A belt and magnetic wave technology, applied in magnetic therapy, clothing belts, magnetic fields generated by permanent magnets, etc., can solve the problems of neglecting tourmaline's textile performance and comfort, improve circulation, help absorb nutrients, and improve respiratory organs. effect of function
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0026] A preparation method of a magnetic wave health-care body shaping belt: comprising the following steps:
[0027] S1. Production of tourmaline fiber: Put the tourmaline stone in a ball mill and grind it for 14 hours, take it out and add 1 times the quality of vegetable oil, carry out 10°C cold air current crushing for 3 hours, pass through a 180-mesh sieve to obtain tourmaline slurry, After high-voltage electrostatic spraying penetrates into the pores of fiber raw materials, tourmaline fibers are obtained.
[0028] The vegetable oil is seabuckthorn fruit oil and orange oil, and the mass ratio is 1:1.6;
[0029] The jet mill is a flat jet mill, and the handling capacity is 48kg / h;
[0030] The fiber raw material includes modal fiber;
[0031] The flow rate of the high-voltage electrostatic spray is 0.1mL / h, and the voltage is 25kV;
[0032] S2. Put the above-mentioned tourmaline fiber, banana fiber, golden vine fiber, and seaweed fiber in a refining solution at a temper...
Embodiment 2
[0036] A preparation method of a magnetic wave health-care body shaping belt: comprising the following steps:
[0037] S1. Production of tourmaline fiber: put the tourmaline stone in a ball mill and grind it for 20 hours, take it out and add 3 times the quality of vegetable oil, carry out 20°C cold air current crushing for 5 hours, and pass through a 200-mesh sieve to obtain tourmaline slurry. After high-voltage electrostatic spraying penetrates into the pores of fiber raw materials, tourmaline fibers are obtained.
[0038] Described vegetable oil is pomegranate seed oil;
[0039] The jet mill is a flat jet mill with a processing capacity of 110kg / h;
[0040] Described fiber raw material comprises in the bamboo charcoal fiber;
[0041] The high-voltage electrostatic spray flow rate is 1.6mL / h, and the voltage is 40kV;
[0042] S2. Refining the above-mentioned tourmaline fiber, banana fiber, golden vine fiber, and seaweed fiber in a refining solution at a temperature of 120°...
Embodiment 3
[0046] A preparation method of a magnetic wave health-care body shaping belt: comprising the following steps:
[0047] S1. Production of tourmaline fiber: Put the tourmaline stone in a ball mill and grind it for 17 hours, then take it out and add 2 times the quality of vegetable oil to carry out 15°C cold air current crushing for 4 hours, and pass through a 200-mesh sieve to obtain tourmaline slurry. After high-voltage electrostatic spraying penetrates into the pores of fiber raw materials, tourmaline fibers are obtained.
[0048] The vegetable oil is seabuckthorn fruit oil and orange oil, with a mass ratio of 1 to 1.3;
[0049] The jet mill is a flat jet mill with a processing capacity of 80kg / h;
[0050] The fiber raw material comprises mushroom fiber;
[0051] The flow rate of the high-voltage electrostatic spray is 1.4mL / h, and the voltage is 30kV;
[0052] S2. Refining the above-mentioned tourmaline fiber, banana fiber, golden vine fiber, and seaweed fiber in a refinin...