Preparation method and application of improved wood-plastic composite material

A wood-plastic composite material and wood-plastic composite technology are applied in the field of preparation of improved wood-plastic composite materials, which can solve the problems of reduced toughness, low strength, and voids in products, and achieve high bending and flexural strength. The effect of many times of recycling and not easy to fade

Active Publication Date: 2022-04-19
GUANGDONG HUANGTIAN ENVIRONMENTAL PROTECTION TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned wood-plastic composite material has many components, and the preparation process is relatively cumbersome; at the same time, after the mixed above-mentioned wood-plastic composite material is extruded into a product through an extruder, due to the presence of calcium carbonate powder, PVC plastic will appear. A series of problems such as reduced adhesion and fusion, reduced toughness of the product, incompatibility of wood powder and light calcium carbonate powder, and gaps in the product will lead to defects such as easy oxidative fading, low strength, and easy breakage of the finished product. Meet user needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of improved wood-plastic composite material
  • Preparation method and application of improved wood-plastic composite material
  • Preparation method and application of improved wood-plastic composite material

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] The present invention also provides a method for preparing an improved wood-plastic composite material, including the above-mentioned wood-plastic composite material, and the preparation method of the above-mentioned wood-plastic composite material includes the following steps:

[0057] S1. Melting of high-density polyethylene: Add high-density polyethylene into a high-speed mixer and heat-melt it into a flowable liquid to obtain a molten plastic liquid for later use.

[0058] In this step, the high-speed mixer of this embodiment adopts the high-speed mixer commonly used in the plastic industry on the market, which is suitable for mixing and stirring materials such as powder / granule / auxiliary / color powder / color masterbatch / plastic . The barrel body adopts an arc-shaped structure, and the special blade structure is mainly used to make the material form a vortex-like high-speed stirring and can be modified by heating. The heating temperature of the high speed mixer of th...

Embodiment 1

[0089] An improved wood-plastic composite material, including the following components in weight percentage:

[0090] High-density polyethylene 60%;

[0091] Nylon plastic powder 10%;

[0092] Bamboo fiber powder 25%;

[0093] Coloring agent 5%.

[0094] The preparation method of the wood-plastic composite material in embodiment 1 specifically comprises the following steps:

[0095] The following components are calculated in parts by weight.

[0096] S1. Melting of high-density polyethylene: add 60% of high-density polyethylene into a high-speed mixer and heat-melt it into a flowable liquid to obtain a molten plastic liquid, which is set aside. The heating temperature of the high-speed mixer of this embodiment is controlled at about 150°C.

[0097] S2. Dyeing: add 5% dyeing agent into the high-speed mixer to dye the molten plastic liquid.

[0098] S3. Mixing: add 25% wood fiber powder into the high-speed mixer, mix and stir evenly, then add 10% nylon plastic powder into th...

Embodiment 2

[0102] An improved wood-plastic composite material, including the following components in weight percentage:

[0103] High-density polyethylene 63%;

[0104] Nylon plastic powder 12%;

[0105] Bamboo fiber powder 20%;

[0106] Coloring agent 5%.

[0107] The preparation method of the wood-plastic composite material in embodiment 2 specifically comprises the following steps:

[0108] The following components are calculated in parts by weight.

[0109] S1. Melting of high-density polyethylene: add 63% high-density polyethylene into a high-speed mixer and heat-melt it into a flowable liquid to obtain molten plastic liquid, which is set aside. The heating temperature of the high-speed mixer of this embodiment is controlled at about 157°C.

[0110] S2. Dyeing: add 5% dyeing agent into the high-speed mixer to dye the molten plastic liquid.

[0111] S3. Mixing: add 20% wood fiber powder into the high-speed mixer, mix and stir evenly, then add 12% nylon plastic powder into the h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing an improved wood-plastic composite material, which includes the steps of melting, dyeing, mixing, and molding high-density polyethylene. The wood-plastic composite material includes the following components in weight percentage: high-density polyethylene 50-70%; nylon plastic powder 10-20%; wood fiber powder 20-30%. The wood-plastic composite material is obtained by uniformly mixing the above-mentioned components. The improved wood-plastic composite material of the present invention uses high-density polyethylene as the main raw material, and then mixes nylon plastic and wood fiber powder, and adds wood fiber powder so that it is completely covered by high-density polyethylene melt, so that the wood fiber powder The hygroscopicity is greatly reduced, and the dispersibility, oxidation resistance and flame retardancy are greatly improved, thereby improving the strength of the wood-plastic composite material; and the addition of nylon plastic further improves its strength, and the products manufactured by the wood-plastic composite material Oxidation resistance, bending resistance, bending resistance and other properties are excellent, which can meet the needs of use.

Description

technical field [0001] The invention relates to the field of materials, in particular to a preparation method and application of an improved wood-plastic composite material. Background technique [0002] Wood-plastic composites (Wood-Plastic Composites, WPC) is a new type of composite material that has been booming at home and abroad in recent years. It refers to the use of polyethylene, polypropylene and polyvinyl chloride, etc. Wood flour, rice husk, straw and other waste plant fibers are mixed into new wood materials, and then processed by extrusion, molding, injection molding and other plastic processing techniques to produce boards or profiles. Mainly used in building materials, furniture, logistics packaging and other industries. [0003] As shown in the Chinese Invention Patent No. 201310417130.0, it discloses a PVC foamed wood-plastic composite material and its manufacturing method. The wood-plastic composite material is made of the following raw materials in parts ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/06C08L77/00C08L97/02C08K7/06
CPCC08L23/06C08L2201/08C08L2207/062C08L2205/16C08L77/00C08L97/02C08K7/06
Inventor 孔德玲
Owner GUANGDONG HUANGTIAN ENVIRONMENTAL PROTECTION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com