Ester plasticizer for PVC

A plasticizer and lipid technology, applied in the field of polymer material additives, can solve the problems of unenvironmental protection, high cost, human health threat, etc., and achieve the effects of short production cycle, satisfying use requirements and simple production process

Inactive Publication Date: 2018-11-27
GUANGXI NORMAL UNIV OF SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such plasticizers in my country mainly include dioctyl phthalate (DOP), dibutyl phthalate (DBP), diheptyl phthalate (DBP), di Isodecyl ester (DIDP) and diisooctyl phthalate (DIOP), these plasticizers generally have the disadvantages of high cost and environmental protection, and at the same time pose a serious threat to human health, so the EU since 2007 In January, the use of DBP dibutyl phthalate and DOP dioctyl phthalate plasticizers in children's toys and supplies was banned, and the use of DINP, DIDP, and DNOP was restricted

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of PVC lipid plasticizer, described plasticizer is mainly made up of the raw material of following weight part:

[0030] Diethylene glycol dibenzoate 10 parts; cage silicone hybrid star poly 10 parts; polyvinyl chloride 10 parts; activated carbon 5 parts; glycerin 3 parts; soda ash 5 parts; octyl ethylene oxide 1 3 parts; 3 parts of carbamide; 1 part of epoxidized soybean oil.

[0031] A preparation method of PVC lipid plasticizer mainly comprises the steps:

[0032] Step (1), weighing corresponding weight parts of diethylene glycol dibenzoate, cage silicone hybrid star poly, polyvinyl chloride, activated carbon and glycerol;

[0033] Step (2), adding the raw materials obtained in step (1) into a stirrer, heating and stirring until the temperature is 60° C., and continuously stirring at this temperature for 20 minutes to obtain a semi-finished product;

[0034] Step (3), taking by weight soda ash, octyl oxirane, carbamide and epoxidized soybean oil;

[0035] I...

Embodiment 2

[0037] A kind of PVC lipid plasticizer, described plasticizer is mainly made up of the raw material of following weight part:

[0038] Diethylene glycol dibenzoate 30 parts; cage silicone hybrid star poly 30 parts; polyvinyl chloride 20 parts; activated carbon 10 parts; glycerol 5 parts; soda ash 8 parts; octyl ethylene oxide 5 parts parts; 5 parts of carbonamide; 3 parts of epoxidized soybean oil.

[0039] A preparation method of PVC lipid plasticizer mainly comprises the steps:

[0040] Step (1), weighing corresponding weight parts of diethylene glycol dibenzoate, cage silicone hybrid star poly, polyvinyl chloride, activated carbon and glycerol;

[0041] Step (2), adding the raw materials obtained in step (1) into a stirrer, heating and stirring until the temperature is 50° C., and continuously stirring at this temperature for 25 minutes to obtain a semi-finished product;

[0042] Step (3), taking by weight soda ash, octyl oxirane, carbamide and epoxidized soybean oil;

...

Embodiment 3

[0045] A kind of PVC lipid plasticizer, described plasticizer is mainly made up of the raw material of following weight part:

[0046] Diethylene glycol dibenzoate 20 parts; cage silicone hybrid star poly 20 parts; polyvinyl chloride 15 parts; activated carbon 8 parts; glycerin 4 parts; soda ash 6 parts; octyl ethylene oxide 3 parts 4 parts; 4 parts of carbonamide; 2 parts of epoxidized soybean oil.

[0047] A preparation method of PVC lipid plasticizer mainly comprises the steps:

[0048] Step (1), weighing corresponding weight parts of diethylene glycol dibenzoate, cage silicone hybrid star poly, polyvinyl chloride, activated carbon and glycerol;

[0049] Step (2), adding the raw materials obtained in step (1) into a stirrer, heating and stirring until the temperature is 60° C., and continuously stirring at this temperature for 20 minutes to obtain a semi-finished product;

[0050] Step (3), taking by weight soda ash, octyl oxirane, carbamide and epoxidized soybean oil;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ester plasticizer for PVC. The plasticizer mainly consists of the following raw materials, by weight: 10-30 parts of diethylene glycol dibenzoate, 10-30 parts of a polyhedral organosilicon hybrid star polymer, 10-20 parts of polyvinyl chloride, 5-10 parts of activated carbon, 3-5 parts of glycerol, 5-8 parts of soda ash, 1-5 parts of octyl ethylene oxide, 3-5 parts of carbamide, and 1-3 parts of epoxy soybean oil. The ester plasticizer for PVC of the invention has characteristics of non-toxicity and environmental protection, can meet the application requirements, isshort in production cycle, has application properties of migration resistance, solvent effect resistance, weather resistance and the like, is easy in production process, and is beneficial to market-oriented production applications.

Description

technical field [0001] The invention relates to the technical field of polymer material additives, in particular to a PVC lipid plasticizer. Background technique [0002] Plasticizers refer to organic substances that increase the plasticity of plastics, improve the fluidity of resins during plastic processing, and make plastic products flexible. Plasticizers are usually viscous liquids with high boiling points, difficult to volatilize or solids with low melting points. Plasticizers are generally required to be colorless, non-toxic, odorless, cold-resistant, heat-resistant, volatile and mobile, and chemically Good stability, cheap and easy to get. Plasticizers can weaken the van der Waals force between plastic polymer molecules, increase the mobility of polymer molecular chains, reduce the crystallinity of polymer molecular chains, and enhance the plasticity of polymers, thereby reducing the hardness and softening temperature of polymers. As well as the embrittlement temper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L91/00C08L83/04C08K13/02C08K3/04C08K5/053C08K5/103C08K5/1515
CPCC08L27/06C08L83/04C08L2205/03C08L91/00C08K13/02C08K3/04C08K5/053C08K5/103C08K5/1515
Inventor 文胜蓝峻峰覃逸明廖政达
Owner GUANGXI NORMAL UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com