High-performance formaldehyde adsorbent and preparation method thereof

A formaldehyde adsorption, high-performance technology, applied in the field of high-performance formaldehyde adsorbent and its preparation, can solve the problem of unsatisfactory formaldehyde removal effect, achieve the effect of improving physical adsorption performance, improving purification efficiency, and promoting adsorption

Inactive Publication Date: 2018-11-06
ANHUI KEPU ENVIRONMENT TECH CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, the removal of formaldehyde has become the top priority of purifying indoor pollutants. However, the existing products are not ideal for removing formaldehyde. Therefore, it is urgent to develop a high-performance formaldehyde removal product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A high-performance formaldehyde adsorbent, comprising by weight: 60 parts of modified activated carbon, 30 parts of sepiolite, 10 parts of zeolite, 10 parts of microcrystalline cellulose, 10 parts of diatomaceous earth, and 30 parts of polyethylene polyamine polymer , 1 part of polyethylene glycol, 2 parts of nano-titanium dioxide, and 0.5 part of nano-zinc dioxide.

Embodiment 2

[0020] A high-performance formaldehyde adsorbent, comprising by weight: 60 parts of modified activated carbon, 30 parts of sepiolite, 10 parts of zeolite, 10 parts of microcrystalline cellulose, 10 parts of diatomaceous earth, and 30 parts of polyethylene polyamine polymer , 1 part of polyethylene glycol, 2 parts of nano-titanium dioxide, and 0.5 part of nano-zinc dioxide; the particle diameters of the modified activated carbon, sepiolite, zeolite, microcrystalline cellulose, and diatomite are all between 1-100um ; The particle diameters of the nano-titanium dioxide and nano-zinc dioxide are between 10-100nm.

[0021] Preparation of the modified activated carbon: Weigh 8 g of activated carbon and add it to potassium permanganate solution, stir at room temperature for 10 h, filter, dry the solid product at a temperature lower than 80°C, mix it with manganese sulfate solution, stir for 5 h, and filter , washed 5 times with distilled water, dried at below 100°C, and roasted under...

Embodiment 3

[0026] A high-performance formaldehyde adsorbent, comprising by weight: 80 parts of modified activated carbon, 15 parts of sepiolite, 20 parts of zeolite, 5 parts of microcrystalline cellulose, 20 parts of diatomaceous earth, and 15 parts of polyethylene polyamine polymer , 4 parts of polyethylene glycol, 0.5 parts of nano-titanium dioxide, and 2 parts of nano-zinc dioxide; the particle diameters of the modified activated carbon, sepiolite, zeolite, microcrystalline cellulose, and diatomite are all between 1-100um ; The particle diameters of the nano-titanium dioxide and nano-zinc dioxide are between 10-100nm.

[0027] Preparation of the modified activated carbon: Weigh 15g of activated carbon and add it to potassium permanganate solution, stir at room temperature for 6h, filter, dry the solid product at a temperature lower than 80°C, mix it with manganese sulfate solution, stir for 10h, and filter , washed 3 times with distilled water, dried at below 100°C, and roasted under ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Concentrationaaaaaaaaaa
Login to View More

Abstract

A high-performance formaldehyde adsorbent is prepared from components in parts by weight as follows: 60-80 parts of modified activated carbon, 15-30 parts of sepiolite, 10-20 parts of zeolite, 5-10 parts of microcrystalline cellulose, 10-20 parts of diatomaceous earth, 15-30 parts of a polyethylene polyamine polymer, 1-4 parts of polyethylene glycol, 0.5-2 parts of nano-titania and 0.5-2 parts ofnano-zinc peroxide. A preparation method of the high-performance formaldehyde adsorbent comprises the following steps: the polyethylene polyamine polymer and polyethylene glycol are mixed, deionized water is added for dilution, and a solution a is obtained; then the modified activated carbon, the sepiolite, the zeolite, microcrystalline cellulose, the diatomaceous earth, nano-titania and nano-zincperoxide are added to the solution a, and a thermal insulation reaction is performed; vacuum drying is performed, and the adsorbent is obtained. The prepared high-performance formaldehyde adsorbent has excellent formaldehyde removal performance, and tests prove that formaldehyde degradation rate of the formaldehyde adsorbent within 24 h reaches 99% or higher.

Description

technical field [0001] The invention relates to the technical field of adsorbent materials, in particular to a high-performance formaldehyde adsorbent and a preparation method thereof. Background technique [0002] Indoor environment, due to the widespread use of decoration materials and furniture, air pollutants accumulate in confined spaces for a long time. Living in this environment for a long time will pose a serious threat to human physical and mental health, and formaldehyde is one of the most harmful pollutants. According to the investigation of indoor formaldehyde content by a large number of scholars, it is found that the formaldehyde content in the living environment in most areas has already exceeded the limit of 0.10mg / m2 in my country's indoor air quality standards. 3 , and even after decoration of new houses in some areas, the amount of indoor formaldehyde exceeds the standard value by more than ten times, and the harm it poses is self-evident. Therefore, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B01J20/22B01J31/38B01D53/86B01D53/02B01J20/30B01D53/72
CPCB01D53/02B01D53/8668B01J20/06B01J20/22B01J31/38B01D2257/708B01J35/39
Inventor 柯锐
Owner ANHUI KEPU ENVIRONMENT TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com