A plasma cladding and cladding technology, which is applied in metal material coating technology, additive manufacturing, additive processing, etc., can solve the problem of difficulty in guaranteeing the bonding strength of the composite interface, high precision requirements for equipment and molds, and difficulty in controlling interface oxidation, etc. problems, to achieve the effect of easy mechanization, meeting the demand for strengthening and toughening, cladding process conditions and air tightness

Active Publication Date: 2020-06-30
NANJING UNIV OF SCI & TECH
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are the following problems in this technology: (1) It is difficult to control the oxidation of the interface; (2) The size of the sample obtained by high-pressure torsion is too small; (3) The precision requirements for equipment and molds are very high, the process is complicated, and the production efficiency is low.
Its limitations are: (1) The pre-rolling treatment work includes multiple operations such as surface cleaning, cutting, argon arc welding sealing, heating, etc. The requirements are high and the production efficiency is low; (2) There are surface cleanliness, sealing Oxidation is difficult to control during hot rolling; (3) It is difficult to guarantee the bonding strength of the composite interface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing heterogeneous material through plasma cladding
  • Method for preparing heterogeneous material through plasma cladding
  • Method for preparing heterogeneous material through plasma cladding

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0045] Example 1: Plasma cladding Al / 7075 aluminum alloy strip heterostructure

[0046] (1) Pretreatment: including substrate pretreatment and cladding powder pretreatment.

[0047] Substrate pretreatment: cutting the high-strength 7075 aluminum alloy into strips with a size of 100mm×20mm×20mm. Then carry out sandblasting (black corundum sand) treatment on 7075 aluminum alloy to remove rust. During sandblasting, the gun is 6cm away from the sample surface, and the sandblasting angle is 80°. After sandblasting, it is blown with cold compressed air; Ultrasonic cleaning for 30 minutes in order to remove oil, dry and set aside.

[0048] Cladding powder pretreatment: sieve the high-toughness Al and high-strength 7075 aluminum alloy powder for the second time, so that the particle size distribution is 80-100 mesh, and the powder shape is spherical or spherical; Keep drying at 150°C for 4 hours in a vacuum drying oven, and it can be turned during the drying process.

[0049] (2) B...

example 2

[0055] Example 2: Plasma cladding Al / 7075 aluminum alloy bulk heterostructure

[0056] (1) Pretreatment: including substrate pretreatment and cladding powder pretreatment.

[0057] Substrate pretreatment: cutting the high-strength 7075 aluminum alloy into blocks with a size of 60mm×40mm×30mm. Then carry out sandblasting (black corundum sand) treatment on 7075 aluminum alloy to remove rust. During sandblasting, the gun is 6cm away from the sample surface, and the sandblasting angle is 80°. After sandblasting, it is blown with cold compressed air; Ultrasonic cleaning for 30 minutes in order to remove oil, dry and set aside.

[0058] Cladding powder pretreatment: sieve the high-toughness Al and high-strength 7075 aluminum alloy powder for the second time, so that the particle size distribution is 80-100 mesh, and the powder shape is spherical or spherical; Keep drying at 150°C for 4 hours in a vacuum drying oven, and it can be turned during the drying process.

[0059] (2) Bot...

example 3

[0065] Example 3: Concave-convex heterogeneous structure of plasma cladding Al / 7075 aluminum alloy

[0066](1) Pretreatment: including substrate pretreatment and cladding powder pretreatment.

[0067] Substrate pretreatment: Cut the high-strength 7075 aluminum alloy into a concave-convex shape with a lower plane size of 45mm×30mm×10mm and three upper convex sizes of 45mm×10mm×10mm (size 1) distributed on the left, middle and right sides. Then carry out sandblasting (black corundum sand) treatment on 7075 aluminum alloy to remove rust. During sandblasting, the gun is 6cm away from the sample surface, and the sandblasting angle is 80°. After sandblasting, it is blown with cold compressed air; Ultrasonic cleaning for 30 minutes in order to remove oil, dry and set aside.

[0068] Cladding powder pretreatment: sieve the high-toughness Al and high-strength 7075 aluminum alloy powder for the second time, so that the particle size distribution is 80-100 mesh, and the powder shape is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of preparation of heterogeneous materials, and particularly relates to a method for preparing a heterogeneous material through plasma cladding. The method includes the four procedures of pre-treatment, bottom layer cladding, multi-layer cladding and solution treatment and aging precipitation, and comprises the specific steps that plasma cladding is utilized, a high-strength material B is cladded on a high-toughness material A matrix, then the high-toughness material A is cladded on a high-strength material B matrix, the above operation is repeated according to a specific lap joint and stacking mode, finally the heterogeneous material controllable and devisable in a three-dimensional direction is obtained through solid treatment and aging precipitation, and finally high strength and high toughness of the material are achieved. According to the method, the multi-layer complex heterogeneous composite material is prepared through the plasma cladding process and solid treatment and aging precipitation, so that impurity doping and interfacial oxidation are effectively avoided, industrial production is easy, the applicable raw material range is wide, cladding patterns and shapes are diversified, and a heterogeneous structure is controllable and devisable in the three-dimensional direction.

Description

technical field [0001] The invention belongs to the field of preparation of heterogeneous materials, and in particular relates to a method for preparing heterogeneous materials by plasma cladding. Background technique [0002] Metal structural materials are widely used in military, industrial, aviation and other fields. People improve the mechanical properties of materials through a variety of strengthening and toughening mechanisms, making them more efficient and safe to use. However, for homogeneous materials, the improvement of strength is often at the expense of plasticity, which severely limits the application and development of structural materials. Therefore, how to achieve both strength and plasticity has become a hot spot and focus in the research of metal structural materials. [0003] Heterogeneous materials are a new type of high-strength and high-toughness materials proposed in recent years. Different from traditional homogeneous materials, it constructs soft...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F3/105C23C24/10B22F3/24C22F1/04B33Y10/00B33Y70/00
CPCC23C24/103B22F3/24C22F1/04B33Y10/00B33Y70/00B22F2003/248B22F10/00B22F10/25B22F10/34B22F10/36B22F10/32Y02P10/25
Inventor 周浩黄家喜高波肖礼容陈雪飞曹阳李玉胜聂金凤
Owner NANJING UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap