A kind of nylon polymer powder material and preparation method thereof

A technology of powder material and nylon powder, which is applied in the field of additive manufacturing, can solve the problems of inability to form heat absorption and conduction of heat medium and heat preservation temperature field, poor absorption effect of nylon powder, slow heat conduction speed, etc., so as to improve the performance of parts and prevent carbon Black agglomeration, effect of improving fluidity

Active Publication Date: 2020-06-30
HUNAN FARSOON HIGH TECH CO LTD
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The prior art still has the problem of poor absorption effect of nylon powder. The conventional nylon powder material and heat medium are mixed together by stirring. The heat medium only exists on the outer surface of the nylon powder material, while the inner surface of the nylon powder material does not There is no heat medium, so the heat transfer can only be transferred from the outer surface of the nylon powder material to the inner surface, the heat conduction speed is slow, the heat absorption effect is not good, and it is impossible to form a heat absorption conduction and heat preservation temperature field that contains heat medium on both the inner and outer surfaces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nylon polymer powder material and preparation method thereof
  • A kind of nylon polymer powder material and preparation method thereof
  • A kind of nylon polymer powder material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] (1) Add 100 parts of nylon 1212 pellets, 1 part of carbon black with a particle size of 1 μm, and 600 parts of methanol into the polymerization kettle. The whole solvent precipitation method is divided into four stages. The first stage is the stage of temperature rise and pressure increase. The stirring rate is controlled at 200r / min, the temperature is raised to 200°C, and the pressure is raised to 1.8Mpa; the second stage is the stage of temperature drop and pressure drop. Stirring is controlled The speed is 600r / min, the temperature is lowered to 100°C, and the pressure is reduced to 1.0Mpa; the third stage is heat preservation and pressure holding for 100min, the control stirring rate is 50r / min, heat preservation is 100°C, and pressure holding is 1.0MPa; the fourth stage is rapid The temperature was lowered to normal temperature and normal pressure, and the stirring rate was 800r / min to finally obtain nylon powder grown with the heat medium as the nucleating agent, ...

Embodiment 2

[0049] (1) Add 100 parts of nylon 1010 pellets, 0.1 part of graphene with a particle size of 0.1 μm, and 700 parts of ethanol into the polymerization kettle. The whole solvent precipitation method is divided into four stages. The first stage is the stage of temperature rise and pressure, and the stirring rate is controlled at 220r / min, the temperature is raised to 200°C, and the pressure is raised to 1.8Mpa; the second stage is the stage of temperature drop and pressure drop, and the stirring is controlled The speed is 520r / min, the temperature is lowered to 110°C, and the pressure is reduced to 1.1Mpa; the third stage is heat preservation and pressure holding for 40min, the control stirring rate is 70r / min, heat preservation is 110°C, and pressure holding is 1.1MPa; the fourth stage is rapid The temperature was lowered to normal temperature and normal pressure, and the stirring rate was 640r / min to finally obtain nylon powder grown with heat medium as a nucleating agent, and t...

Embodiment 3

[0054] (1) Add 100 parts of nylon 6 pellets, 10 parts of ferric oxide powder with a particle size of 10 μm, and 1000 parts of dimethylformamide into the polymerization kettle. The whole solvent precipitation method is divided into four stages. The first stage is the stage of temperature rise and pressure increase. The stirring rate is controlled at 260r / min, the temperature is raised to 200°C, and the pressure is raised to 1.8Mpa; the second stage is the stage of temperature drop and pressure drop. Stirring is controlled The speed is 570r / min, the temperature is lowered to 120°C, and the pressure is reduced to 1.2Mpa; the third stage is heat preservation and pressure holding for 70min, the control stirring rate is 70r / min, heat preservation is 120°C, and pressure holding is 1.2MPa; the fourth stage is rapid The temperature was lowered to normal temperature and pressure, and the stirring rate was 700r / min to finally obtain the nylon 6 powder grown with the heat medium as the nuc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a preparation method of a nylon polymer powder material. The preparation method comprises the following steps: adding the following components into a polymerizing pot in percentage by mass: 85-99.9% of nylon aggregate and 0.1-15% of a thermal medium material, adding a solvent, and preparing a nylon powder material taking the thermal medium as a nucleating agent by adopting asolvent precipitation method; adding 20 parts of nylon powder material and 0.1-1.5 parts of carbon black into a mixing tank, and performing the first high-speed mixing so as to prepare a nylon and carbon black mixed powder material; adding the nylon and carbon black mixed powder material, 0.1-1 part of a flow promoter and 80 parts of the nylon powder material into the mixed powder barrel, performing the second high-speed mixing and screening, thereby obtaining the nylon polymer powder material. By adopting the nylon powder taking the thermal medium material as the nucleating agent and the high-speed mixing, the carbon black is uniformly attached onto the nylon powder surface, so that the nylon powder in the prior art is applied to fiber laser sintering, the surface quality of the parts isexcellent, the structure is fine, and the overall performance is excellent.

Description

technical field [0001] The invention belongs to the technical field of additive manufacturing, and in particular relates to a nylon polymer powder material and a preparation method thereof. Background technique [0002] The selective sintering of multiple powder layers by laser sintering is a method of manufacturing three-dimensional objects that allows three-dimensional entity. This method is primarily accomplished using thermoplastic polymers. Patents US6136948 and WO9606881 describe this method of manufacturing three-dimensional objects using powdered polymers in detail. [0003] The existing mainstream selective laser sintering mainly uses CO2 lasers with a wavelength of 10600nm, which corresponds to the mid-infrared region. Nylon powder materials have a higher wavelength absorption rate in this range, but when nylon powder materials are used in fiber laser sintering, the The wavelength has an extremely low absorption rate, making it difficult to apply existing nylon ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L77/06C08L77/02C08K9/10C08K3/04C08K3/22C08K3/08B29C64/153B33Y70/00
CPCB29C64/153B33Y70/00C08K3/04C08K3/042C08K3/08C08K3/22C08K9/10C08K2003/085C08K2003/2272C08K2201/003C08L77/02C08L2205/02C08L2205/24C08L77/06
Inventor 鲍光许小曙文杰斌曾思齐尹志勇赖端
Owner HUNAN FARSOON HIGH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com