Anticorrosive resin coating and production method thereof

A technology for anti-corrosion coatings and resins, applied in the direction of anti-corrosion coatings, epoxy resin coatings, coatings, etc., can solve the problems of general anti-corrosion coatings, inability to form long-term protective films, and unsatisfactory anti-corrosion effects, etc., and achieve simple preparation methods Mature, low cost, outstanding chemical resistance effect

Inactive Publication Date: 2019-04-19
TONGLING HUADONG FRP IND CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] There are many kinds of coatings in the building materials market, and there are few types of anti-corrosion coatings. Generally, the anti-corrosion effect of anti-corrosion coatings is average, the coating performance of coatings is weak, it is easy to evaporate, cannot form a long-term protective film, and the anti-corrosion effect is not ideal.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0011] Specific embodiment 1: a kind of resin anticorrosion coating, it is made up according to the parts by weight of following raw material: 12 parts of cellulose acetate butyrate, 12 parts of silyl acrylate, 15 parts of water-soluble epoxy acrylic resin, sodium bisulfite 6 parts 10 parts of silicone resin, 8 parts of calcium stearate, 7 parts of isooctyl acrylate, 8 parts of quartz sand, 5 parts of linseed oil, 8 parts of trimethylolpropane, 4 parts of hydrogenated styrene, 8 parts of carbon black , 6 parts of tackifier, 8 parts of rosin water, 5 parts of silicon dioxide powder, and 5 parts of molybdenum disulfide.

[0012] The tackifier is phenolic resin.

[0013] A kind of production method of resin anticorrosion coating is: the described ratio cellulose acetate butyrate, silyl acrylate, water-soluble epoxy acrylic resin, sodium bisulfite, organosilicon resin, calcium stearate, isooctyl acrylate , quartz sand, linseed oil, trimethylolpropane, hydrogenated styrene, carbon...

specific Embodiment 2

[0014] Specific embodiment 2: a kind of resin anticorrosion coating, it forms according to the weight portion of following raw material: 15 parts of cellulose acetate butyrate, 16 parts of silyl acrylate, 19 parts of water-soluble epoxy acrylic resin, 8 parts of sodium bisulfite , 13 parts of silicone resin, 10 parts of calcium stearate, 10 parts of isooctyl acrylate, 11 parts of quartz sand, 8 parts of linseed oil, 11 parts of trimethylolpropane, 8 parts of hydrogenated styrene, 11 parts of carbon black, 8 parts of tackifier, 12 parts of rosin water, 8 parts of silicon dioxide powder, 7 parts of molybdenum disulfide.

[0015] The tackifier is polyisobutylene.

[0016] A kind of production method of resin anticorrosion coating is: the described ratio cellulose acetate butyrate, silyl acrylate, water-soluble epoxy acrylic resin, sodium bisulfite, organosilicon resin, calcium stearate, isooctyl acrylate , quartz sand, linseed oil, trimethylolpropane, hydrogenated styrene, carbo...

specific Embodiment 3

[0017] Specific embodiment 3: a kind of resin anticorrosion coating, it is formed by the weight portion of following raw material: 18 parts of cellulose acetate butyrate, 20 parts of silyl acrylate, 22 parts of water-soluble epoxy acrylic resin, 11 parts of sodium bisulfite , 16 parts of silicone resin, 12 parts of calcium stearate, 12 parts of isooctyl acrylate, 14 parts of quartz sand, 10 parts of linseed oil, 14 parts of trimethylolpropane, 10 parts of hydrogenated styrene, 14 parts of carbon black, 10 parts of tackifier, 16 parts of rosin water, 10 parts of silicon dioxide powder, 9 parts of molybdenum disulfide.

[0018] The tackifier was zinc naphthenate.

[0019] A kind of production method of resin anticorrosion coating is: the described ratio cellulose acetate butyrate, silyl acrylate, water-soluble epoxy acrylic resin, sodium bisulfite, organosilicon resin, calcium stearate, isooctyl acrylate , quartz sand, linseed oil, trimethylolpropane, hydrogenated styrene, carb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anticorrosive resin coating and a production method thereof. The coating comprises, by weight, 12-18 parts of cellulose acetate butyrate, 12-20 parts of silyl acrylate, 15-22 parts of water-soluble epoxy acrylic resin, 6-11 parts of sodium bisulfite, 10-16 parts of silicone resin, 8-12 parts of calcium stearate, 7-12 parts of isooctyl acrylate, 8-14 parts of quartz sands, 5-10 parts of linseed oil, 8-14 parts of trimethylolpropane, 4-10 parts of hydrogenated styrene, 8-14 parts of carbon black, 6-10 parts of a tackifier, 8-16 parts of rosin water, 5-10 parts of silica powder and 5-9 parts of molybdenum disulfide. The anticorrosive resin coating has a wide application range, can be applied to the fields of large-area outdoor floor decoration, wall decoration and the like, and also has the advantages of low cost and high viscosity.

Description

technical field [0001] The invention belongs to the field of paint material manufacturing, and in particular relates to a resin anticorrosion paint and a production method thereof. Background technique [0002] Coatings with synthetic resin as the main film-forming substance are called synthetic resin coatings. Synthetic resin coatings are based on petrochemical products. They have various names and excellent performance, and have become the main varieties of modern coatings. High-molecular-weight polymer is a resin that has both or exceeds the inherent characteristics of natural resins. The mechanical properties, decoration and protection of resin coatings are superior to oil coatings and natural resin coatings. The service life of resin coatings is longer. Resin anti-corrosion coatings can be seen in interior decoration, outdoor floors, walls of public buildings, etc. Anti-corrosion coatings are generally divided into conventional anti-corrosion coatings and heavy-duty ant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/10C09D183/04C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2201/014C08L2205/035C09D5/08C09D7/61C09D7/63C09D7/65C09D163/10C08L83/04C08K13/02C08K3/36C08K5/098C08K5/053C08K3/04
Inventor 杨超汪小丽肖晓
Owner TONGLING HUADONG FRP IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap