Preparation method of wet-process zinc oxide pre-dispersion master batch

A wet-process zinc oxide and pre-dispersion technology, applied in the field of rubber additives, can solve the problems of unsatisfactory zinc oxide dispersion effect, high energy consumption, and more dust, and achieve the effects of good dispersibility, high activity and low actual dosage.

Inactive Publication Date: 2019-07-19
青岛泰联新材料有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantages of this manufacturing method are obvious, one is high energy consumption, the other is more dust, and the third is that the dispersion effect of zinc oxide is not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of wet-process zinc oxide pre-dispersion master batch
  • Preparation method of wet-process zinc oxide pre-dispersion master batch
  • Preparation method of wet-process zinc oxide pre-dispersion master batch

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0048] A kind of wet process zinc oxide predispersed masterbatch of example 1

[0049] Its preparation raw materials include by weight:

[0050] 50 parts of zinc oxide, 5 parts of modifier, 9 parts of organic processing aid, 15 parts of inorganic carrier, 21 parts of rubber latex, 0.5 part of stabilizer, 300 parts of the first part of water, 35 parts of the second part of water;

[0051] Zinc oxide is nano zinc oxide, nano zinc oxide: the purity is 90%; the particle size is 30nm ~ 50nm; the specific surface area is 20m 2 / g; lead content is 8ppm; manganese content is 30ppm; copper content is 1ppm; cadmium content is ppm; mercury content is 0ppm and arsenic content is 0ppm.

[0052] Described modifying agent is stearic acid, and described organic processing aid is paraffin oil, and described inorganic carrier is white carbon black, and described rubber latex is the natural concentrated latex that solid content is 60%, and described stabilizer is laurel ammonium acid soap; the...

Embodiment 2

[0066] Embodiment 2 A kind of preparation method of wet-process zinc oxide predispersed masterbatch, preparation method

[0067] Its preparation raw materials include by weight:

[0068] 30 parts of zinc oxide, 7 parts of modifier, 1 part of organic processing aid, 35 parts of inorganic carrier, 27 parts of rubber latex, 0.5 part of stabilizer, 300 parts of the first part of water, 60 parts of the second part of water;

[0069] Zinc oxide is nano zinc oxide, nano zinc oxide: the purity is 90%; the particle size is 30nm ~ 50nm; the specific surface area is 20m 2 / g; lead content is 8ppm; manganese content is 30ppm; copper content is 1ppm; cadmium content is ppm; mercury content is 0ppm and arsenic content is 0ppm.

[0070] The modifying agent is acrylic acid, the inorganic carrier is kaolin, the organic processing aid is protective wax, the rubber latex is natural concentrated latex with a solid content of 60%, and the stabilizer is ammonium laurate soap; The first part of wa...

Embodiment 3

[0079] Embodiment 3 A kind of preparation method of wet-process zinc oxide predispersed masterbatch,

[0080] Its preparation raw materials include by weight:

[0081] 70 parts of zinc oxide, 10 parts of modifier, 5 parts of organic processing aid, 0 part of inorganic carrier, 15 parts of rubber emulsion, 0.5 part of stabilizer, 300 parts of the first part of water, 30 parts of the second part of water;

[0082] Zinc oxide is nano zinc oxide, nano zinc oxide: the purity is 90%; the particle size is 30nm ~ 50nm; the specific surface area is 20m 2 / g; lead content is 8ppm; manganese content is 30ppm; copper content is 1ppm; cadmium content is ppm; mercury content is 0ppm and arsenic content is 0ppm.

[0083] The modifying agent is methacrylic acid, the organic processing aid is calcium silicate, the inorganic processing aid is petroleum resin, the rubber latex is natural concentrated latex with a solid content of 60%, and the stabilizer It is ammonium laurate soap; the first p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
mechanical stabilityaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a wet-process zinc oxide pre-dispersion master batch, which comprises the following steps: dispersing zinc oxide, an inorganic carrier, a modifier and aprocessing aid in a first part of water to obtain mixed slurry A; uniformly stirring a rubber emulsion, a stabilizer and a second part of water to obtain a rubber liquid B; mixing and flocculating the mixed slurry A and the rubber liquid B to obtain a zinc oxide and rubber compound; and drying and granulating the zinc oxide and rubber compound to obtain the zinc oxide pre-dispersed master batch.Zinc oxide in the prepared zinc oxide pre-dispersion master batch is better in dispersity, smaller in particle size and higher in activity. In the formula, the zinc oxide pre-dispersed master batch isequivalent or reduced by 40% to replace indirect zinc oxide or ZnO-80, the Mooney viscosity, the scorch time and the vulcanization rate of the unvulcanized rubber are basically kept consistent; physical and mechanical properties of vulcanized rubber are basically kept consistent before and after aging.

Description

technical field [0001] The invention relates to the field of rubber additives, in particular to a preparation method of wet-process zinc oxide pre-dispersed master batches. Background technique [0002] Pre-dispersed rubber additive masterbatch is a widely used rubber additive product. The pre-dispersed rubber additive masterbatch successfully turns the powder into a solid product coated with polymers. The pre-dispersed rubber additive masterbatch is mainly a pretreatment for rubber additives that are difficult to disperse well in the rubber body. The product obtained by the method is applied in rubber products, which can not only improve the dispersion uniformity of rubber additives and thus improve the quality of rubber products, but also effectively reduce energy consumption and improve environmental dust pollution. The method of masterbatching pre-dispersed rubber additives is divided into dry granulation and wet granulation. At present, the processing methods of powde...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/02C08K13/02C08K3/22C08J3/22C08L7/00C08L23/16C08L9/02
CPCC08J3/226C08J2307/00C08J2309/02C08J2323/16C08J2407/02C08K13/02C08K2003/2296C08K2201/003C08K2201/006
Inventor 张明栋赵旭魁
Owner 青岛泰联新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap