Preparation method of blended silk-like fabric

A silk-like fabric technology, applied in the field of preparation of blended silk-like fabrics, can solve the problems of poor quality of silk-like products, achieve the effects of improving softness and gloss, excellent strength and toughness, and low production cost

Inactive Publication Date: 2020-04-10
宁波太平鸟潮服饰营销有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the deficiencies of the prior art, the present invention provides a method for preparing a blended imitation silk fabric, which has the advantages of being soft and elastic, skin-friendly, smooth and glossy, and solves the problem of the imitation silk produced by the current processing technology. The problem of poor product quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of blended silk-like fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method for a blended silk-like fabric, comprising the following steps:

[0026] S1. Select raw materials: 30 parts of polyester fiber, 20 parts of cotton fiber, 20 parts of mercerized cotton and 10 parts of wool fiber, wherein the cotton fiber is made of long-staple cotton;

[0027] S2. Polyester fiber treatment: carry out alkali reduction treatment on polyester fiber, wash with distilled water after the treatment is completed, put it in a dryer for low-temperature drying after cleaning, and the caustic soda solution used for alkali reduction treatment is hydroxide Sodium solution, the treatment temperature is 25 degrees Celsius, the treatment time is 2 hours, and the reduction rate is 14.6%;

[0028] S3. Cotton fiber treatment: Alkali treatment is carried out on the cotton fiber. After the treatment is completed, it is cleaned with distilled water. After the cleaning is completed, it is placed in a dryer for low-temperature drying. The temperature is 80 ...

Embodiment 2

[0035] A preparation method for a blended silk-like fabric, comprising the following steps:

[0036] S1, select raw materials: 40 parts of polyester fiber, 25 parts of cotton fiber, 25 parts of mercerized cotton and 15 parts of wool fiber, wherein the cotton fiber adopts the fiber of long-staple cotton;

[0037] S2. Polyester fiber treatment: carry out alkali reduction treatment on polyester fiber, wash with distilled water after the treatment is completed, put it in a dryer for low-temperature drying after cleaning, and the caustic soda solution used for alkali reduction treatment is hydroxide Sodium solution, the treatment temperature is 28 degrees Celsius, the treatment time is 2.5 hours, and the reduction rate is 16.5%;

[0038] S3. Cotton fiber treatment: Alkali treatment is carried out on the cotton fiber. After the treatment is completed, it is cleaned with distilled water. After the cleaning is completed, it is placed in a dryer for low-temperature drying. The tempera...

Embodiment 3

[0045] A preparation method for a blended silk-like fabric, comprising the following steps:

[0046] S1, select raw materials: 50 parts of polyester fiber, 30 parts of cotton fiber, 30 parts of mercerized cotton and 20 parts of wool fiber, wherein the cotton fiber adopts the fiber of long-staple cotton;

[0047]S2. Polyester fiber treatment: carry out alkali reduction treatment on polyester fiber, wash with distilled water after the treatment is completed, put it in a dryer for low-temperature drying after cleaning, and the caustic soda solution used for alkali reduction treatment is hydroxide Sodium solution, the treatment temperature is 30 degrees Celsius, the treatment time is 3 hours, and the reduction rate is 17.7%;

[0048] S3. Cotton fiber treatment: Alkali treatment is carried out on the cotton fiber. After the treatment is completed, it is cleaned with distilled water. After the cleaning is completed, it is placed in a dryer for low-temperature drying. The temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a piece of blended silk-like fabric, and relates to the technical field of textiles. The preparation method of the blended silk-like fabric comprises the steps of selecting raw materials, processing polyester fibres, processing cotton fibres, processing mercerized cotton, processing wool fibres, blending, processing a piece of gray cloth, and performing quality detection. The polyester fibres, the cotton fibres, the mercerized cotton and the wool fibres are individually processed before being blended; therefore, performances of the raw materialsare greatly improved; after being blended into a finished product, the fabric is softened; the performance of the finished silk-like fabric is greatly improved; due to addition of the mercerized cotton and the wool fibres, silk-like strength and toughness are greatly improved; due to addition of the cotton fibres, silk-like skin affinity is greatly improved; the gray cloth is processed through silicone oil; therefore, the softness and the glossiness of the cloth are greatly improved; the product has the appearance of silk; furthermore, in terms of the softness and the glossiness, compared withreal silk, the blended silk-like fabric is also just right; in terms of the strength and the toughness, the blended silk-like fabric is better than the real silk; and, compared with the real silk, the preparation cost of the blended silk-like fabric is low.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a method for preparing a blended silk-like fabric. Background technique [0002] Silk fabrics have always represented a noble and high-quality life. The main reason is that the drape and feel of silk fabrics are particularly comfortable, and they are also very skin-friendly when worn, full of light and beauty. However, silk resources are limited, the relative price is relatively high, and the cost performance is not very good. At present, more and more researches are devoted to silk-like fabrics, which have silk-like luster and comfort, low production cost, and abundant raw material sources. However, the current imitation silk processing technology ignores the characteristics of silk fabric itself. Most of the processing technology only uses chemical fiber products to achieve the shape of silk. Such products are often of poor quality, with only the shape of silk but no silk. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/643D06M11/38D06M11/54D06M16/00D06B3/10D06B3/02D06B15/00D02G3/04D06M101/32D06M101/06D06M101/12
CPCD02G3/04D06B3/02D06B3/10D06B15/00D06M11/38D06M11/54D06M15/643D06M16/003D06M2101/06D06M2101/12D06M2101/32D06M2200/50D10B2201/02D10B2211/02D10B2331/04
Inventor 邵新平申亚欣窦倩王冻洋
Owner 宁波太平鸟潮服饰营销有限公司