A kind of aluminum template release agent of high turnover times ultraviolet light curing and preparation method thereof

An ultraviolet light, aluminum template technology, applied in coatings, epoxy resin coatings, etc., can solve the problems of low cycle turnover, high film-forming energy consumption, coating pollution, etc., to achieve convenient on-site operation, no three waste pollution, Energy saving effect

Active Publication Date: 2021-10-08
HUNAN HUITIAN HIGH MOLECULAR TECH CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The object of the present invention is to provide a high-turnover UV-cured aluminum template release agent and a preparation method thereof, to solve the problems of high film-forming energy consumption, low cycle turnover, and peeled-off coating in the release agent in the prior art. Technical problems such as layer contamination of concrete surfaces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aluminum template release agent of high turnover times ultraviolet light curing and preparation method thereof
  • A kind of aluminum template release agent of high turnover times ultraviolet light curing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Weigh 1 part of acrylic acid, 2 parts of hydroxyethyl acrylate, 2 parts of isophthalic acid, 4 parts of phthalic anhydride, 1 part of trimellitic anhydride, 1 part of epichlorohydrin, 2 parts of ethylene glycol diglycidyl ether, epoxy resin Add 3 parts into a three-necked flask equipped with stirring, heating and cooling devices, heat and stir, control the temperature in the reactor to 80-130°C, stop heating when the acid value is less than 1mg KOH / g and cool to room temperature to obtain the modified permanent acrylic epoxy resin.

[0029] Raise the temperature of the stainless steel reaction kettle equipped with a disc dispersion stirring device to 30°C, add 7 parts of modified acrylic epoxy resin, 2 parts of UV monomer diluent pentaerythritol triacrylic acid monomer diluent, adhesion promoter A 0.5 part of hydroxyethyl acrylate phosphate, 0.5 part of leveling agent MONENG-1153, 0.3 part of surface slip agent GWN-N, ultraviolet photoinitiator (2,4,6-trimethylbenzoyl) ...

Embodiment 2

[0031] Weigh 2 parts of acrylic acid, 3 parts of hydroxyethyl acrylate, 1 part of isophthalic acid, 5 parts of phthalic anhydride, 1 part of trimellitic anhydride, 2 parts of epichlorohydrin, 1 part of ethylene glycol diglycidyl ether, epoxy resin Add 3 parts into a three-necked flask equipped with stirring, heating and cooling devices, heat and stir, control the temperature in the reactor to 80-130°C, stop heating when the acid value is less than 1mg KOH / g and cool to room temperature to obtain the modified modified acrylic epoxy resin.

[0032] Heat the stainless steel reaction kettle equipped with a disc dispersion stirring device to 40°C, add 7 parts of modified acrylic epoxy resin, 2 parts of UV monomer diluent trimethylolpropane triacrylate, adhesion promoter 0.5 parts of ethylene glycol diglycidyl ether dimethacrylate phosphate, 0.5 parts of leveling agent XYS-5630A, 0.3 parts of surface slip agent GWC-L, ultraviolet photoinitiator 2-hydroxy-methyl-1- 0.5 parts of phen...

Embodiment 3

[0034] Weigh 2 parts of acrylic acid, 3 parts of hydroxyethyl acrylate, 2 parts of isophthalic acid, 4 parts of phthalic anhydride, 2 parts of trimellitic anhydride, 2 parts of epichlorohydrin, 2 parts of ethylene glycol diglycidyl ether, epoxy resin Add 4 parts into a three-necked flask equipped with stirring, heating and cooling devices, heat and stir, control the temperature in the reactor to 80-130°C, stop heating when the acid value is less than 1mg KOH / g and cool to room temperature to obtain the modified permanent acrylic epoxy resin.

[0035] Raise the temperature of the stainless steel reaction kettle equipped with a disc dispersion stirring device to 50°C, add 8 parts of modified acrylic epoxy resin, 1 part of UV monomer diluent hexanediol diacrylate, (meth)acrylic acid iso 1 part of bornyl ester, 0.5 part of adhesion promoter glyceryl dimethacrylate phosphate, 0.5 part of leveling agent BYK-306, 0.3 part of surface slip agent GWA-L, 0.3 part of ultraviolet photoinit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-turnover UV-cured aluminum template release agent, which comprises the following components calculated in parts by weight: 6-10 parts of modified acrylic epoxy resin, 1-3 parts of UV monomer diluent, and 0.1-0.6 parts of force accelerator, 0.1-0.6 parts of leveling agent, 0.1-0.4 parts of surface slippery agent, 0.3-0.9 parts of ultraviolet photoinitiator; modified acrylic epoxy resin is made of acrylic acid, hydroxyethyl acrylate, methane It is prepared by modifying epoxy resin with one or more of phthalic acid, phthalic anhydride, trimellitic anhydride, ethylene glycol diglycidyl ether, and epichlorohydrin. The present invention also provides a preparation method of the above-mentioned release agent. The release agent of the present invention is coated on the aluminum alloy formwork, and is irradiated with ultraviolet light at room temperature to make it solidify into a film. It is used in the concrete pouring process. The demoulding quality of the concrete is good, the surface is smooth and pollution-free, and there is no concrete on the surface of the formwork. Residue, the template can be used up to 100 times after one application of the release agent, prolonging the service life of the template.

Description

technical field [0001] The invention belongs to the field of auxiliary agents for building materials, and in particular relates to a high-turnover UV-cured aluminum template release agent and a preparation method thereof. Background technique [0002] Concrete molding needs to be fixed with the help of templates, and the templates will be removed after the concrete has formed a certain strength. In concrete pouring, if the product is connected with the formwork, it will not only easily damage the product, but also cause difficulty in removing and cleaning the formwork, high labor intensity and low production efficiency. [0003] Concrete release agent is a preparation that can reduce or prevent the adhesion between concrete and the formwork surface, and there are many types of release agents currently in use. According to the appearance, the release agent can be divided into solid, solution, emulsion and paste; according to the effect, it can be divided into one-time and lo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/10
CPCC09D163/10
Inventor 凌立志李本祥肖勋陈玉文
Owner HUNAN HUITIAN HIGH MOLECULAR TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products