Glue for sticky mat film and preparation method of glue

A film and glue technology, applied in the direction of adhesives, adhesive types, ester copolymer adhesives, etc., can solve the problems of poor performance, low viscosity and slow drying speed of sticky dust pads, and achieve fast drying speed and transparency. Good, not easy to degumming effect

Inactive Publication Date: 2019-07-12
广东京华新材料科技股份有限公司
1 Cites 3 Cited by

AI-Extracted Technical Summary

Problems solved by technology

[0003] The sticky mat film used for the production and processing of the sticky mat is made by coating glue (adhesive) on the PE film, but the current drying speed of the glue for th...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Abstract

The invention discloses glue for a sticky mat film. The glue is prepared from raw materials as follows: a component A: soft water, baking soda, an initiator, an emulsifier, iso-octyl acrylate, butyl acrylate, methyl methacrylate, hydroxyethyl acrylate, acrylic acid, starch, caustic soda flakes, dichloromethane and 1-hydroxycyclohexyl phenyl ketone; a component B: soft water, ammonium persulfate and oxidized water; a component C: soft water and tert-butyl hydroperoxide; a component D: soft water and rongalite; a component E: a defoaming agent; a component F: ammonium hydroxide with concentration being 20%. The glue can be applied to the sticky mat film and has high drying speed and lower drying temperature, and the produced film is good in transparency and not prone to tackifying or glue failure.

Application Domain

Technology Topic

Examples

  • Experimental program(3)

Example Embodiment

[0033] Example 1
[0034] A glue for sticky mat film, by weight, includes the following raw materials:
[0035] Part A: 230 parts of soft water, 1 part of baking soda, 4 parts of initiator, 20 parts of emulsifier, 280 parts of isooctyl acrylate, 400 parts of butyl acrylate, 50 parts of methyl methacrylate, 13 parts of hydroxyethyl acrylate , 20 parts of acrylic acid, 0.5 parts of starch, 0.1 parts of flake base, 5 parts of dichloromethane, 1 part of 1-hydroxycyclohexyl phenyl ketone;
[0036] B component: 800 parts of soft water, 0.1 part of ammonium persulfate, 0.1 part of oxidized water (oxidation for 1h in summer, 2h in winter);
[0037] Component C: 25 parts of soft water, 1 part of tert-butyl hydroperoxide;
[0038] D component: 25 parts of soft water, 1 part of white powder;
[0039] E component: 0.1 part of defoamer; F component: 12 parts of 20% ammonia water.
[0040] Wherein, the initiator is ammonium persulfate. The emulsifier adopts 6:5 mixing of ethoxylated alkylphenol ammonium sulfate and sodium dodecylbenzene sulfonate. The defoamer adopts polyoxyethylene polyoxypropanolamine ether.
[0041] The preparation method of the glue for sticky mat film includes the following steps:
[0042] 1) Preparation of pre-emulsion: add the raw materials in component A to the emulsification tank, emulsify and stir for 0.5h;
[0043] 2) Preparation of the bottom material: Add the raw materials in the B component to the reaction kettle at room temperature and stir evenly;
[0044] 3) Emulsification reaction: the bottom material in step 2) is heated to 50°C, and then the pre-emulsion obtained in step 1) is added dropwise to the reactor within 2-4 hours, and the temperature in the reactor is controlled to 82°C;
[0045] 4) Heat preservation: control the temperature in the reactor to rise to 90℃ and keep it for 3 hours;
[0046] 5) Cooling and supplementing additives: Cool down to 65°C, add component C dropwise within 20 minutes, add component D dropwise within 20 minutes after the drop, and keep it at 60°C for 30 minutes after dropping;
[0047] 6) Cool down to 50°C and add component E, then cool down to 48°C and add component F to adjust PH=6.8, and cool to 45°C to discharge.

Example Embodiment

[0048] Example 2
[0049] A glue for sticky mat film, by weight, includes the following raw materials:
[0050] Component A: 240 parts of soft water, 2 parts of baking soda, 4.5 parts of initiator, 22 parts of emulsifier, 300 parts of isooctyl acrylate, 430 parts of butyl acrylate, 60 parts of methyl methacrylate, 15 parts of hydroxyethyl acrylate , 24 parts of acrylic acid, 1 part of starch, 0.3 parts of flake base, 8 parts of dichloromethane, 3 parts of 1-hydroxycyclohexyl phenyl ketone;
[0051] Component B: 860 parts of soft water, 0.3 parts of ammonium persulfate, 0.25 parts of oxidized water (oxidation for 1h in summer, 2h in winter);
[0052] Component C: 30 parts of soft water, 1.6 parts of tert-butyl hydroperoxide;
[0053] D component: 30 parts of soft water, 1.5 parts of white powder;
[0054] E component: 0.2 parts of defoamer; F component: 16 parts of 20% ammonia water.
[0055] Wherein, the initiator is ammonium persulfate. The emulsifier adopts 6:5 mixing of ethoxylated alkylphenol ammonium sulfate and sodium dodecylbenzene sulfonate. The defoamer adopts polyoxypropylene glycerol ether.
[0056] The preparation method of the glue for sticky mat film includes the following steps:
[0057] 1) Preparation of pre-emulsified liquid: add each raw material in component A to the emulsification tank, emulsify and stir for 1 hour;
[0058] 2) Preparation of the bottom material: Add the raw materials in the B component to the reaction kettle at room temperature and stir evenly;
[0059] 3) Emulsification reaction: the bottom material in step 2) is heated to 50°C, and then the pre-emulsion obtained in step 1) is added dropwise to the reactor within 2-4 hours, and the temperature in the reactor is controlled to 83°C;
[0060] 4) Heat preservation: control the temperature in the reactor to rise to 90℃ and keep it for 3 hours;
[0061] 5) Cooling and supplementing additives: Cool down to 65°C, add component C dropwise within 20 minutes, add component D dropwise within 20 minutes after the drop, and keep it at 60°C for 30 minutes after dropping;
[0062] 6) Cool down to 50°C and add component E, then cool down to 48°C and add component F to adjust PH=6.8, and cool to 45°C to discharge.

Example Embodiment

[0063] Example 3
[0064] A glue for sticky mat film, by weight, includes the following raw materials:
[0065] Component A: 250 parts of soft water, 3 parts of baking soda, 5 parts of initiator, 30 parts of emulsifier, 320 parts of isooctyl acrylate, 450 parts of butyl acrylate, 70 parts of methyl methacrylate, 18 parts of hydroxyethyl acrylate , 25 parts of acrylic acid, 1.5 parts of starch, 0.5 parts of flake base, 10 parts of dichloromethane, 5 parts of 1-hydroxycyclohexyl phenyl ketone;
[0066] Component B: 900 parts of soft water, 0.5 parts of ammonium persulfate, 0.5 parts of oxidized water (oxidation for 1h in summer and 2h in winter);
[0067] Component C: 35 parts of soft water, 2 parts of tert-butyl hydroperoxide;
[0068] D component: 35 parts of soft water, 2 parts of white powder; E component: 0.3 parts of defoamer;
[0069] F component: 18 parts of 20% ammonia water.
[0070] Wherein, the initiator is ammonium persulfate. The emulsifier adopts 6:5 mixing of ethoxylated alkylphenol ammonium sulfate and sodium dodecylbenzene sulfonate. The defoamer adopts polyoxyethylene polyoxypropylene pentaerythritol ether.
[0071] The preparation method of the glue for sticky mat film includes the following steps:
[0072] 1) Preparation of pre-emulsion: add the raw materials in component A to the emulsification tank, emulsify and stir for 1.5 hours;
[0073] 2) Preparation of the bottom material: Add the raw materials in the B component to the reaction kettle at room temperature and stir evenly;
[0074] 3) Emulsification reaction: the bottom material in step 2) is heated to 50°C, and then the pre-emulsion obtained in step 1) is added dropwise to the reactor within 2-4 hours, and the temperature in the reactor is controlled to 85°C;
[0075] 4) Heat preservation: control the temperature in the reactor to rise to 90℃ and keep it for 3 hours;
[0076] 5) Cooling and supplementing additives: Cool down to 65°C, add component C dropwise within 20 minutes, add component D dropwise within 20 minutes after the drop, and keep it at 60°C for 30 minutes after dropping;
[0077] 6) Cool down to 50°C and add component E, then cool down to 48°C and add component F to adjust PH=6.8, and cool to 45°C to discharge.
[0078] The glue of the present invention has a solid content of 43%, can be used for sticky mat film, has a fast drying speed, a relatively low temperature required for drying, a finished film has good transparency, does not increase viscosity, and is not easy to degummed.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Similar technology patents

Rosewood treatment method

Owner:SHANDONG QIAODUO TIANGONG FURNITURE

Low-gram-weight digital ink jet transfer printing base paper and production method thereof

ActiveCN110130142AProper adsorptionFast dryingWater-repelling agents additionPaper coatingGramCrosslinked chitosan
Owner:ZHEJIANG UNIVERSITY OF SCIENCE AND TECHNOLOGY

Classification and recommendation of technical efficacy words

  • Good transparency
  • Fast drying

System and method for management of health care services

InactiveUS7493266B2Good transparencyMore flexibility and portabilityOffice automationElectric digital data processingHealth programPrimary component
Owner:CANOPY ACQUISITION

Pasty calcium-zinc composite heat stabilizer and preparation method thereof

InactiveCN102093648AImprove the thermal stability of PVCGood transparencyAntioxidantRefractive index
Owner:ZHEJIANG HIMPTON NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products