High adhesion waterborne wood coating and manufacturing method thereof
A wood coating and high-adhesion technology, applied in coatings and other directions, can solve the problems of high formaldehyde content in organic polymers, poor sealing ability, peeling, etc., to improve environmental performance and functionality, excellent adhesion, and cost saving. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0028]A kind of high-adhesion water-based wood coating, the water-based wood coating is water-based acrylic resin 70Kg, sodium silicate 18Kg, potassium hydroxide 1.5Kg, titanium dioxide powder 0.3Kg, active carbon powder 2Kg, CNC cellulose nano crystal 8Kg by weight. , Tackifier extracted from goat horn 35Kg, blocked isocyanate 3Kg, water-based defoamer 0.3Kg, water-based adhesion promoter extracted from peach branch 10Kg as raw materials, with deionized water as the medium, 80 ℃ -85 The preparation process of the tackifier includes soaking, dicing, boiling, purification, and concentration; the preparation process of the water-based adhesion promoter includes foaming, microbial wall breaking, collagen release and activation, and concentration.
[0029] A kind of manufacture method of high-adhesion waterborne woodware coating, comprises the following steps:
[0030] 1) Raw material preparation
[0031] ① Raw material preparation: Prepare water-based acrylic resin 70Kg, sodium ...
Embodiment 2
[0047] The whole is consistent with Example 1, the difference is:
[0048] A kind of high adhesion water-based woodware coating, this water-based woodware coating is by weight water-based acrylic resin 80Kg, sodium silicate 15Kg, ammonium hydroxide 1Kg, titanium dioxide powder 0.2Kg, active carbon powder 1Kg, CNC cellulose nanocrystal 5Kg, Tackifier extracted from goat horn 30Kg, blocked isocyanate 2Kg, water-based defoamer 0.2Kg, water-based adhesion promoter extracted from peach branch 8Kg as raw materials, deionized water as medium, 70°C-75°C The preparation process of the tackifier includes infiltration, dicing, stewing, purification, and concentration; the preparation process of the water-based adhesion promoter includes foaming, microbial wall breaking, collagen release and activation, and concentration.
[0049] A kind of manufacture method of high-adhesion waterborne woodware coating, comprises the following steps:
[0050] 1) Raw material preparation
[0051] ① Raw ...
Embodiment 3
[0063] The whole is consistent with Example 1, the difference is:
[0064] A high-adhesion water-based wood coating, the water-based wood coating is based on 75Kg of water-based acrylic resin, 16Kg of sodium silicate, 0.6Kg of sodium hydroxide, 0.5Kg of ammonium hydroxide, 0.25Kg of titanium dioxide powder, and 1.5Kg of activated carbon powder in parts by weight. , CNC cellulose nanocrystal 6Kg, tackifier extracted from goat horn 32Kg, blocked isocyanate 2.5g, water-based defoamer 0.25Kg, water-based adhesion promoter extracted from peach branch 9Kg as raw materials, deionized Water is the medium, and it is fully reacted at 75°C-80°C; the preparation process of the tackifier includes infiltration, dicing, stewing, purification, and concentration; the preparation process of the water-based adhesion promoter includes foaming, microbial wall breaking, Collagen is released, activated and concentrated.
[0065] A kind of manufacture method of high-adhesion waterborne woodware coat...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Kinematic viscosity | aaaaa | aaaaa |
Kinematic viscosity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com