A kind of preparation method of high wear-resistant uv matte coating and the preparation method of uv matte coating

A high wear-resistant, matte technology, applied in the direction of coating, etc., can solve the problems of poor dispersion, poor stability, easy-to-return coarse powder particle size distribution range, etc., to improve scratch resistance, improve product yield and Improve production efficiency and improve the effect of insufficient surface scratch resistance

Active Publication Date: 2021-10-29
GUANGZHOU SHENWEI NEW MATERIAL TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention provides a method for preparing a highly wear-resistant UV matte coating in order to overcome the defects of poor dispersibility, poor stability, easy coarsening of the powder after dispersion and large particle size distribution range of the powder described in the above-mentioned prior art. The high wear-resistant UV matte coating prepared by the provided preparation method has good dispersibility and good stability, which well solves the problem of dispersion and wettability of organic polymers and inorganic powders in high wear-resistant UV matte coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high wear-resistant uv matte coating and the preparation method of uv matte coating
  • A kind of preparation method of high wear-resistant uv matte coating and the preparation method of uv matte coating
  • A kind of preparation method of high wear-resistant uv matte coating and the preparation method of uv matte coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] 1. Preparation of high wear-resistant matte coating

[0059] Add 6.68g of photoinitiator 1-hydroxy-cyclohexyl-phenyl ketone to 22.12g of pentaerythritol triacrylate and 8.44g of 1,6-hexanediol diacrylate and stir at low speed until completely dissolved, add 2.61g of disperse Agent Tegodispers628, 0.39g defoamer BYK-067A continue to stir at low speed, then add 5.35g C803 matting agent (produced by Grace Company), 3.48g polyethylene wax PEW-0851 (produced by Nanjing Tianshi Wax Powder) and continue to stir at low speed 1h, then add 0.19g of leveling agent BYK-310, 29.52g of B-619W (manufactured by Guangdong Boxing) and 21.22g of 230SH-T70 (manufactured by DSM) and stir for 30min at high speed, and use it after the powder is completely wetted Grind and disperse twice with a three-roll machine, and finally stir and disperse the mixed solution at high speed for 30 minutes to obtain a high wear-resistant matte coating.

[0060] 2. Performance of high wear-resistant matte coa...

Embodiment 2

[0071] 1. Preparation of high wear-resistant matte coating

[0072] Add 4.24 g of 1-hydroxy-cyclohexyl-phenyl ketone and 1.41 g of 2,4,6-trimethylbenzoyldiphenylphosphine oxide to 12.66 g of ethoxylated modified tris Methylolpropane triacrylate EM2380TF and 8.47g of 1,6-hexanediol diacrylate were stirred at medium and low speed until completely dissolved, then 2.9g of dispersant Tegodispersers670 and 0.48g of defoamer TegoAirex96 were added and 8.47g was added after stirring evenly at low speed M7 matting agent (produced by Perguang Company), 3.38g polytetrafluoroethylene wax PTFE-0101 (produced by Nanjing Tianshi Wax Powder) were stirred at a low speed for 1h, and then 38.61g B-912 and 19.31g B-375 (produced by Guangdong Boxing Production) Stir at low speed until uniform, finally add 0.10g of leveling agent Flow370 and stir at high speed for 30min, after the powder is completely wetted, use a three-roll machine to grind and disperse twice, and finally stir and disperse the gr...

Embodiment 3

[0084] 1. Preparation of high wear-resistant matte coating

[0085] Add 6g of photoinitiator 1-hydroxy-cyclohexyl-phenyl ketone to 22g of dipentaerythritol hexaacrylate and stir at low speed until completely dissolved, add 2.9g of dispersant BYK-2013, 0.25g of defoamer BYK-065, low speed Stir evenly, then add 11g M7 matting agent (produced by Poguang Company), 3.6g YN-L001s matting agent (produced by Xiangyang Yinuoxing Chemical Industry), 3.6g polytetrafluoroethylene wax PTFE-0101 (produced by Nanjing Tianshi wax powder) and continue Stir and disperse at low speed for 1 hour, then add 51g of B-919B (manufactured by Guangdong Boxing) and stir at low speed until uniform, and finally add 0.15g of leveling agent BYK-333 and stir at high speed for 30 minutes, and grind with a three-roller machine after the powder is completely wet Disperse twice, and finally stir and disperse the ground and dispersed mixture for another 30 minutes to obtain a high wear-resistant matte coating.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a high wear-resistant UV matte coating, which comprises the following steps: S1. firstly mix a photosensitive monomer, a photoinitiator, a dispersant and a defoamer evenly, and let it stand until the defoaming is complete, Obtain mixed liquid A; S2. Add matting powder and matting wax to mixed liquid A of S1. at low speed to make the powder fully wet, then add photosensitive prepolymer and smoothing agent and stir at high speed Evenly, mixed solution B is obtained; S3. Mechanically grind and disperse the mixed solution B of S2. to obtain mixed solution C; S4. Stir the mixed solution C of S3. at a high speed to obtain a high wear-resistant UV matte coating. The low-viscosity, low-speed, low-foam stirring pre-dispersion method, followed by high-speed stirring, grinding and finally high-speed stirring, can effectively solve the problems of easy coarsening of powder after dispersion and large particle size distribution range of powder. The preparation of the coating adopts a high-energy and high-speed curing process under the protection of nitrogen, which can effectively improve the insufficient scratch resistance of the surface caused by oxygen inhibition during thin coating.

Description

technical field [0001] The invention relates to the technical field of coatings, more specifically, to a method for preparing a high-wear-resistant UV matte coating and a method for preparing the UV matte coating. Background technique [0002] In the field of consumer electronics, protective and packaging films are needed for process protection and product protection packaging before leaving the factory. Most of the commonly used materials are soft materials such as OPP and BOPP. In the decoration industry, PVC film, as a decorative film material with the characteristics of rich patterns, clear, good layering, high simulation and convenient construction, has developed rapidly in furniture decoration, decoration industry, car interior decoration and other applications and has become a new type of surface decoration. The materials sector dominates. In the field of sealing, graphite gaskets have good corrosion resistance, high and low temperature resistance, compression resili...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D4/02C09D7/65
CPCC09D4/00C09D7/65
Inventor 袁慧雅张涛王锐涛
Owner GUANGZHOU SHENWEI NEW MATERIAL TECH