Anti-crack and anti-corrosion inorganic artificial stone and its preparation method and application
An artificial stone and corrosion-resistant technology, applied in the field of building materials, can solve the problems of poor carbonation resistance, poor stability, easy deformation and cracking, etc., and achieve good crack resistance and corrosion resistance, high compressive strength, and strong market competitiveness Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment approach
[0078] In order to further improve the crack resistance of the inorganic artificial stone, as an optional embodiment of the present invention, the raw material of the crack-resistant and corrosion-resistant inorganic artificial stone further includes fibers.
[0079] The specific type of fiber is not specifically limited, preferably alkali-resistant glass fiber, carbon fiber, basalt fiber, polyvinyl alcohol fiber, polyacrylonitrile fiber, high-density polyethylene fiber, polyamide fiber, polyimide fiber, polypropylene fiber or Any one or a combination of at least two of aramid fibers.
[0080] The amount of fiber needs to be added according to the actual product performance. As an optional embodiment of the present invention, the weight fraction of fibers is 0.01-3.0%, typical but non-limiting weight fractions of fibers are 0.01%, 0.05%, 0.1%, 0.5%, 1.0%, 1.2%, 1.5%, 1.8%, 2.0%, 2.2%, 2.5%, 2.8%, 2.9%, or 3.0%.
[0081] As an optional embodiment of the present invention, the...
Embodiment 1
[0099] This embodiment provides a crack-resistant and corrosion-resistant inorganic artificial stone, which is mainly made of powder and water, and the weight of water is 14% of the weight of the powder;
[0100] Wherein, taking the powder as the basis for calculation, the powder includes the raw materials of the following weight fractions:
[0101] S95 grade granulated blast furnace slag powder 40.0%, granulated blast furnace slag activator 15.0%, aggregate 44.7%, 2651 water reducer 0.1% and coagulant lithium sulfate 0.20%.
[0102] Among them, aggregates include 17% of 20-40 mesh white quartz sand, 15.8% of 40-80 mesh quartz sand, 10.9% of 80-120 mesh quartz sand and 1.00% of 1-6mm colored tempered glass.
[0103] The preparation method of the anti-crack and corrosion-resistant inorganic artificial stone provided in this embodiment comprises the following steps:
[0104] The above raw materials are mixed and stirred (the fluidity of which is controlled by Blaine’s consisten...
Embodiment 2
[0106] This embodiment provides a crack-resistant and corrosion-resistant inorganic artificial stone, which is mainly made of powder and water, and the weight of water is 13% of the weight of the powder;
[0107] Wherein, taking the powder as the basis for calculation, the powder includes the raw materials of the following weight fractions:
[0108] S95 grade granulated blast furnace slag powder 36.0%, granulated blast furnace slag activator 8.0%, 42.5 grade anti-cracking double fast cement 10.0%, aggregate 45.93%, C900 water reducer 0.06% and coagulant lithium sulfate 0.01%.
[0109] Among them, aggregates include 21% of 20-40 mesh white quartz sand, 12.93% of 40-80 mesh quartz sand, 11.0% of 80-120 mesh quartz sand and 1.00% of 1-6mm colored tempered glass.
[0110] The preparation method of the anti-crack and corrosion-resistant inorganic artificial stone provided in this example is the same as that in Example 1.
PUM
| Property | Measurement | Unit |
|---|---|---|
| compressive strength | aaaaa | aaaaa |