High-toughness and aging-resistant ABS material

An ABS material and anti-aging technology, which is applied in the field of plastics, can solve the problems of poor toughness and aging resistance of ABS plastics, and achieve the effects of easy cracking, improved aging resistance, and improved dispersibility

Inactive Publication Date: 2020-06-02
叶丹平
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In view of the above-mentioned defects in the prior art, the technical problem to be solved by the present invention is to provide a high-toughness anti-aging ABS material, which can effectively solve the problems of poor toughness and aging resistance of ABS plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A high-toughness and aging-resistant ABS material is prepared from the following raw materials in parts by weight: 100 parts of ABS resin and 4.5 parts of alkylated graphene oxide. Weigh ABS and alkylated graphene oxide respectively according to the formula, and add the materials to the hopper after pre-mixing. The temperature of the twin-screw extruder is: 200°C in the first zone, 205°C in the second zone, 201°C in the third zone, and 220°C in the fourth zone. , 5 zone 200 ℃, 6 zone 205 ℃, rotating speed 20rpm, pelletize, obtain high toughness and anti-aging ABS material.

[0035] The preparation method of the alkylated graphene oxide is as follows: 100 mg of graphene oxide is added to 180 mL of sodium hydroxide aqueous solution, and ultrasonic treatment is performed for 30 min at an ultrasonic power of 400 W and an ultrasonic frequency of 20 kHz; then 100 mL of tetraoctyl Ammonium bromide and 5mL 1-iodododecane were stirred and mixed at 80°C for 72h; 30mL chloroform w...

Embodiment 2

[0037] A high-toughness and aging-resistant ABS material is prepared from the following raw materials in parts by weight: 100 parts of ABS resin and 4.5 parts of alkylated reduced graphene oxide. Weigh ABS and alkylated reduced graphene oxide respectively according to the formula, and add the materials to the hopper after pre-mixing. The temperature of the twin-screw extruder is: 200°C in the first zone, 205°C in the second zone, 201°C in the third zone, and 220 in the fourth zone. ℃, five zone 200 ℃, six zone 205 ℃, rotating speed 20rpm, pelletize to obtain high toughness and anti-aging ABS material.

[0038] The preparation method of described alkylation reduction graphene oxide comprises the steps:

[0039] S1 Add 100mg of graphene oxide to 180mL of sodium hydroxide aqueous solution, sonicate for 30min under the conditions of ultrasonic power of 400W and ultrasonic frequency of 20kHz; then add 100mL of tetraoctylammonium bromide and 5mL of 1-iodododecane Stir and mix at 80°C...

Embodiment 3

[0042] A high-toughness and aging-resistant ABS material is prepared from the following raw materials in parts by weight: 100 parts of ABS resin and 4.5 parts of nanocellulose / attapulgite composite material. Weigh ABS and nanocellulose / attapulgite composite materials respectively according to the formula, and put the materials into the hopper after pre-mixing. Zone 220°C, zone 5 200°C, zone 6 205°C, rotating speed 20rpm, pelletize to obtain high toughness and anti-aging ABS material.

[0043] The preparation method of described nanocellulose / attapulgite composite material, comprises the steps:

[0044] I Attapulgite pretreatment

[0045] Add 1.0g of attapulgite to 20mL of water, stir and mix evenly, then add 0.1g of sodium hexametaphosphate, stir and mix evenly; then add 1mL of concentrated sulfuric acid, stir at 60°C for 4h; after filtering, dry the filter residue at 105°C for 24h, that is Obtain pretreated attapulgite; the mass fraction of the concentrated sulfuric acid is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-toughness and aging-resistant ABS material, which comprises the following raw materials by weight: 100 parts of ABS resin, 0.5-5.0 parts of alkylated graphene oxide or alkylated reduced graphene oxide and 1.0-10.0 parts of a nano cellulose / attapulgite composite material. Compared with the prior art, according to the invention, graphene oxide is alkylated by tetraoctyl ammonium bromide and 1-iodododecane, so that the dispersity of graphene oxide in a polypropylene material can be remarkably improved, and the toughness of the ABS material is remarkably optimized; moreover, the nano cellulose / attapulgite composite material is also added, so that the toughness and aging resistance of the ABS material can be further improved.

Description

technical field [0001] The invention belongs to the field of plastics, in particular to a high-toughness anti-aging ABS material. Background technique [0002] ABS resin is a thermoplastic engineering plastic widely used after general plastics such as polypropylene, polyethylene, polystyrene, polyvinyl chloride, etc. Widely used, it has excellent properties such as easy processing, good impact resistance, corrosion resistance, high mechanical strength, good dimensional processing stability, and has the advantages of secondary processing. [0003] The physical and chemical properties of ABS resin materials are very excellent, but the bending strength and compressive strength of ABS materials are relatively poor, which is relatively weak among most plastic materials. The ABS resin material has stable properties and can exist stably in water, inorganic salts and various acids, but it can achieve a better dissolution state in solvents such as ketones, aldehydes and chlorinated ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L1/02C08K9/04C08K3/04C08K9/02C08K3/34
CPCC08K2201/011C08L55/02C08L2201/08C08L1/02C08K9/04C08K3/042C08K9/02C08K3/346
Inventor 叶丹平
Owner 叶丹平
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More