Water-based cigarette packet laser transfer adhesive

A technology of laser transfer and cigarette pack, applied in the direction of adhesive type, ester copolymer adhesive, etc., to achieve the effect of convenient production, easy acquisition and good market prospect

Inactive Publication Date: 2020-05-08
NANJING WEISAI MEDICAL TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the water-based transfer adhesives currently used in the market have certain defects in product performance and quality, and cannot truly meet the requirements of enterprises in these four aspects.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] This embodiment is a water-based cigarette case laser transfer adhesive, which contains a water-based acrylic emulsion polymer with a solid content of 45 wt%. , pH adjuster, and water-based additives are copolymerized.

[0025] The monomer mixture is formed by mixing ethyl acrylate and propyl acrylate; the emulsifier is an ionic emulsifier, which is benzenesulfonate, and the weight of the emulsifier is 0.4% of the total mass of the monomer mixture; the initiator is potassium persulfate , and its weight is 0.2% of the total mass of the monomer mixture.

[0026] The preparation method is as follows:

[0027] Step 1, according to the formula in claim 2, each raw material is taken for subsequent use;

[0028] Step 2, put deionized water, emulsifier, monomer mixture, and chain transfer agent accounting for 40% of the total weight of deionized water into the emulsification kettle, and start stirring to emulsify for not less than 30 minutes to obtain a pre-emulsion;

[0029...

Embodiment 2

[0033] Embodiment 2: This embodiment is a water-based cigarette package laser transfer adhesive, which contains a water-based acrylic emulsion polymer with a solid content of 45 to 55 wt%. The water-based acrylic emulsion polymer is prepared from a monomer mixture in deionized water, an emulsifier, It is formed by copolymerization under the action of initiator, chain transfer agent, pH regulator and water-based additives.

[0034] The monomer mixture is composed of ethyl acrylate, propyl acrylate, butyl acrylate, isobutyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate, and isobutyl methacrylate; emulsification The agent is an ionic emulsifier, which is polyoxyethylene alkyl ether sulfate, and the weight of the emulsifier is 3.0% of the total mass of the monomer mixture; the initiator is any one of ammonium persulfate, and its weight is 3.0% of the monomer mixture 0.8% of the total mass.

[0035] The preparation method is as follows:

[0036] Step 1, ac...

Embodiment 3

[0043] This embodiment is a water-based cigarette case laser transfer adhesive, which contains a water-based acrylic emulsion polymer with a solid content of 50 wt%. , pH adjuster, and water-based additives are copolymerized.

[0044]The monomer mixture is composed of C2-C4 alkyl acrylate monomers and C1-C4 alkyl methacrylate monomers; the emulsifier is an ionic emulsifier, which is succinic acid monoester sulfonate, polyethylene oxide alkyl The combination of base ether sulfate, and the weight of the emulsifier is 1.7% of the total mass of the monomer mixture; the initiator is potassium persulfate, and its weight is 0.5% of the total mass of the monomer mixture.

[0045] The preparation method is as follows:

[0046] Step 1, according to the formula in claim 2, each raw material is taken for subsequent use;

[0047] Step 2, put deionized water, emulsifier, monomer mixture, and chain transfer agent accounting for 45% of the total weight of deionized water into the emulsifica...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a water-based cigarette packet laser transfer adhesive which comprises a water-based acrylic emulsion polymer with the solid content of 45-55wt%. The laser transfer adhesive hasgood printing adaptability, can enable a laser aluminized layer to be firmly combined with paper, meets the VOC requirement, does not exceed the standard of residual solvents and residual monomers, does not contain o-benzene plasticizers or formaldehyde, is environmentally friendly, is easy in component obtaining and convenient to produce, and has a good market prospect.

Description

technical field [0001] The invention belongs to the field of adhesives, and in particular relates to a water-based laser transfer adhesive for cigarette packs. Background technique [0002] At present, transfer laser cardboard has been widely used as a new type of environmentally friendly packaging material in the field of cigarette packs. Transfer laser cardboard is to use the detachability of the laser aluminum layer to transfer the laser aluminum layer with various laser effects evaporated on the plastic film to the paper through the adhesive to form paper with various aesthetic effects; its process The process includes: (1) Coating release and information coatings on the PET film; (2) Molding the coating to form an anti-counterfeit laser layer; (3) Vacuum aluminum plating on the laser layer; Aluminum-coated film and cardboard are combined; (5) PET substrate film is peeled off to form laser cardboard with laser anti-counterfeiting effect; (6) cigarette outer box is forme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C08F220/18C08F220/14C08F2/26C08F2/30
CPCC08F2/26C08F2/30C08F220/14C08F220/18C09J133/08
Inventor 尹艳洪梁康荣苏芬
Owner NANJING WEISAI MEDICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com