Evanescent mode water-based paint for large alloy steel casting
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of alloy cast steel and water-based coatings, applied in coatings, casting molds, cores, etc., can solve the problems of poor air permeability, surface pores, etc., and achieve the effects of improving coating air permeability, high temperature air permeability, and low temperature strength
Inactive Publication Date: 2018-11-13
河北冀凯铸业有限公司
View PDF9 Cites 3 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0009] In order to solve the above technical problems, the present invention provides a lost foam water-based coating for large alloy steel castings, which solves casting defects such as surface pores caused by poor gas permeability of the coating, and improves the low-temperature strength, high-temperature strength, and high-temperature gas permeability of the coating. flexibility, so that large steel castings meet the needs of mass production
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
example 1
[0036] A kind of lost foam water-based paint for large alloy steel castings, comprising the following components by weight:
[0037] 30 parts of quartz powder, 15 parts of zircon powder, 10 parts of talc powder, 14 parts of super bauxite, 15 parts of synthetic mullite, 3 parts of perlite particles, 5 parts of sodium bentonite, 3 parts of sodium hydroxymethyl starch, 2 parts of tapioca starch, 1 part of refractory fiber, 2 parts of mica powder.
example 2
[0039] A kind of lost foam water-based paint for large alloy steel castings, comprising the following components by weight:
[0040] 34 parts of quartz powder, 15 parts of zircon powder, 10 parts of talc powder, 10 parts of super bauxite, 15 parts of synthetic mullite, 3 parts of perlite particles, 5 parts of sodium bentonite, 3 parts of sodium hydroxymethyl starch, 2 parts of tapioca starch, 1 part of refractory fiber, 2 parts of mica powder.
example 3
[0042] A kind of lost foam water-based paint for large alloy steel castings, comprising the following components by weight:
[0043] 37 parts of quartz powder, 10 parts of zircon powder, 10 parts of talc powder, 12 parts of super bauxite, 15 parts of synthetic mullite, 3 parts of perlite particles, 5 parts of sodium bentonite, 3 parts of sodium hydroxymethyl starch, 2 parts of tapioca starch, 1 part of refractory fiber, 2 parts of mica powder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
flame retardant
aaaaa
aaaaa
flame retardant
aaaaa
aaaaa
melting point
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an evanescent mode water-based paint for a large alloy steel casting. The evanescent mode water-based paint comprises the following components in parts by weight: 30 45 parts of quartz powder, 7 17 parts of zircon powder, 5 10 parts of talcum powder, 10 15 parts of bauxite, 15 parts of synthetic mullite, 2 4 parts of perlite particles, 4 6 parts of sodium bentonite, 2 4 parts of sodium carboxymethyl starch, 1 3 parts of cassava starch, 0.5-1.5 parts of refractory fiber, and 1 3 parts of mica powder. The evanescent mode water-based paint for the large alloy steel castingovercomes the casting defect that there air holes in the surface due to poor air permeability of the paint and improves the low-temperature strength, high-temperature strength and high-temperature air permeability of a coating, thereby enabling the large alloy steel casting to meet the requirements for mass production.
Description
technical field [0001] The invention relates to a lost foam water-based paint for large alloy steel castings. Background technique [0002] Conventional lost foam casting (also known as solid casting) is made of EPS foam material to form a solid mold with the same structure and size as the part to be cast, dip-coated with refractory coating (for strengthening, smoothness, and ventilation) and dried Finally, it is buried in dry quartz sand and subjected to three-dimensional vibration modeling. The casting mold box is poured with molten metal under negative pressure, so that the polymer material model is heated and vaporized, and then it is replaced by liquid metal and formed after cooling and solidification. A new casting method for the production of castings by a new process of permanent shape casting. When this method is used to produce large steel castings, insufficient EPS combustion during the pouring process can easily cause carbonization on the surface of the steel ca...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more