A kind of preparation and regeneration method of iron complex type carbon film electric fenton cathode

A technology of complexation and carbon membrane, applied in chemical instruments and methods, water/sludge/sewage treatment, water/sewage treatment, etc. Low-level problems, to achieve the effect of good electrical reduction and regeneration performance, eliminating the need for stirring devices, and simple and convenient operation

Active Publication Date: 2021-11-09
JILIN NORMAL UNIV
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to provide a kind of preparation and regeneration method of iron-complexed carbon film gas diffusion electrode, this electrode is used as the negative electrode of electric Fenton system, active component iron is fixed on the electrode with the mode of ionic state complexation, Simultaneously press O 2 The direction of flow is done sequentially on the electrodes H 2 o 2 In-situ generation and Fenton reaction can solve the problems of poor diffusion and mass transfer, H 2 o 2 Low yield, Fe 2+ Problems such as easy complexation and inactivation and difficulty in reduction and regeneration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation and regeneration method of iron complex type carbon film electric fenton cathode
  • A kind of preparation and regeneration method of iron complex type carbon film electric fenton cathode
  • A kind of preparation and regeneration method of iron complex type carbon film electric fenton cathode

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] 1. Preparation method of gas diffusion electrode:

[0042] The chemical substance material used in the present invention is:

[0043] Nitrogen-doped graphitized carbon nanotubes: NCNT, purity>95%, outer diameter 10-30nm, length 5-15μm, nitrogen content 3.46wt%;

[0044] Graphene oxide dispersion: GO, the concentration is 4mg / mL;

[0045] Sodium hydroxide: NaOH, analytically pure;

[0046] Ferrous Sulfate Heptahydrate: FeSO 4 ·7H 2 O, analytically pure;

[0047] Polytetrafluoroethylene emulsion; PTFE, the concentration is 60wt%;

[0048] Absolute ethanol: C 2 h 6 O, analytically pure;

[0049] Acetone: CH 3 COCH 3 , analytically pure;

[0050] Deionized water: H2 O, resistivity ≥ 18MΩ;

[0051] Oxygen: O 2 , purity ≥ 99.999%;

[0052] Nitrogen: N 2 , purity ≥ 99.999%;

[0053] Anhydrous sodium sulfate: Na 2 SO 4 , analytically pure;

[0054] 4-Nitrophenol: C 6 h 5 NO 3 , analytically pure.

[0055] (1) Preparation of iron-complexed graphene oxide p...

Embodiment 2

[0089] The preparation steps and dosage of iron-complexed graphene oxide powder and iron-complexed carbon film gas diffusion electrode are the same as in Example 1.

[0090] use figure 2 The bubbling electric Fenton reactor shown treats methylene blue simulated wastewater. The specific test conditions are as follows: the anode is a graphite electrode (50 × 40mm), and the cathode is an iron-complexed carbon film gas diffusion electrode (50mm in diameter); the reaction solution is a mixed solution of 400mL of 0.1mol / L sodium sulfate and 10mg / L methylene blue, The pH value is not adjusted; the gas used in the reaction is compressed air, and the flow rate of the gas is 100mL / min; at 5mA / cm 2 The solution can be completely decolorized when the current density is reacted for 90 minutes, and the TOC removal rate of the solution can reach 60.3% when reacted for 300 minutes, which can effectively treat organic wastewater.

[0091] Regeneration of iron-complexed carbon film gas diffu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
clearance rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for preparing and regenerating an iron-complexed carbon film gas diffusion electrode applied to an electro-Fenton system. Prepared from the following components: nitrogen-doped graphitized carbon nanotubes, graphene oxide dispersion, sodium hydroxide, ferrous sulfate heptahydrate, polytetrafluoroethylene emulsion, absolute ethanol, acetone, deionized water, oxygen, nitrogen. Preparation method: (1) preparing iron-complexed graphene oxide powder (2) preparing iron-complexed carbon film gas diffusion electrode. Electrode regeneration method: install the gas diffusion electrode in the reactor, pass through nitrogen, put in the electrolyte, and perform electric reduction regeneration at a constant cathode potential. The regenerated electrode is washed with deionized water and dried. The gas diffusion electrode not only acts as the cathode in the reactor, but also completes the O 2 Catalytic reduction and OH generation reaction, and at the same time, the gas distribution effect is also taken into account, which promotes the mass transfer in the liquid phase region. The performance of the regenerated electrode is basically unchanged compared with the new electrode.

Description

technical field [0001] The invention relates to the technical field of preparation and application of electro-Fenton system cathode materials, in particular to a preparation and regeneration method of an iron-complexed carbon film gas diffusion electrode. Background technique [0002] Water resource pollution has become a global problem. Especially in recent years, the types of organic pollutants in water bodies have increased year by year, and their components are complex, highly toxic, and difficult to biodegrade. With the increasingly stringent environmental protection standards, some conventional treatment technologies are difficult to achieve satisfactory results in the treatment of refractory organic matter. Therefore, it is an urgent problem to seek efficient, economical and environmentally friendly advanced treatment technology to control the discharge of refractory organic pollutants or restore the polluted water environment. [0003] Fenton oxidation technology is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C02F1/461C02F1/72
Inventor 汤茜高永慧石淑云杨春维孙玉伟郜航李冰伦周昊
Owner JILIN NORMAL UNIV