A method for preparing polycarbazole derivative nanofibers

A technology of nanofibers and derivatives, applied in the fields of nanotechnology, fiber chemical characteristics, single-component synthetic polymer rayon, etc., can solve the problems of low production efficiency, many factors to be controlled by equipment, and high cost of electrospinning equipment , to achieve the effect of improving efficiency

Active Publication Date: 2020-12-22
ZHENGZHOU UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the solution blending method, the cost of electrospinning equipment is high, the production efficiency is low, and the factors to be controlled by the equipment are many and complex (such as voltage, flow rate, spinning distance, temperature, humidity, etc.)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing polycarbazole derivative nanofibers
  • A method for preparing polycarbazole derivative nanofibers
  • A method for preparing polycarbazole derivative nanofibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A kind of preparation of polycarbazole derivative nanofiber, the steps are as follows:

[0049] Step 1: Surface treatment of the silicon wafer: oxidize the silicon wafer for 1 hour by irradiating a P100 type silicon wafer of 1 cm×1 cm with ozone generated by ultraviolet light.

[0050] Step 2: Select PCDTBT with a weight-average molecular weight of 34.9kg / mol and PEO with a molecular weight of 35 kg / mol as raw materials, and dissolve them in chlorobenzene at a mass ratio of PCDTBT:PEO of 1:1 (each 10 mg of PCDTBT and PEO) to obtain a total Mixed solution, the sum of the mass percentages of PCDTBT and PEO in the blended solution is 0.1 wt%.

[0051] Step 3: The blended solution was placed in a hot stage at 70°C and heated for 6h until the solute was dissolved.

[0052] Step 4: take the surface-treated silicon wafer as the substrate, and use a spin coater to spin at a speed of 3000 rpm for 30 seconds to prepare a film to obtain a PCDTBT and PEO blend film with a thicknes...

Embodiment 2

[0056] A preparation of polycarbazole derivative nanofibers, the steps of which are basically the same as in Example 1, and the similarities will not be repeated, except that the sum of the mass percentages of PCDTBT and PEO in the blending solution is 0.25wt %, PCDTBT and PEO blend films with a thickness of about 15nm were obtained.

[0057] Such as figure 2 As shown, the PCDTBT film on the silicon wafer has a network morphology composed of nanofibers and aggregates, and the width of the PCDTBT nanofibers is about 20nm.

Embodiment 3

[0059] A preparation of polycarbazole derivative nanofibers, the steps of which are basically the same as in Example 1, and the similarities will not be repeated, except that the sum of the mass percentages of PCDTBT and PEO in the blending solution is 0.5wt %, PCDTBT and PEO blend films with a thickness of about 20nm were obtained.

[0060] Such as image 3 As shown, the PCDTBT film on the silicon wafer in figure a is a network morphology composed of nanofibers and aggregates, in which the width of PCDTBT nanofibers is about 20nm. The diagram of conductive atoms in b shows that PCDTBT nanofibers have obvious electrical signals and form a conductive network together with PCDTBT aggregates.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a polycarbazole derivative nanofiber. The method comprises the following steps that surface treatment is carried out on a silicon chip; raw materials PCDTBT and PEO are added into a solvent to prepare a blended solution; the blended solution is placed on a heating stage until solute is dissolved; the treated silicon chip serves as a substrate, and a rotating coating machine is utilized to prepare blending film through a rotating coating method; and the blending film is washed and blow-dried with a nitrogen gun to obtain nanofibrous PCDTBT film. The method for preparing the polycarbazole derivative nanofiber has the advantages that the difficulty of conjugated macromolecular chain motion represented by PCDTBT is overcome, a method for preparinga conjugated macromolecular nanofiber simply and easily is provided, and the method is conductive to improving the efficiency of PCDTBT-based photoelectric device in the production practice.

Description

technical field [0001] The invention belongs to the technical field of nanofiber preparation, and in particular relates to a method for preparing polycarbazole derivative nanofibers. Background technique [0002] Polycarbazole derivatives, full name poly[[9-(1-octylnonyl)-9H-carbazole-2,7-diyl]-2,5-thiophenediyl-2,1,3-benzothiadiyl Azole-4,7-diyl-2,5-thiophenediyl], English abbreviation PCDTBT. As a conjugated polymer, it has higher thermal stability and narrower optical band gap than the widely studied poly(3-hexylthiophene) (P3HT), so organic photovoltaic devices based on PCDTBT It is expected to replace P3HT-based devices. In addition, since PCDTBT is synthesized by the copolymerization of carbazole and benzothiadiazole, it has both electron acceptor and donor properties, which further expands its applicable range. Studies have shown that increasing the crystallinity of materials or preparing crystal structures such as nanofibers can significantly improve the charge tr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/74B82Y40/00
CPCB82Y40/00D01F6/74
Inventor 陈静波井磊张彬
Owner ZHENGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap