Tantalum steel composite plate and preparation method thereof

A composite plate and steel plate technology, applied in chemical instruments and methods, lamination, coating, etc., can solve problems such as unsatisfactory continuous production, high production site requirements, exhaust gas pollution, etc., and achieve a wide range of product sizes. The effect of good environment and simple process

Active Publication Date: 2019-04-05
NANJING YOUTIAN METAL TECH
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Explosive composite method is to use the huge energy generated by explosives at the moment of explosion to accelerate two metal plates to a very high speed and then collide rapidly for welding. However, the production noise is large and exhaust gas pollution is generated, which req

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tantalum steel composite plate and preparation method thereof
  • Tantalum steel composite plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0026] A preparation method of a tantalum steel composite plate specifically includes the following steps:

[0027] 1) Choose a carbon steel plate with a thickness of 100mm and a tantalum plate with a thickness of 10mm, and polish the surface of the tantalum plate and steel plate to be bonded, so that the surface to be bonded is free of oxide layers, impurities and voids, and presents a fresh metal surface;

[0028] 2) Prepare a release agent, take alumina powder and polyvinyl chloride powder with a mesh number greater than 200 meshes and mix with water according to the ratio of (2-3): (1-2): 100, stir evenly, and evenly apply to the tantalum plate Non-bonding surface, thickness of 0.3-0.8mm, dry statically or dry in an oven, the temperature of the oven should not be higher than 180℃;

[0029] 3) Such as figure 1 As shown, the side where the tantalum plate is coated with the release agent 5 is placed opposite, and the tantalum plate is sealed and welded, and a vent hole is left at on...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a tantalum steel composite plate and a preparation method thereof. The tantalum steel composite plate comprises a tantalum plate layer and a steel plate layer, and a diffusionlayer is formed between the tantalum plate layer and the steel plate layer. The preparation method of the tantalum steel composite plate comprises the following steps: material selection, surface treatment, separant painting, tantalum plate welding, assembling (including periphery welding, ventilation tube welding, gas tightness inspection, vacuumizing and inert gas filling), heating, rolling, heat treatment, leveling, trimming, surface treatment, finishing composite plate. This method has low requirement for production site and is high in production efficiency and low in production cost.

Description

technical field [0001] The invention discloses a composite material and a manufacturing method thereof, in particular to a tantalum steel composite plate and a manufacturing method thereof. Background technique [0002] Tantalum is a rare refractory metal with high melting point, low vapor pressure and small thermal expansion coefficient. Since the surface of tantalum is very easy to form dense and stable tantalum pentoxide (Ta2O 5 ) protective film, showing very excellent corrosion resistance, no matter in cold or hot state, it does not react to hydrochloric acid, concentrated nitric acid and aqua regia. At room temperature, tantalum has no effect on alkali solution, chlorine gas, bromine water, dilute sulfuric acid and many other agents. In addition, tantalum and its alloys also have good high temperature strength, excellent processing performance, good welding performance and thermal conductivity. In view of its good comprehensive performance, tantalum has broad applic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B37/00B32B37/06B32B15/01B32B15/18B32B3/24B32B33/00
CPCB32B3/266B32B15/013B32B15/18B32B33/00B32B37/00B32B37/06B32B2255/06
Inventor 魏洁陈怀浩
Owner NANJING YOUTIAN METAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap