Preparation method of titanium-doped iron oxide photo-anode with high photoelectric water decomposition performance

A technology of decomposition performance and iron oxide light, applied in chemical instruments and methods, electrodes, electrolysis process, etc., can solve the problems of high turn-on voltage and low photocurrent density of titanium-doped iron oxide photoelectrode, so as to reduce turn-on voltage and improve Photoelectric water splitting performance and high yield effect

Active Publication Date: 2020-07-03
HUAQIAO UNIVERSITY
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to overcome the deficiencies of the prior art, to provide a method for preparing a titanium-doped iron oxide photoanode with high photoelectric water splitting perf

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of titanium-doped iron oxide photo-anode with high photoelectric water decomposition performance
  • Preparation method of titanium-doped iron oxide photo-anode with high photoelectric water decomposition performance
  • Preparation method of titanium-doped iron oxide photo-anode with high photoelectric water decomposition performance

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A method for preparing a titanium-doped iron oxide photoanode with high photoelectric water splitting performance in this embodiment comprises the following steps:

[0030] 1) 0.61g ferric chloride hexahydrate (FeCl 3 ·6H 2 O) Dissolve in 100mL water, stir to dissolve, then add 0.34g sodium acetate (CH 3 COONa), after continuing to stir and dissolve, adjust the pH to 1.5 with 37% concentrated hydrochloric acid, after stirring for 10min, pour it into a 50mL hydrothermal reaction kettle, take 1×2cm 2 A clean FTO glass of the size is vertically immersed in the mixed solution. The reaction kettle was placed in an oven at 95°C for 3 h. After the reaction, the FTO glass was taken out, washed and dried to obtain a β-FeOOH electrode.

[0031] 2) Prepare a butyl titanate ethanol solution with a volume fraction of 1%. The specific preparation method is as follows: add 40 μL of butyl titanate into 4 mL of ethanol, shake to dissolve. Immerse the β-FeOOH electrode in the butyl ...

Embodiment 2

[0036] The difference between embodiment 2 and embodiment 1 is: 0.61g ferric trichloride hexahydrate (FeCl 3 ·6H 2 O) Dissolve in 100mL water, stir to dissolve, then add 0.34g sodium acetate (CH 3 COONa), after continuing to stir and dissolve, adjust the pH to 1.5 with 37% concentrated hydrochloric acid, after stirring for 10min, pour it into a 50mL hydrothermal reaction kettle, take 1×2cm 2A clean FTO glass of the size is vertically immersed in the mixed solution. The reaction kettle was placed in an oven at 95°C for 6 h. After the reaction, the FTO glass was taken out, washed and dried to obtain a β-FeOOH electrode. Prepare a butyl titanate ethanol solution with a volume fraction of 1%, put the obtained β-FeOOH:Ti electrode into a muffle furnace for roasting, and roast it at a heating rate of 10 °C / min to 750 °C for 15 min to obtain Fe 2 o 3 : Ti electrode. the Fe 2 o 3 : The Ti electrode was immersed in a 50mL hydrothermal kettle containing 10mL of methanol, placed ...

Embodiment 3

[0038] 0.61g ferric chloride hexahydrate (FeCl 3 ·6H 2 O) Dissolve in 100mL water, stir to dissolve, then add 0.21g sodium nitrate (NaNO 3 ), continue stirring and dissolving, adjust the pH to 1.5 with 37% concentrated hydrochloric acid, stir for 10 minutes, pour into a 50mL hydrothermal reaction kettle, take 1×2cm 2 A clean FTO glass of the size is vertically immersed in the mixed solution. The reaction kettle was placed in an oven at 95°C for 3 h. After the reaction, the FTO glass was taken out, washed and dried to obtain a β-FeOOH electrode. Prepare a butyl titanate ethanol solution with a volume fraction of 1%, immerse the β-FeOOH electrode in the butyl titanate solution, take it out after 5s, place it on a flat surface, and let it dry naturally. Put the obtained β-FeOOH:Ti electrode into a muffle furnace and bake it at a heating rate of 10°C / min to 750°C for 15 minutes to obtain Fe 2 o 3 : Ti electrode. the Fe 2 o 3 : The Ti electrode was immersed in a 50mL hydro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a titanium-doped iron oxide photo-anode with a high photoelectric water decomposition performance. The preparation method comprises the following steps:generating beta-FeOOH on a conductive substrate through hydrothermal synthesis, and carrying out butyl titanate solution soaking and heat treatment to obtain a titanium-doped iron oxide (Fe2O3:Ti) photo-anode; then carrying out solvothermal treatment on the obtained titanium-doped iron oxide electrode to obtain Fe2O3:Ti-M; and finally, carrying out hydrothermal treatment on the Fe2O3: Ti-M through an acid solution. After two-step treatment, oxygen vacancies and other surface defects are introduced to the surface of the Fe2O3:Ti photo-anode, the surface hydrophilicity of the Fe2O3:Ti photo-anode is remarkably improved, the photoelectric water decomposition reaction performance of the Fe2O3:Ti photo-anode obtained through the method is remarkably improved, and the titanium-doped iron oxidephoto-anode has high application value in the future industrial aspect.

Description

technical field [0001] The invention belongs to the technical field of new energy materials, and in particular relates to a preparation method of a titanium-doped iron oxide photoanode with high photoelectric water splitting performance. Background technique [0002] In the field of photocatalytic water splitting, iron oxide (Fe 2 o 3 ) photoanodes have attracted extensive attention from researchers due to their wide light absorption range, good stability, low cost and non-toxicity. However, Fe 2 o 3 Poor conductivity and short lifetime of photogenerated carriers lead to short diffusion distance of photogenerated holes, resulting in low photocurrent density. Metal ions (such as Ti 4+ ) doping improves its electrical conductivity, which can increase the photocurrent density to a certain extent. In addition, Fe 2 o 3 There are a large number of surface states on the surface, and the surface charge recombination is serious, which makes the surface water oxidation reacti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C25B1/04C25B11/06B01J23/745
CPCB01J23/745B01J35/0033C25B1/04C25B1/55C25B11/051C25B11/091Y02E60/36
Inventor 肖静冉詹国武周树锋
Owner HUAQIAO UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap