Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Blended ceramic pigment glaze, production method thereof, stone-like glazed tile, and production method of the stone-like glazed tile

A technology of ceramic pigments and production methods, applied in the fields of blended ceramic pigment glaze and imitation stone glazed tiles, can solve the problems of far distance between stones, intensified loss of details, loss of details, etc.

Active Publication Date: 2020-01-21
GUANGDONG KITO CERAMICS GROUP CO LTD +2
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The defect of imitation stone glazed tiles produced by this method is that the original image scanned by the scanning machine has lost some original details compared with the scanned stone, and after post-processing in Photoshop, it is compared with the material stone itself , the loss of details is further exacerbated by
Although aided by advanced equipment and supplemented with new materials, the characteristics and textures of the stone itself can be restored as much as possible, but it is still far from the real stone.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Blended ceramic pigment glaze, production method thereof, stone-like glazed tile, and production method of the stone-like glazed tile
  • Blended ceramic pigment glaze, production method thereof, stone-like glazed tile, and production method of the stone-like glazed tile
  • Blended ceramic pigment glaze, production method thereof, stone-like glazed tile, and production method of the stone-like glazed tile

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0081] The present embodiment provides a kind of imitation stone material glazed tile, and it is produced through the following steps:

[0082] S1: Raw materials are used to prepare slurry through batching and ball milling, and after iron removal, sieving, aging, spray tower milling, and then sieving to obtain a blank; wherein, the blank formula is the green body formula of ordinary glazed ceramics;

[0083] S2: Press and shape the billet by a press to form a green body;

[0084] S3: Transporting the green body to a drying kiln for drying to obtain a dried green body;

[0085]S4: Adjust the flow rate of the colored glaze to 45-50s by adding sodium tripolyphosphate and debonding agent on the basis of the base glaze of the colored glaze, and then import it into the fluid colored glaze container; the amount of added sodium tripolyphosphate is according to 0.2 to 0.8 parts by weight, and the amount of the additional debonding agent is 5 to 30 parts by weight; meanwhile, the base ...

Embodiment 2

[0092] This embodiment provides a kind of imitation stone material glazed tile, the difference of its preparation method and the preparation method that embodiment 1 provides is:

[0093] In step S4, the flow rate of the color glaze is 48s, the amount of added sodium tripolyphosphate is 0.35 parts by weight, and the amount of added debonding agent is 15 parts by weight; meanwhile, The base glaze of the color glaze includes: potassium feldspar: 31 parts; albite feldspar: 20 parts; burnt talc: 10 parts; corundum: 4 parts; barium carbonate: 10 parts; kaolin: 6 parts; nepheline: 5 parts; calcite: 4 parts ; Dolomite: 7 parts; Zinc oxide: 3 parts; Sodium tripolyphosphate: 0.35 parts; Carboxymethylcellulose sodium C50A: 0.15 parts; Sodium humate: 0.2 parts;

[0094] In step S5, the top glaze includes Lidejia top glaze LM2042: 97 parts; zirconium silicate 14 parts; dolomite powder: 5 parts; zinc oxide: 3 parts; parts; sodium carboxymethylcellulose C50A: 0.15 parts, sodium humate: 0.2...

Embodiment 3

[0097] This embodiment provides a kind of imitation stone material glazed tile, the difference of its preparation method and the preparation method that embodiment 1 provides is:

[0098] In step S4, the flow rate of the color glaze is 48s, the amount of added sodium tripolyphosphate is 0.8 parts by weight, and the amount of added debonding agent is 30 parts by weight; meanwhile, The base glaze of colored glaze includes: potassium feldspar: 32 parts; albite feldspar: 30 parts; burnt talc: 10 parts; corundum: 4 parts; barium carbonate: 12 parts; kaolin: 8 parts; nepheline: 7 parts; calcite: 5 parts ; Dolomite: 20 parts; Zinc oxide: 4 parts; Sodium tripolyphosphate: 0.8 parts; Carboxymethylcellulose sodium C50A: 0.2 parts; Sodium humate: 0.3 parts;

[0099] In step S5, the surface glaze includes Lidejia surface glaze LM2042: 100 parts; zirconium silicate: 15 parts; dolomite powder: 5 parts; zinc oxide: 4 parts; ~0.8 parts; sodium carboxymethylcellulose C50A: 0.15 parts, sodium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses blended ceramic pigment glaze and a production method thereof as well as a stone-like glazed tile and a production method of the stone-like glazed tile, and relates to the technical field of ceramic production. According to the method, flowing colored glaze and surface glaze are mutually blended and combined to form blended ceramic pigment glaze; and then the blended ceramic pigment glaze is applied to the surface of the dried green body to prepare the stone-like glazed tile. According to the method, flowing colored glaze and surface glaze are blended with each other; the flowing irregularity of the colored glaze can be utilized; law-free characteristics, the characteristics of different flow rates between the colored glaze and the cover glaze, mutual permeation andfusion and the like are realized; the stone-like glazed tile has a more vivid, more harmonious and more natural stone grain effect, so that the ceramic glazed tile which is natural and smooth in grain, uniform in inside and outside and clear and fine in veins and has a real stone feeling is manufactured, and the decorative effect of the stone-like glazed tile product on buildings can be further improved.

Description

technical field [0001] The invention relates to the technical field of ceramic production, in particular to a blended ceramic pigment glaze and a production method thereof, and a stone imitation glazed tile and a production method thereof. Background technique [0002] Ceramic glazed tiles are a building decoration material that has become popular in recent years, especially stone-like glazed tiles. The imitation stone glazed tiles on the market are generally obtained by buying stones, scanning them, post-processing them through Photoshop, and then printing them on the brick embryos by multi-channel inkjet printing and firing them. The defect of imitation stone glazed tiles produced by this method is that the original image scanned by the scanning machine has lost some original details compared with the scanned stone, and after post-processing in Photoshop, it is compared with the material stone itself , the loss of detail is exacerbated. This will make the imitated stone ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B41/86C03C8/00
CPCC04B41/86C04B41/5022C03C8/00C04B41/4535
Inventor 李光伟李德英喻劲军钟礼丰戴永刚吉永发温景辉万里
Owner GUANGDONG KITO CERAMICS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com