Ultraviolet irradiation cross-linked cable material

A cross-linked cable, ultraviolet light technology, used in circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problems of low working environment temperature, heat resistance, etc., to improve thermal performance, good heat and cold resistance , the effect of improving performance

Inactive Publication Date: 2019-03-19
上海电缆厂(南京)有限公司
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a UV-irradiated cross-linked cable material to solve the problem of low working environment temperature and heat resistance of the UV-irradiated cross-linked polyethylene insulating material in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A cable material cross-linked by ultraviolet light irradiation, comprising the following components in parts by mass: 20 parts of high-density polyethylene, 80 parts of low-density polyethylene, 30 parts of flame retardant, 6 parts of melamine cyanurate, epoxy 2 parts of soybean oil, 0.5 part of ultraviolet absorber, 0.2 part of coupling agent, 1 part of antioxidant, 0.2 part of stearic acid.

[0021] The degree of polymerization of the high-density polyethylene is 1200.

[0022] The degree of polymerization of the low density polyethylene is 1000.

[0023] The epoxy value of the epoxidized soybean oil is greater than 6.6%.

[0024] The ultraviolet absorber is bisphenol A disalicylate.

[0025] The flame retardant is ammonium polyphosphate.

[0026] The coupling agent is vinyltrimethoxysilane.

[0027] The purity of the melamine cyanurate is greater than 99.9%.

[0028] The stearic acid has a melting point of 60°C.

Embodiment 2

[0030] A cable material cross-linked by ultraviolet light irradiation, comprising the following components in parts by mass: 30 parts of high-density polyethylene, 90 parts of low-density polyethylene, 40 parts of flame retardant, 7 parts of melamine cyanurate, epoxy 3 parts of soybean oil, 3 parts of ultraviolet absorber, 0.3 part of coupling agent, 3 parts of antioxidant, 0.3 part of stearic acid.

[0031] The degree of polymerization of the high-density polyethylene is 1250.

[0032] The degree of polymerization of the low density polyethylene is 1050.

[0033] The epoxy value of the epoxidized soybean oil is greater than 6.6%.

[0034] The ultraviolet absorber is bisphenol A disalicylate.

[0035] The flame retardant is ammonium polyphosphate.

[0036] The coupling agent is vinyltrimethoxysilane.

[0037] The purity of the melamine cyanurate is greater than 99.9%.

[0038] The stearic acid has a melting point of 65°C.

Embodiment 3

[0040] A cable material cross-linked by ultraviolet light irradiation, comprising the following components in parts by mass: 50 parts of high-density polyethylene, 100 parts of low-density polyethylene, 50 parts of flame retardant, 8 parts of melamine cyanurate, epoxy 4 parts of soybean oil, 5 parts of ultraviolet absorber, 0.5 part of coupling agent, 5 parts of antioxidant, 0.4 part of stearic acid.

[0041] The degree of polymerization of the high-density polyethylene is 1300.

[0042] The degree of polymerization of the low-density polyethylene is 1100.

[0043] The epoxy value of the epoxidized soybean oil is greater than 6.6%.

[0044] The ultraviolet absorber is bisphenol A disalicylate.

[0045] The flame retardant is ammonium polyphosphate.

[0046] The coupling agent is vinyltrimethoxysilane.

[0047] The purity of the melamine cyanurate is greater than 99.9%.

[0048] The stearic acid has a melting point of 68°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultraviolet irradiation cross-linked cable material. The ultraviolet irradiation cross-linked cable material comprises, by weight, 20-50 parts of high-density polyethylene,80-100 parts of low-density polyethylene, 30-50 parts of flame retardants, 6-8 parts of melamine cyanurate, 2-4 parts of epoxidized soybean oil, 0.5-5 parts of ultraviolet absorbers, 0.2-0.5 part of coupling agents, 1-5 parts of antioxidants and 0.2-0.4 part of stearic acid. The ultraviolet irradiation cross-linked cable material has the advantages that the thermal properties and the temperature resistance of the ultraviolet irradiation cross-linked cable material can be improved, and accordingly the problems of low work environment temperatures and heat intolerance of existing ultraviolet irradiation cross-linked polyethylene insulation materials can be effectively solved by the aid of the ultraviolet irradiation cross-linked cable material.

Description

technical field [0001] The invention belongs to the technical field of cable materials, in particular to an ultraviolet light irradiation cross-linked cable material. Background technique [0002] With polyolefin as the main raw material mixed with an appropriate amount of enhanced cross-linking photoinitiation system, under certain conditions, it is irradiated with ultraviolet light, and the photoinitiator absorbs ultraviolet light of a specific wavelength to generate active macromolecular free radicals. A series of rapid cross-linking reactions with other additives, the individual polyethylene long-chain macromolecules are chemically bonded to form a three-dimensional network cross-linked polyethylene supramolecular structure. The cross-linked polyolefin material has excellent high temperature resistance, solvent resistance, excellent electrical properties and significantly enhanced mechanical properties, etc. Ultraviolet light irradiation crosslinking wire and cable is t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L91/00C08K13/02C08K3/32C08K5/3492C08K5/09C08K5/134H01B3/44
CPCC08K2003/323C08L23/06C08L2201/08C08L2203/202C08L2205/025C08L2205/03C08L2207/062C08L2207/066C08L2312/06H01B3/441C08L91/00C08K13/02C08K3/32C08K5/34928C08K5/09C08K5/1345
Inventor 程江
Owner 上海电缆厂(南京)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com