Aqueous low-temperature hot-painting coating and preparation method thereof

A low-temperature heat and water-based technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve problems such as scrapped rework, earthworm-like arching of cold-laminated film layers, and affecting product use, and achieves good yellowing resistance. The film is easy to operate and has good sticking firmness

Active Publication Date: 2019-08-23
HUIZHOU YIDU IMAGE TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the oil-based pressure-sensitive adhesive layer used in cold lamination film contains rosin-type tackifying resin, and the tackifying resin used outdoors for a long time will age and cause the picture to turn yellow. When printing pictures with water-based ink, especially where the ink is heavy, it is easy to have the problem of not sticking firmly and wrinkling
At the same time, the lamination effect of the cold lamination film is highly dependent on the operating experience of the equipment and personnel. In the case of unbalanced pressure adjustment at both ends of the composite rubber roller and uncoordinated film tension by the personnel operation, cold lamination film will appear in the lamination. Wrinkled and deformed with the material, after 24 hours of storage, there will be earthworm-like arching of the cold lamination film layer, which will affect the use of the product and cause it to be scrapped and reworked
In addition, the thermoplastic layer of the card film PET material of the coil mainly uses the extrusion coating technology, and the thermoplastic rubber particles are melted and then poured on the PET. The melting temperature is as high as 300-400°C. The minimum heat-mounting temperature for the finished product is 140°C. , can only adapt to the lamination of color inkjet paper inkjet materials, and is not adaptable to the advertising inkjet materials widely used in the market with PP paper and PVC as the main material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous low-temperature hot-painting coating and preparation method thereof
  • Aqueous low-temperature hot-painting coating and preparation method thereof
  • Aqueous low-temperature hot-painting coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0061] In order to better explain the present invention, it will be further described in conjunction with the following specific examples, but the present invention is not limited to the specific examples.

[0062] Table 1: The formula of embodiment 1-4 and every square wet glue amount (g / m 2 ).

[0063]

[0064]

[0065] The amount of wet glue per square meter refers to the amount of raw materials contained in the glue coated on the substrate per square meter.

[0066] The spherical silicone light diffusing agent is provided by Shanghai Jinghong Chemical Technology Co., Ltd., the model is JIAYID750. Polyurethane-acrylate copolymer emulsion was provided by Clariant Chemical (China) Co., Ltd., model ADC616. Ethylene-vinyl acetate copolymer was provided by Guangxi Guangwei Chemical Co., Ltd., model GW-707. The anti-scratch wax is provided by Beijing Tianhengjian Technology Development Co., Ltd., the model is THK-F4. 1,2-bis(5-methyl-2-benzoxazolyl)-ethylene is provided ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an aqueous low-temperature hot-painting coating and a preparation method thereof. The aqueous low-temperature hot-painting coating comprises the following components: in partsby weight, 10-50 parts of water, 1-10 parts of an organic alcohol solvent, 0.05-5 parts of an organosilicon light diffusing agent, 10-40 parts of a polyurethane-acrylate copolymer emulsion, 10-50 parts of an ethylene-vinyl acetate copolymer, 0.1-5 parts of a film-forming aid, 1-10 parts of an anti-sticking agent, 0-5 parts of a whitening agent, 0-5 parts of a defoamer and 0-5 parts of a wetting agent. The coating is painted on the surface of a substrate through a direct painting method, and drying and winding are conducted so as to complete painting; the product is suitable for a low-temperature hot-painting machine, can be adhered tightly to images formed through printing of water-based and oil-based ink, and has no wrinkles in the late stage, and the obtained coating has good yellowing resistance; the coating can be applied to PET, CPP, OPP and other different media, the coating has no adhesion at normal temperature, no release paper is needed for winding of a coated product, and a silicone oil layer is eliminated on the surface; and the coating has a good hot melt effect, and is especially suitable for low-temperature hot painting of heat-labile materials.

Description

technical field [0001] The invention belongs to the technical field of printing and decoration, and in particular relates to a water-based low-temperature thermal mounting paint and a preparation method thereof. Background technique [0002] In the printing and decoration industry, polypropylene (PP) advertising paper, photo paper, body stickers and other products are often spray-painted. After spray-painting, a layer of cold lamination film is usually attached to the surface to play the role of waterproof, scratch-resistant, and prolonging the use time. . The more common cold lamination films on the market mainly use back-adhesive composite technology to coat oil-based or water-based pressure-sensitive adhesive layers on paper or PET (polyethylene terephthalate) surfaces containing silicone oil, and dry the glue with The main material is laminated, and the main material components are mainly PVC (polyvinyl chloride), CPP, OPP (biaxially oriented polypropylene film). The o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D123/08C09D175/14C09D7/63C09D7/65
CPCC09D123/0853C09D175/14C09D7/63C09D7/65C09D7/70C08L75/14C08L91/06C08K7/16C08L23/0853
Inventor 罗晓琪
Owner HUIZHOU YIDU IMAGE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products