Flame-retardant nylon 1010 material and preparation method thereof

A technology of flame-retardant nylon and nylon, which is applied in the field of materials, can solve the problems of low flame retardant addition and high cost, and achieve the effects of improving toughness and strength, strong flame retardancy, and improving mechanical stability

Inactive Publication Date: 2020-03-24
山东祥龙新材料股份有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] CN201711376591, a kind of flame retardant nylon 1012 elastomer and its preparation method discloses the production by direct polymerization, the flame retardant can be more evenly dispersed in the nylon 1012 elastomer, compared with the way of blending modification, the flame retardant The addition amount of combustion agent is few; Yet its flame retardant is the spherical MCA that adopts the particle diameter below 5 microns of targeted nano synergistic technology organic treatment, and its cost is higher, therefore, the present invention intends to adopt a kind of new method, utilizes Low-cost diatomaceous earth achieves high-efficiency flame retardant effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] A flame-retardant nylon 1010 material, which is made up of the following raw materials in parts by weight:

[0025] Nylon 1010110, phosphorous acid 4, catalyst 0.01, pentaerythritol 3, propylene oxide 1.6, diatomaceous earth dispersion 30, cyanoethyl cellulose 2, calcium acetylacetonate 1, diisopropylethanolamine 0.1.

[0026] The catalyst is p-toluenesulfonic acid.

[0027] Described diatomite dispersion liquid is made up of the raw material of following weight part:

[0028] Diatomaceous earth 50, acrylamide 20, urea 1, ammonium persulfate 0.6, calcium stearate 1, ethyl cellulose 3, aluminum dihydrogen phosphate 0.1.

[0029] The preparation method of described diatomite dispersion liquid, comprises the following steps:

[0030] (1) Get ammonium persulfate, join it in the deionized water of 30 times of its weight, stir;

[0031] (2) Mix diatomite and calcium stearate, put it into a sintering furnace, sinter at 270° C. for 50 minutes, cool to normal temperature, and...

Embodiment 2

[0039] A flame-retardant nylon 1010 material, which is made up of the following raw materials in parts by weight:

[0040] Nylon 1010130, phosphorous acid 6, catalyst 0.02, pentaerythritol 5, propylene oxide 2, diatomite dispersion 40, cyanoethyl cellulose 3, calcium acetylacetonate 2, diisopropylethanolamine 0.2.

[0041] The catalyst is p-toluenesulfonic acid.

[0042] Described diatomite dispersion liquid is made up of the raw material of following weight part:

[0043] Diatomaceous earth 60, acrylamide 30, urea 2, ammonium persulfate 1, calcium stearate 2, ethyl cellulose 4, aluminum dihydrogen phosphate 0.2.

[0044] The preparation method of described diatomite dispersion liquid, comprises the following steps:

[0045] (1) Get ammonium persulfate, join in the deionized water of 40 times of its weight, stir;

[0046] (2) Mix diatomite and calcium stearate, put it into a sintering furnace, sinter at 300° C. for 60 minutes, cool to normal temperature, and grind into fine...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
impact strengthaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a flame-retardant nylon 1010 material, which is prepared from the following raw materials in parts by weight: 110 to 130 parts of nylon 1010, 4 to 6 parts of phosphorous acid,0.01 to 0.02 part of a catalyst, 3 to 5 parts of pentaerythritol, 1.6 to 2 parts of epoxypropane, 30 to 40 parts of a diatomite dispersion liquid, 2 to 3 parts of cyanoethyl cellulose, 1 to 2 parts ofcalcium acetylacetonate and 0.1 to 0.2 part of diisopropylethanolamine. According to the invention, the dispersion compatibility between the intercalation filler and the nylon base material is achieved, the mechanical stability of the finished product is further improved, and the composite material is high in flame retardance and excellent in comprehensive performance.

Description

technical field [0001] The invention belongs to the field of materials, and in particular relates to a flame-retardant nylon 1010 material and a preparation method thereof. Background technique [0002] At present, nylon is widely used in machine tools, machinery, electrical insulation protection, lighting equipment, automobile manufacturing, aviation equipment, rail transit, automation control and other industries. In recent years, with the continuous development of high-speed rail, subway, and intelligent machine tools, nylon bellows Higher requirements are required, low temperature resistance requires -50 ℃ ~ -60 ℃, ammonia water, oxalic acid corrosion resistance, higher wear resistance requirements, flame retardant requirements low smoke and halogen-free; [0003] Polymer materials are an important cornerstone of modern industry and high technology, and an important guarantee for the basic industries of the national economy and national security. On the one hand, polyme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L33/26C08L1/28C08K13/06C08K9/10C08K5/21C08K3/32C08K7/26C08K5/1515C08F120/56
CPCC08L77/06C08F120/56C08L2201/02C08L2312/00C08L2205/03
Inventor 马学彬
Owner 山东祥龙新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com