A kind of hydrogenated petroleum resin and preparation method thereof

A hydrogenation petroleum resin and catalyst technology, which is applied in the field of petroleum resin processing, can solve the problems of affecting the hydrogenation effect of petroleum resin, inconvenience, and unsatisfactory production of petroleum resin, so as to achieve good catalytic effect, reduce use cost and improve service life Effect

Active Publication Date: 2019-12-27
乐清市智格电子科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the deepening of petroleum resin research, the requirements for petroleum resin in the market are getting higher and higher, and the output of petroleum resin with high quality and high softening point cannot meet the current demand, which brings us inconvenience.
[0004] At the same time, in today's petroleum resin preparation technology, the finished product contains a large amount of impurities and unsaturated bonds, so we generally carry out hydrogenation operation on petroleum resin to improve the quality of petroleum resin, but in the process of hydrogenation, petroleum Chloride ions and sulfur elements in resin will greatly affect the hydrogenation effect of petroleum resin, which will bring us great inconvenience

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrogenated petroleum resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] First prepare the raw materials, weigh the C5 fraction, isopentene, toluene and solvent in proportion, and set aside; prepare the first catalyst, weigh aluminum trichloride and methanesulfonic acid in proportion, and put the aluminum trichloride into the flask , add water to dissolve, then add methanesulfonic acid, stir magnetically, heat and distill until the liquid in the bottle becomes viscous, evaporate to dryness, and dry in a vacuum oven at 95°C for 2 hours to obtain the first catalyst; to prepare the second catalyst, press Proportionally weigh urea, ammonium molybdate tetrahydrate, cobalt nitrate hexahydrate, titanium sulfate, aluminum sulfate and ammonia water, dissolve titanium sulfate and aluminum sulfate in deionized water, slowly add ammonia water dropwise, and vigorously stir to adjust the pH to 8 , precipitation and aging for 2 hours, centrifugal filtration, repeated washing with deionized water until the filtrate has no sulfate radicals, drying at 110°C, a...

Embodiment 2

[0050] First prepare the raw materials, weigh the C5 fraction, isopentene, toluene and solvent in proportion, and set aside; prepare the first catalyst, weigh aluminum trichloride and methanesulfonic acid in proportion, and put the aluminum trichloride into the flask , add water to dissolve, then add methanesulfonic acid, stir magnetically, heat and distill until the liquid in the bottle becomes viscous, evaporate to dryness, and dry in a vacuum oven at 100°C for 2.5 hours to obtain the first catalyst; prepare the second catalyst, Weigh urea, ammonium molybdate tetrahydrate, cobalt nitrate hexahydrate, titanium sulfate, aluminum sulfate and ammonia water in proportion, dissolve titanium sulfate and aluminum sulfate in deionized water, slowly add ammonia water dropwise, and vigorously stir to adjust the pH to 8. Precipitation and aging for 2.5 hours, centrifugal filtration, repeated washing with deionized water until the filtrate has no sulfate radicals, drying at 120°C, and roa...

Embodiment 3

[0055] First prepare the raw materials, weigh the C5 fraction, isopentene, toluene and solvent in proportion, and set aside; prepare the first catalyst, weigh aluminum trichloride and methanesulfonic acid in proportion, and put the aluminum trichloride into the flask , add water to dissolve, then add methanesulfonic acid, stir magnetically, heat and distill until the liquid in the bottle becomes viscous, evaporate to dryness, and dry in a vacuum oven at 105°C for 3 hours to obtain the first catalyst; to prepare the second catalyst, press Proportionally weigh urea, ammonium molybdate tetrahydrate, cobalt nitrate hexahydrate, titanium sulfate, aluminum sulfate and ammonia water, dissolve titanium sulfate and aluminum sulfate in deionized water, slowly add ammonia water dropwise, and vigorously stir to adjust the pH to 8 , precipitation and aging for 3 hours, centrifugal filtration, repeated washing with deionized water until the filtrate has no sulfate radicals, drying at 130°C, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses hydrogenated petroleum resin and a preparation method thereof. Generally speaking, at present, all catalysts used for preparing the C5 petroleum resin are aluminum trichloride;however, aluminum trichloride is easy to decompose in water, so that the catalyst is easy to remove incompletely, a large amount of industrial wastewater is generated after the catalyst is used, theenvironment is polluted, and the quality of the generated C5 petroleum resin is influenced by residual chloride ions and aluminum ions in the petroleum resin. Aluminum trichloride reacts with methanesulfonic acid to synthesize aluminum methanesulfonate. The aluminum methanesulfonate does not decompose in water, has a good catalytic effect and high reaction activity, and is an environment-friendlycatalyst. The invention has the advantages of reasonable formula design and simple preparation process. The hydrogenated petroleum resin with good quality is effectively prepared, the softening pointis increased, impurities are reduced, meanwhile, the preparation process is optimized, the cost is saved, and the hydrogenated petroleum resin has better practicability and generalization performance.

Description

technical field [0001] The invention relates to the technical field of petroleum resin processing, in particular to a hydrogenated petroleum resin and a preparation method thereof. Background technique [0002] Petroleum resin is a kind of C5 and C9 fractions produced by petroleum cracking. It is a thermoplastic resin produced by pretreatment, polymerization, distillation and other processes. Petroleum resin is named for its source of petroleum derivatives. It has an acid value Low, good miscibility, water resistance, ethanol resistance and chemical resistance, chemical stability to acid and alkali, and good viscosity adjustment and thermal stability. [0003] With the deepening of petroleum resin research, the requirements for petroleum resin in the market are getting higher and higher, and the output of petroleum resin with high quality and high softening point cannot meet the current demand, which brings us inconvenience. . [0004] At the same time, in today's petroleu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F240/00C08F210/14C08F4/52C08F8/04
Inventor 陆春华姚瞻秋管伟
Owner 乐清市智格电子科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com