A kind of anti-aging polystyrene plastic product

A polystyrene plastic, polystyrene technology, applied in the field of daily necessities, can solve the problems of shortened service life, failure to meet the requirements of actual use, aging and brittleness, etc.

Active Publication Date: 2022-03-01
浙江美仕达日用品有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Due to the lack of current polystyrene resin molding technology, the polystyrene plastic products produced by it are prone to aging and brittle problems under the dual effects of light and heat, and long-term exposure to direct sunlight will greatly shorten the Its service life cannot meet the requirements of actual use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-aging polystyrene plastic product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] The components of an anti-aging polystyrene plastic product include: 100Kg polystyrene, 10Kg ethyl methacrylate, 3Kg polyethylene terephthalate, 0.5Kg organic rare earth composite stabilizer, 2Kg stearyl benzene Formylmethane, 0.1Kg 4-acetylphenyl potassium sulfate, 4Kg silicon carbide fiber, 3Kg titanium dioxide, 1Kg calcium carbonate, 0.1Kg coupling agent, 4Kg toughening agent, 2Kg lubricant.

[0025] Described a kind of anti-aging polystyrene plastic product is processed according to the following method:

[0026] Add silicon carbide fiber, titanium dioxide, and calcium carbonate into the mixing kettle, mix evenly, then add organic rare earth composite stabilizer, coupling agent, toughening agent and lubricant, continue to stir and mix evenly; then add other materials, stir 10 minutes to mix well and evenly to obtain the mixture; then use a twin-screw extruder to extrude and granulate, and use an injection molding machine to form the particles at an injection molding...

Embodiment 2

[0035] The components of an anti-aging polystyrene plastic product include: 110Kg polystyrene, 13Kg ethyl methacrylate, 8Kg polyethylene terephthalate, 2Kg organic rare earth composite stabilizer, 5Kg stearoyl benzo Acyl methane, 0.4Kg 4-acetylphenyl potassium sulfate, 6Kg silicon carbide fiber, 7Kg titanium dioxide, 3Kg calcium carbonate, 0.3Kg coupling agent, 7Kg toughening agent, 5Kg lubricant.

[0036] Described a kind of anti-aging polystyrene plastic product is processed according to the following method:

[0037] Add silicon carbide fiber, titanium dioxide, and calcium carbonate into the mixing kettle, mix evenly, then add organic rare earth composite stabilizer, coupling agent, toughening agent and lubricant, continue to stir and mix evenly; then add other materials, stir Mix well for 15 minutes to obtain a mixture; then use a twin-screw extruder to extrude and granulate, and use an injection molding machine to process the resulting particles at an injection molding te...

Embodiment 3

[0046] The components of an anti-aging polystyrene plastic product include: 120Kg polystyrene, 15Kg ethyl methacrylate, 12Kg polyethylene terephthalate, 4Kg organic rare earth composite stabilizer, 7Kg stearoyl benzoate Acyl methane, 0.8Kg 4-acetylphenyl potassium sulfate, 8Kg silicon carbide fiber, 10Kg titanium dioxide, 5Kg calcium carbonate, 0.5Kg coupling agent, 9Kg toughening agent, 7Kg lubricant.

[0047] Described a kind of anti-aging polystyrene plastic product is processed according to the following method:

[0048] Add silicon carbide fiber, titanium dioxide, and calcium carbonate into the mixing kettle, mix evenly, then add organic rare earth composite stabilizer, coupling agent, toughening agent and lubricant, continue to stir and mix evenly; then add other materials, stir After 20 minutes, mix thoroughly and evenly to obtain the mixture; then use a twin-screw extruder to extrude and granulate, and use an injection molding machine to process the resulting particles...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
impact strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
Login to View More

Abstract

The present invention relates to the field of plastic products, and specifically relates to an anti-aging polystyrene plastic product; an anti-aging polystyrene plastic product of the present invention, and the present invention discloses a preparation method of a polystyrene product resistant to sunlight aging. Invented and optimized the formula of polystyrene materials, and used an organic rare earth composite stabilizer to improve the anti-sunlight aging performance of the material. This stabilizer can not only meet the processing requirements, but also is non-toxic, efficient, cheap, weather-resistant and Excellent plasticizing performance, certain internal lubrication and coupling compatibilization, which can effectively improve the comprehensive performance of the product.

Description

technical field [0001] The invention relates to the field of daily necessities, in particular to an anti-aging polystyrene plastic product. Background technique [0002] Polystyrene plastic is widely used in optical instruments, chemical industry and daily necessities, and is used to make tea trays, sugar bowls, soap boxes, cigarette boxes, student rulers, combs, etc. Due to its certain air permeability, when made into film products, it can also be used as a good food packaging material. [0003] CN200710156303.2 relates to an antistatic polystyrene composition, a preparation method thereof and a sheet prepared from the composition. An antistatic polystyrene composition, which is prepared by kneading the following components in terms of weight percentage: HIPS polystyrene 65.0-85.0%, polyethylene glycol monomethyl ether methacrylate 8.0% ~28.0%, 3.14~6.78% of hydroxyethyl methacrylate, 1.72~3.97% of sodium perchlorate, 0.0963~0.145% of azobisisobutyronitrile, and 0.92~2.4%...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L25/06C08L67/02C08L53/02C08L55/02C08L29/10C08K13/06C08K9/10C08K3/26C08K7/10C08K3/22C08K5/098
CPCC08L25/06C08L2201/08C08L2205/06C08L2207/04C08L2205/03C08K2003/2241C08K2003/265C08L67/02C08L53/02C08K13/06C08K9/10C08K3/26C08K7/10C08K3/22C08L55/02C08K5/098C08L29/10
Inventor 陈锡明
Owner 浙江美仕达日用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com