A kind of high anti-cracking high performance PVC cable sheathing material and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A cable sheathing material, high-performance technology, applied in circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problems of low temperature resistance without quantitative indicators, unable to judge the applicable temperature, etc., to achieve good cross-linking effect, The effect of long overall service life and improved stress fracture resistance
Active Publication Date: 2021-03-26
WUXI HUAMEI CABLE
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Although this invention has low temperature resistance performance, its specific low temperature resistance performance has no quantitative index, and it is impossible to determine its applicable temperature.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0039] A kind of high anti-cracking high-performance PVC cable sheathing material of the present invention, by weight, it comprises:
[0086] The preparation method of described anti-cracking composite agent, it comprises the following steps,
[0087] (1) Add poly-1-butene, low-density polyethylene, and modifier in...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention relates to a PVC cable sheath material with high performance and high cracking resistance, which comprises the following raw materials in parts by weight: 120-200 parts of PVC resin, 35-55 parts of an anti-cracking composite agent, 40-66 parts of a plasticizer, 15-20 parts of an antioxidant, 10-14 parts of a heat stabilizer, 5-12 parts of filler, 3-8 parts of a flame retardant, 2-5 parts of whiskers, and 1-3 parts of ultraviolet-proof powder. A preparation method comprises the steps of mixing and pelletizing the PVC resin, anti-cracking composite agent and whiskers in a twin-screw extruder, adding the mixture into an internal mixer, then adding the plasticizer, antioxidant, heat stabilizer, filler and fire retardant, mixing, discharging, cooling, adding the mixture into the internal mixer again, adding the ultraviolet-proof powder, mixing, cooling, and feeding into an open mill for mixing, thereby obtaining the PVC cable sheath material. The sheath material has good electrical insulation performance, mechanical and physical performance, excellent resistance to environmental stress cracking, impact and tear, and long service life.
Description
technical field [0001] The invention relates to a cable sheath and a preparation method thereof, in particular to a highly crack-resistant cable sheath and a preparation method thereof. Background technique [0002] With the rapid development of the economy, cables are widely used in the fields of communication and electric power. When the cables are used in high-temperature or low-temperature environments, the cable material on the surface of the existing cables will crack, which will lead to cable power transmission or transmission in severe cases. The interruption of the signal will seriously affect people's normal life. [0003] The Chinese patent application whose publication number is CN108410045A discloses a high-temperature-resistant flame-retardant and non-toxic cable material. The cable material includes the following components: polyolefinthermoplasticelastomer, polyurethaneelastomer rubber, EPDM rubber, ceramicpowder, trioctyl trimellitate, zincstearate, re...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More