A functionalized polymer-coated ionic liquid lubricating oil additive and its preparation method and application

A lubricating oil additive and ionic liquid technology, applied in the direction of additives, lubricating compositions, petroleum industry, etc., can solve problems such as unsatisfactory use requirements and single function, and achieve improved anti-wear and extreme pressure performance and stable chemical properties Effect

Active Publication Date: 2022-08-09
圣保路石油化工(天津)股份有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing lubricating oil additives have relatively single functions and cannot meet the requirements for use in extremely harsh environments

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A functionalized polymer-coated ionic liquid lubricating oil additive, the lubricating oil additive is composed of an ionic liquid, a high-molecular polymer layer coated on the surface of the ionic liquid, and a surface modification of the high-molecular polymer layer The silane coupling agent with a carbon-carbon double bond at the end is composed of a modified calcium sulfonate layer grafted on the surface of the high molecular polymer layer in a cross-linked manner.

[0029] The ionic liquid is a benzothiazole ionic liquid.

[0030] The high molecular polymer layer is polyimide.

[0031] The silane coupling agent with carbon-carbon double bond at the end is 2-hydroxy-3-[3-(trimethoxysilyl)propoxy]propyl acrylate.

[0032] The modified calcium sulfonate is 2-(4-methyl-1-piperazinyl)-4-(methylsulfonyl) benzaldehyde and 2-acrylamido-2-methylpropane-1-sulfonic acid The reaction product of calcium acid.

[0033] Correspondingly, as above-mentioned preparation method of...

Embodiment 2

[0041] A functionalized polymer-coated ionic liquid lubricating oil additive, the lubricating oil additive is composed of an ionic liquid, a high molecular polymer layer coated on the surface of the ionic liquid, and a surface modification of the high molecular polymer layer. The silane coupling agent with a carbon-carbon double bond at the end is composed of a modified calcium sulfonate layer grafted on the surface of the high molecular polymer layer in a cross-linked manner.

[0042] The ionic liquid is a benzotriazole ionic liquid.

[0043] The high molecular polymer layer is polyimide.

[0044] The silane coupling agent with carbon-carbon double bond at the end is 2-hydroxy-3-[3-(trimethoxysilyl)propoxy]propyl acrylate.

[0045] The modified calcium sulfonate is 2-(4-methyl-1-piperazinyl)-4-(methylsulfonyl) benzaldehyde and 2-acrylamido-2-methylpropane-1-sulfonic acid The reaction product of calcium acid.

[0046] Correspondingly, as the above-mentioned preparation meth...

Embodiment 3

[0053] The functionalized polymer-coated ionic liquid lubricating oil additive in this example, its composition and preparation method are basically similar to those in Example 1, and the main difference is that S1: under the condition of high-speed mechanical stirring, through emulsion polymerization The high molecular polymer is coated on the surface of the ionic liquid to obtain the high molecular polymer coated ionic liquid product A; more specifically, the ionic liquid is dispersed in N-methylpyrrolidone under the condition of high-speed mechanical stirring at 8000 rpm, and added Polyimide, wherein the mass ratio of polyimide, N-methylpyrrolidone, and ionic liquid is 1:27:12.6, in an oil bath at 100 °C, stirring and dissolving for 60 minutes, and then stirring at 30 °C and 1000 rpm 45min, and finally extruded through a 600um pore size channel to obtain a spheroidized polymer-coated ionic liquid product A;

[0054] Correspondingly, the above-mentioned functionalized polyme...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a functional polymer covering liquid liquid lubricant additive, which is a polymer polymer layer on the surface of the ionic liquid on the surface of the ionic liquid, and through the polymer polymer on the polymer polymerThe surface modifier of the layer modifies the carbon -carbon dual -bond sirrius coupling agent is composed of the modified sulfonate layer of the surface of the polymer polymer layer by the cross -linked branches.The functional polymers of the present invention cover the ionic liquid liquid lubricating oil additive in the steel / steel friction vice, which significantly improves the decrease and abrasion resistance of lubricant additives in the friction sideline.Small friction and side loss and long service life.The present invention also disclosed the preparation method and application of functional polymer to cover the ionic liquid lubricant additive.

Description

technical field [0001] The invention relates to the technical field of lubricating oil additives, in particular to a functionalized polymer-coated ionic liquid lubricating oil additive and a preparation method and application thereof. Background technique [0002] The operation of equipment is inseparable from lubricating oil additives, and lubricating oil is inseparable from lubricating oil additives. Lubricating oil additives are the essence of modern advanced lubricating oils. According to statistics, about 30% of energy is consumed in friction, and 70% of damaged parts are scrapped by wear and tear. Therefore, improving lubricating properties to reduce friction, wear and prevent sintering is of great significance to the national economy. Commonly used additives in lubricating oil are divided into antioxidants, anti-wear agents, friction modifiers (also known as oily agents), extreme pressure additives, detergents, dispersants, foam inhibitors, anti-corrosion and anti-ru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C10M161/00C10N30/02C10N30/04C10N30/06C10N30/10C10N30/12
CPCC10M161/00C10M2219/104C10M2215/223C10M2217/044C10M2221/02Y02P20/54
Inventor 徐武警
Owner 圣保路石油化工(天津)股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com