High-sensitivity phosphor powder material for temperature sensing and preparation method of high-sensitivity phosphor powder material

A high-sensitivity, phosphor technology, applied in luminescent materials, chemical instruments and methods, etc., can solve the problems of unstable physical and chemical properties of fluoride, sensitive to oxygen surface contact, strong corrosiveness and volatility, etc., and achieve low production costs. , Simple operation, high sensitivity effect

Active Publication Date: 2018-11-16
HUAIYIN TEACHERS COLLEGE
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Up-conversion luminescent material is a luminescent material that can convert near-infrared light into visible light, usually including activator, sensitizer and matrix, Er 3+ 、Tm 3+ Plasma has abundant energy levels, and some energy levels have a long lifetime. It is the activator of up-conversion materials that have been studied more at present. Er 3+ 、Tm 3+ Up-conversion materials with ions as activators usually use ytterbium ions Yb 3+ As a sensitizer, for the matrix in the up-conversion material, the phosphor with high-efficiency luminescence generally uses fluoride with low phonon energy as the matrix, such as NaYF 4 , is currently the host material with the highest up-conversion luminous efficiency, doped with Yb 3+ -Er 3+ Synthesize up-conversion luminescent materials after various ion pairs, such as NaYF 4 :Er 3+ -Yb 3+ ; but the physical and chemical properties of fluoride itself are very unstable, and it is very sensitive to the surface contact with oxygen, which is easily polluted and deteriorated to affect the subsequent luminous performance; in addition, the fluorine source used in the preparation process of fluoride materials has a strong Corrosive and volatile, easy to cause environmental pollution
[0004] Compared with fluoride, the oxide matrix material has high physical and chemical stability, the production process is simple, easy to synthesize, and no pollutants are produced during the preparation process, such as SrWO 4 、BaMoO 4 etc., but the currently developed luminescent materials, such as BaMoO 4 :Er 3+ -Yb 3 、SrWO 4 :Er 3+ -Yb 3+ etc., the temperature detection sensitivity is compared to NaYF 4 :Er 3+ -Yb 3+ Lower, and the material emits less color

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-sensitivity phosphor powder material for temperature sensing and preparation method of high-sensitivity phosphor powder material
  • High-sensitivity phosphor powder material for temperature sensing and preparation method of high-sensitivity phosphor powder material
  • High-sensitivity phosphor powder material for temperature sensing and preparation method of high-sensitivity phosphor powder material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Step 1: Accurately weigh the initial raw material Y 2 o 3 , SiO 2 , Yb 2 o 3 and Ho 2 o 3 , and the cosolvent Li 2 CO 3 In an agate mortar, grind after adding sewage ethanol, and mix evenly; the purity of the initial raw material and co-solvent are both 99.99%; Y 2 o 3 , SiO 2 , Yb 2 o 3 ,Ho 2 o 3 with Li 2 CO 3 The mass ratio of Y is 264:100:45.9:4.4:8.29; Y 2 o3 , SiO 2 , Yb 2 o 3 ,Ho 2 o 3 and Li 2 CO 3 The mass and the ratio of ethanol to ethanol are 1g / (4~7ml);

[0031] Step 2, put the ground mixture in a 5ml corundum crucible, and burn it in a heating furnace. After the burning is completed, take out the crucible after the heating furnace cools down, and grind it to obtain a powdery product, that is, the molecular formula of the obtained phosphor material is Y 4.20767 Yb 0.4203 Ho 0.04203 Si 3 o 13 , that is, the molecular formula of the phosphor material Y 4.67(1-x-y) Yb 4.67x Ho 4.67y Si 3 o 13 Take x=9% and y=0.9%; the heating f...

Embodiment 2

[0033] Step 1: Accurately weigh the initial raw material Y 2 o 3 , SiO 2 , Yb 2 o 3 and Ho 2 o 3 , and the cosolvent Li 2 CO 3 In an agate mortar, grind after adding sewage ethanol, and mix evenly; the purity of the initial raw material and co-solvent are both 99.99%; Y 2 o 3 , SiO 2 , Yb 2 o 3 ,Ho 2 o 3 with Li 2 CO 3 The mass ratio of Y is 257:100:56.2:5.9:8.38; Y 2 o 3 , SiO 2 , Yb 2 o 3 ,Ho 2 o 3 and Li 2 CO 3 The mass and the ratio of ethanol to ethanol are 1g / (4~7ml);

[0034] Step 2, put the ground mixture in a 5ml corundum crucible, and burn it in a heating furnace. After the burning is completed, take out the crucible after the heating furnace cools down, and grind it to obtain a powdery product, that is, the molecular formula of the obtained phosphor material is Y 4.10026 Yb 0.5137 Ho 0.05604 Si 3 o 13 , that is, the molecular formula of the phosphor material Y 4.67(1-x-y) Yb 4.67x Ho 4.67y Si 3 o 13 Take x=11% and y=1.2%; the heatin...

Embodiment 3

[0036] Step 1: Accurately weigh the initial raw material Y 2 o 3 , SiO 2 , Yb 2 o 3 and Ho 2 o 3 , and the cosolvent Li 2 CO 3 In an agate mortar, grind after adding sewage ethanol, and mix evenly; the purity of the initial raw material and co-solvent are both 99.99%; Y 2 o 3 , SiO 2 , Yb 2 o 3 ,Ho 2 o 3 with Li 2 CO 3 The mass ratio of Y is 260:100:51.1:4.9:8.32; Y 2 o 3 , SiO 2 , Yb 2 o 3 ,Ho 2 o 3 and Li 2 CO 3 The mass and the ratio of ethanol to ethanol are 1g / (4~7ml);

[0037] Step 2, put the ground mixture in a 5ml corundum crucible, and burn it in a heating furnace. After the burning is completed, take out the crucible after the heating furnace cools down, and grind it to obtain a powdery product, that is, the molecular formula of the obtained phosphor material is Y 4.1563 Yb 0.467 Ho 0.0467 Si 3 o 13 , that is, the molecular formula of the phosphor material Y 4.67(1-x-y) Yb 4.67x Ho 4.67y Si 3 o 13 Take x=10% and y=1%; the heating fur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to View More

Abstract

The invention provides a high-sensitivity phosphor powder material for temperature sensing. The high-sensitivity phosphor powder material has a molecular formula of Y4.67(1-x-y)Yb4.67xHo4.67ySi3O13, wherein 9%<=x<=11%, and 0.9%<=y<=1.2%; in addition, the invention also provides a preparation method of the high-sensitivity phosphor powder material for temperature sensing, and the preparation methodcomprises the following steps: (1), weighing initial raw materials of Y2O3, SiO2, Yb2O3 and Ho2O3 and a fusing assistant Li2CO3 in an agate crucible accurately, adding anhydrous ethanol, performing grinding, and performing even mixing; and (2), placing the ground mixture in an alundum crucible of 5 ml, performing calcination in a heating furnace, taking the crucible out after completion of calcination and cooling of the heating furnace are conducted, and performing grinding to obtain the powdery product which is the phosphor powder material.

Description

technical field [0001] The invention relates to a high-sensitivity phosphor material for temperature sensing and a preparation method thereof, belonging to the technical field of material preparation. Background technique [0002] Temperature, as one of the most important physical quantities, is a parameter that must be accurately measured in many fields such as science, industry, and military affairs. Various temperature sensors are also widely used in daily life, metrology, gas mechanics, atmosphere and maritime affairs, as well as fields such as chemistry, medicine, biology and military technology. With the rapid development of fields such as energy, information and biomedicine, higher and more complex requirements are put forward for the speed and accuracy of temperature detection, such as temperature measurement at submicron or even nanometer scale, temperature detection of cells in living organisms, etc. Traditional temperature detection and sensing materials work bas...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/79
CPCC09K11/7774
Inventor 张佳陈华宝陈贵宾
Owner HUAIYIN TEACHERS COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products