Coated iron oxide black pigment and preparation method thereof
A technology of iron oxide black and coating type, which is applied in the direction of chemical instruments and methods, inorganic pigment treatment, fibrous fillers, etc., can solve the problems of fading, limit the use range of iron oxide black, discoloration, etc., and achieve stable performance and particle size The effect of narrow range and uniform particle size
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0023]Example 1
[0024]A method for preparing coated iron oxide black includes the following steps:
[0025](1) Add 1kg of iron oxide black filter cake and 2kg of water into the reaction vessel, stir evenly, and at the same time open the steam valve to raise the temperature to 85°C, and keep stirring, the stirring speed is 200rpm;
[0026](2) Prepare the additive aqueous solution: add 30g sodium carboxymethyl cellulose, 10g polyvinyl alcohol, 40g calcium lignosulfonate and 20g sodium hexametaphosphate into the reaction solution, add 1kg of water and stir evenly to obtain the additive aqueous solution; Add the aqueous additive solution to a reaction vessel containing iron oxide black, stir evenly, add the above-mentioned uniformly stirred slurry to a ball mill, and use a wear-resistant ceramic ball with a diameter of 20 mm for grinding. The ball mill speed is 500 rpm and the ball milling time is 5 hours. The material ratio is 5:1, and the iron oxide black dispersion liquid is prepared;
[0027]...
Example Embodiment
[0029]Example 2
[0030]A method for preparing coated iron oxide black includes the following steps:
[0031](1) Add 1kg of iron oxide black filter cake and 2kg of water into the reaction vessel, stir evenly, and at the same time open the steam valve to raise the temperature to 85°C, and keep stirring, the stirring speed is 200rpm;
[0032](2) Prepare additive aqueous solution: add 50g sodium carboxymethyl cellulose, 20g polyvinyl alcohol, 80g calcium lignosulfonate and 50g sodium hexametaphosphate into the reaction solution, add 4kg water and stir evenly to obtain the additive aqueous solution; Add the aqueous additive solution to a reaction vessel containing iron oxide black, stir evenly, add the above-mentioned uniformly stirred slurry to a ball mill, and use a wear-resistant ceramic ball with a diameter of 20 mm for grinding. The ball mill speed is 800 rpm, and the ball milling time is 5 hours. The material ratio is 10:1 to obtain iron oxide black dispersion;
[0033](3) Heat the iron oxide...
Example Embodiment
[0035]Example 3
[0036]A method for preparing coated iron oxide black includes the following steps:
[0037](1) Add 1kg of iron oxide black filter cake and 2kg of water into the reaction vessel, stir evenly, and at the same time open the steam valve to raise the temperature to 85°C, and keep stirring, the stirring speed is 200rpm;
[0038](2) Prepare additive aqueous solution: add 50g sodium carboxymethyl cellulose, 20g polyvinyl alcohol, 80g calcium lignosulfonate and 50g sodium hexametaphosphate into the reaction solution, add 4kg water and stir evenly to obtain the additive aqueous solution; Add the aqueous additive solution to a reaction vessel containing iron oxide black, stir evenly, add the above-mentioned uniformly stirred slurry to a ball mill, and use a wear-resistant ceramic ball with a diameter of 20 mm for grinding. The ball mill speed is 800 rpm, and the ball milling time is 5 hours. The material ratio is 10:1 to obtain iron oxide black dispersion;
[0039](3) Heat the iron oxide...
PUM
Property | Measurement | Unit |
---|---|---|
Diameter | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap