Method for preparing emulsion type rubber asphalt
A rubberized asphalt and emulsion type technology, applied in building components, building insulation materials, buildings, etc., can solve the problems of poor mechanical properties and stability of asphalt, and achieve the effects of improving mechanical properties, ensuring stability and reducing density
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0019] Example 1
[0020] Put the diatomaceous earth in a ball mill and pass it through an 80-mesh sieve to obtain diatom powder. Put the diatom powder and 30% hydrochloric acid in a mass ratio of 1:20 in a beaker at a speed of 500r / min. After stirring and mixing for 50 minutes, a mixed slurry was obtained, and then the mixed slurry was filtered to obtain a filter residue, and then the filter residue was washed with 30% ammonia water until the washing liquid was neutral, and then the washed filter residue was placed in an oven. At a temperature of 110℃, dry to a constant weight, pretreat the diatom powder, place the glass fiber in a ball mill and grind it through a 100-mesh sieve to obtain the glass fiber powder. The pretreated diatom powder and the mass concentration are 2.6mg / mL of dopamine solution was soaked in a three-necked flask at a mass ratio of 1:20 for 2 hours, and then added to the three-necked flask with 0.2 times the mass of pretreated diatom powder sodium bicarbon...
Example Embodiment
[0021] Example 2
[0022] Put the diatomaceous earth in a ball mill and pass it through an 80-mesh sieve to obtain diatom powder. Place the diatom powder and 30% hydrochloric acid in a mass ratio of 1:20 in a beaker at a speed of 500r / min. After stirring and mixing for 50 minutes, a mixed slurry was obtained, and then the mixed slurry was filtered to obtain a filter residue, and then the filter residue was washed with 30% ammonia water until the washing liquid was neutral, and then the washed filter residue was placed in an oven. Under the condition of temperature of 110℃, dry to constant weight, pretreat the diatom powder, place the glass fiber in a ball mill and grind it through a 100-mesh sieve to obtain glass fiber powder. The pretreated diatom powder and the mass concentration are 2.6mg / mL of dopamine solution was soaked in a three-necked flask at a mass ratio of 1:20 for 2 hours, and then added to the three-necked flask, 0.2 times the mass of pretreated diatom powder sodiu...
Example Embodiment
[0023] Example 3
[0024] In parts by weight, take 60 parts of asphalt and 40 parts of waste tire rubber powder in sequence, put the asphalt in a high-speed shearing machine, melt the asphalt at a temperature of 185℃, and then add waste to the high-speed shearing machine The rubber powder is mixed at a speed of 1200r / min, high-speed shearing for 60 minutes, and then cooled to 130°C to obtain a mixed slurry. Then, at a temperature of 130°C, keep it warm for use; in parts by weight, 10 Parts of cationic surfactant, 10 parts of non-ionic surfactant, and 60 parts of water are placed in the mixer at a temperature of 55°C and a rotating speed of 800 r.min, heated and stirred for 60 minutes, and then dripped into the mixer Add 3% ammonium chloride solution to adjust the pH to 5.1, stir and mix for 60 minutes at a speed of 800r / min to obtain an emulsion; in parts by weight, mix 60 parts of the mixed slurry and 40 parts of the emulsion , 30 parts of tar and 5 parts of phospholipids were ...
PUM
Property | Measurement | Unit |
---|---|---|
Concentration | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap