispersant, 0.3-0.5 parts of a base material wetting agent, 5-10 parts of deionized water, and 0.5-1.0 parts of a thickening agent. The VOCs content of the paint is low, and a coating has good light resistance, chemically-resistant performance, hardness, bacterinertness, air cleaning performance, and color-changing indication effect.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a color-changing coating for medical devices and a preparation method and application thereof. Background technique [0002] With the improvement of living standards, medical devices are used more and more widely, ranging from medical beds in hospitals to toilets in families. Due to the particularity of the application environment of medical equipment and the customers are mainly patients or the infirm, medical equipment has higher and higher environmental protection requirements for coatings. Traditional paints contain a large amount of volatile organic compounds (VOCs). Various volatile organic compounds such as toluene, benzene, and xylene are released. When VOCs in the air reach a certain concentration, it will cause symptoms such as headache, nausea, vomiting, fatigue, etc., and even cause convulsions and coma in severe cases, damage the liver, kidneys, brain and nervous system, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/14C09D5/14C09D5/16C09D7/61C09D7/63C09D7/65
CPCC08K2003/2227C08K2003/2241C08K2003/2244C08K2003/2296C08K2201/011C09D5/14C09D5/1675C09D5/1687C09D133/066C08L83/04C08K13/02C08K3/22C08K3/36C08K5/103
Inventor 赵宁宁董立志胡中源
Owner HEBEI CHENYANG INDAL & TRADE GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com