A kind of lightfast water-based environment-friendly real stone paint and preparation method thereof

A real stone paint, water-based technology, used in coatings, anti-corrosion coatings, etc., can solve the problems of poor light resistance of real stone paint, and achieve the goal of improving internal adhesion strength and stability, improving light resistance, and improving adhesion strength and stability. Effect

Active Publication Date: 2021-04-30
哈尔滨绿科科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a light-resistant water-based environmental protection real stone paint and its preparation method to solve the problem of poor light resistance of the real stone paint in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lightfast water-based environment-friendly real stone paint and preparation method thereof
  • A kind of lightfast water-based environment-friendly real stone paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The application also provides a preparation method for preparing any one of the above-mentioned light-resistant water-based environmental protection real stone paints, comprising the following steps:

[0034] 1) First add 20-23 parts of water-based acrylic resin emulsion to 80-85 parts of modified filling material, keep the constant temperature at 50°C, and fully stir for 8-10 minutes;

[0035] 2) Add 6-8 parts of film-forming aid and 2-3 parts of defoamer, stir for 8-15 minutes, cool down to room temperature naturally, and pack to obtain the finished product.

preparation example 1

[0038] The preparation method of modified filling material comprises the following steps:

[0039] 1) Soak 50 parts of quartz sand in 25 parts by weight of 15% glacial acetic acid aqueous solution and stir for 5 minutes, filter and dry;

[0040] 2) Add 5 parts of octyl 2-hydroxybenzoate to the dried quartz sand and mix and stir for 2 minutes;

[0041] 3) Add 5 parts of carboxymethyl cellulose, 4 parts of alcohol ether water-based co-solvent and 76 parts of deionized water and mix and stir for 5 minutes;

[0042] 4) Stop stirring, and filter out part of the liquid so that the solid content accounts for 50% of the total weight, that is, the modified filling material is obtained.

preparation example 2

[0044] The preparation method of modified filling material comprises the following steps:

[0045] 1) Soak 55 parts of quartz sand in 27 parts by weight of 20% glacial acetic acid aqueous solution and stir for 10 minutes, filter and dry;

[0046] 2) Add 8 parts of octyl 2-hydroxybenzoate to the dried quartz sand and mix and stir for 5 minutes;

[0047] 3) Add 8 parts of carboxymethyl cellulose, 5 parts of alcohol ether water-based co-solvent and 80 parts of deionized water and mix and stir for 10 minutes;

[0048] 4) Stop stirring, and filter out part of the liquid so that the solid content accounts for 50% of the total weight, that is, the modified filling material is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a light-fast water-based environment-friendly real stone paint and a preparation method thereof. By adding a modified filling material prepared, in the modified filling material, octyl 2-hydroxybenzoate can improve light resistance, and carboxymethyl cellulose can improve light resistance. Adhesion strength and stability of the internal structure, adding water-based co-solvent and deionized water to help dissolve and disperse, the glacial acetic acid aqueous solution can remove impurities in the quartz sand, and form pores to remove impurities to be filled, the pore structure can be fully utilized The effects of octyl 2-hydroxybenzoate and carboxymethyl cellulose, and improve internal bond strength and stability. In this technical scheme, water-based acrylic resin emulsion is used to give full play to its characteristics of weather resistance, light resistance, heat resistance, corrosion resistance, and fullness of the coating film, and then a certain proportion of film-forming aids and defoaming agents are added to obtain a light-fast water-based Environmentally friendly real stone paint has the characteristics of good light resistance, strong adhesion, stable structure and no powder drop.

Description

technical field [0001] The invention belongs to the technical field of architectural coatings, in particular to a light-resistant water-based environmental protection real stone paint and a preparation method thereof. Background technique [0002] In addition to general wall coatings, architectural coatings also include some special appearance and texture exterior wall coatings, such as real stone paint. [0003] Real stone paint is a kind of paint with a decorative effect similar to marble and granite. It is mainly made of natural stone powder of various colors, and it is applied to the imitation stone effect of building exterior walls, so it is also called liquid stone. [0004] Real stone paint has strong decorative properties, wide applicability, good durability, and is not easy to fade. Therefore, it has become a popular exterior wall decorative paint. However, real paint that is exposed to sunlight for a long time on the sunny side will still fade and change color. I...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D125/14C09D5/08C09D7/62C09D7/63C09D7/65
Inventor 唐寒伟张立伟李玉良于洋刘也
Owner 哈尔滨绿科科技有限公司