UV curing ink for aluminum plate and preparation method of UV curing ink

A technology of ink and aluminum plate, which is applied in the field of UV curing ink and its preparation on aluminum plate, can solve the problems of poor water and weather resistance, hot stickiness and cold brittleness, etc., and achieve excellent adhesion, fast curing rate, weather resistance and wear resistance damage performance superior effect

Inactive Publication Date: 2020-01-07
安徽映山红材料科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] If the UV ink only uses polyacrylate as the ink binder, there are many shortcomings, such as hot stickiness, cold brittleness, poor water and weather resistance, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Specific steps are as follows:

[0022] (1) Add 20 parts of epoxy acrylate, 4 parts of butyl acrylate, 2 parts of methyl methacrylate and 2 parts of acrylic acid into the mixing tank, and stir for 15 minutes at a stirring speed of 700 rpm;

[0023] (2) Transfer the pre-mixed ink to the grinder and grind 2 times;

[0024] (3) Transfer the ground liquid to a mixing tank, add 1 part of ethyl 2,4,6-trimethylbenzoylphenyl phosphonate, 2 parts of permanent red pigment and 3 parts of additives to the mixing tank in sequence In the bucket, stir at a stirring speed of 700rpm for 25 minutes to obtain UV ink.

Embodiment 2

[0026] Specific steps are as follows:

[0027] (1) Add 20 parts of epoxy acrylate, 6 parts of butyl acrylate, 2 parts of methyl methacrylate, and 1 part of acrylic acid into the mixing tank, and stir for 10 minutes at a stirring speed of 1000 rpm;

[0028] (2) Transfer the pre-mixed ink to the grinder and grind 2 times;

[0029] (3) Transfer the ground liquid to a mixing tank, add 1 part of 2-methyl-2-(4-morpholinyl)-1-[4-(methylthio)phenyl]-1-propanone, Add 2 parts of phthalocyanine green pigment and 3 parts of additives into the mixing tank in turn, and stir for 20 minutes at a stirring speed of 1000 rpm to make the mixture evenly mixed;

[0030] (3) Pour the uniformly mixed ink into a grinder and grind twice to obtain UV ink.

Embodiment 3

[0032] Specific steps are as follows

[0033] (1) Add 20 parts of epoxy acrylate, 6 parts of butyl acrylate, 1 part of methyl methacrylate and 2 parts of acrylic acid into the mixing tank, and stir for 10 minutes at a stirring speed of 900 rpm;

[0034] (2) Transfer the pre-mixed ink to the grinder and grind 2 times;

[0035] (3) Transfer the ground liquid to the mixing tank, add 1 part of 2-hydroxyl-2-methyl-1-phenylacetone, 2 parts of phthalocyanine green pigment and 3 parts of additives into the mixing tank in sequence, Stir at a stirring speed of 900 rpm for 20 minutes to obtain UV ink.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses UV curing ink for an aluminum plate and a preparation method of the UV curing ink, belonging to the technical field of UV curing ink. The UV curing ink comprises, in parts by weight, 55 to 70 parts of unsaturated resin, 20 to 30 parts of acrylate monomers, 1 to 10 parts of a photoinitiator, 5 to 10 parts of a pigment and 1 to 5 parts of an auxiliary agent. According to theinvention, the UV curing ink with excellent comprehensive performance is obtained by adjusting the types and proportions of the soft and hard acrylate monomers. The ink is environment-friendly and non-toxic and has a high curing rate; epoxy groups in epoxy resin have excellent adhesive force to aluminum products; the ink is excellent in water resistance, solvent resistance, heat resistance, weather resistance and wear resistance after being cured; and the UV curing ink prepared in the invention can be attached to the surface of a metal product, and is especially suitable for roller coating tothe surface of a steel product.

Description

technical field [0001] The invention belongs to the technical field of UV curable inks, in particular to a UV curable ink for aluminum plates and a preparation method thereof. Background technique [0002] UV ink is composed of photosensitive resin, reactive diluent monomer, pigment, initiator and various additives. The solid content of UV ink is 100%, and no organic solvent is used as a solvent. When curing, ultraviolet light with specific wavelength and energy is used to make the ink chain-extended, cross-linked and dried and cured within a few seconds, producing very little volatile organic compounds, which is environmentally friendly. A type of ink. UV ink only uses ultraviolet light to cure the ink, which greatly saves energy. [0003] If the UV ink only uses polyacrylate as the ink binder, there are many shortcomings, such as hot stickiness, cold brittleness, poor water and weather resistance, etc. The epoxy group in epoxy acrylate has excellent adhesion to the meta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/101
CPCC09D11/101
Inventor 潘轸孙文李康朱满洲
Owner 安徽映山红材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap