A kind of waterproof mortar and its preparation method and application

A waterproof mortar and water reducing agent technology, applied in the field of waterproof mortar and its preparation, can solve the problems of long setting time, compressive/flexural strength and viscosity reduction, high bleeding, etc., to achieve high compressive and flexural strength, Strong scratch resistance and low bleeding effect

Active Publication Date: 2022-06-24
FUJIAN KZJ NEW MATERIALS CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Based on this, it is necessary to provide a waterproof mortar, which aims to solve the technical problems of the waterproof mortar using recycled materials in the prior art with reduced compressive / flexural strength and viscosity, high bleeding and long setting time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of waterproof mortar and its preparation method and application
  • A kind of waterproof mortar and its preparation method and application
  • A kind of waterproof mortar and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0092] The present invention also provides a method for preparing the above waterproof mortar, wherein the liquid material components and the powder material components are mixed and stirred evenly; wherein,

[0093] Liquid components include:

[0094] Styrene-acrylate copolymer emulsion: 20-50 parts;

[0095] Vinyl acetate-ethylene copolymer emulsion: 10-40 parts;

[0096] Workability improver: 10-20 parts;

[0097] Film-forming aids: 1 to 5 parts;

[0098] Defoamer: 0.3 to 0.9 parts;

[0099] Water: 15 to 60 parts;

[0100] Powder components include:

[0101] Portland cement: 10 to 40 parts;

[0102] Aluminate cement: 5 to 40 parts;

[0103] Gypsum: 5 to 17 parts;

[0104] Glass sand: 25 to 50 parts;

[0105] Glass powder: 5 to 15 parts;

[0106] Water reducing agent: 0.1 to 0.5 parts;

[0107] Stabilizer: 0.05 to 0.3 parts;

[0108] Coagulant: 0.05~0.5 part;

[0109] Fiber: 0.1 to 1 part.

[0110] Compared with the prior art, the preparation method of the wate...

Embodiment 1

[0117] The liquid component and powder component of waterproof mortar are prepared in the following proportions, wherein,

[0118] Liquid components: 500g styrene-acrylate copolymer emulsion, 100g vinyl acetate-ethylene copolymer emulsion, 100g sodium polyacrylate derivative, 5g triterpenoids, 50g propylene glycol butyl ether, 9g polysiloxane organics, water 236g;

[0119] Powder components: ordinary Portland cement 150g, aluminate cement 300g, gypsum 80g, granulated blast furnace slag powder 30g, (70-140) mesh glass sand 280g, 200 mesh glass powder 120g, calcite powder 40g, naphthalene series Water reducing agent 4g, higher fatty acid 5g, hydroxypropyl methylcellulose (8000 viscosity) 0.7g, Brunei gum 0.3g, potassium silicate 0.3g, crystal nucleus nano-enhancer 0.3g, sodium gluconate 0.1g, basalt Mineral fiber 1g, polypropylene fiber 1.5g;

[0120] Take 500g of liquid material component and 1000g of powder material component and mix and stir evenly to obtain waterproof mort...

Embodiment 2

[0122] The liquid component and powder component of waterproof mortar are prepared in the following proportions, wherein,

[0123] Liquid ingredients: 450g styrene-acrylate copolymer emulsion, 120g vinyl acetate-ethylene copolymer emulsion, 130g sodium polyacrylate derivative, 6g triterpenoids, 40g propylene glycol butyl ether, 8g polysiloxane organics, water 246g;

[0124] Powder components: ordinary Portland cement 200g, aluminate cement 250g, gypsum 70g, granulated blast furnace slag powder 40g, (70-140) mesh glass sand 300g, 200 mesh glass powder 100g, calcite powder 40g, naphthalene series Water reducer 4g, zinc stearate 5g, hydroxypropyl methylcellulose (8000 viscosity) 0.7g, Brunei gum 0.3g, potassium silicate 0.2g, crystal nucleus nano-enhancer 0.3g, sodium hexametaphosphate 0.2 g. Basalt mineral fiber 1g, polypropylene fiber 1.5g;

[0125] Take 400g of liquid material components and 1000g of powder material components and mix and stir evenly to obtain waterproof mor...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a waterproof mortar, which includes a liquid material component and a powder material component. In parts by weight, the liquid material component includes styrene-acrylate copolymer emulsion: 20-50 parts; vinyl acetate-ethylene copolymer emulsion: 10-40 parts; workability improver: 10-20 parts; film-forming aid: 1-5 parts; defoamer: 0.3-0.9 parts; water: 15-60 parts; powder components include ordinary silicic acid Salt cement: 10-40 parts; aluminate cement: 5-40 parts; gypsum: 5-17 parts; glass sand: 25-50 parts; glass powder: 5-15 parts; water reducer: 0.1-0.5 parts; Stabilizer: 0.05 to 0.3 parts; coagulation regulator: 0.05 to 0.5 parts; fiber: 0.1 to 1 part. The waterproof mortar in the present invention also has the properties of good mortar cohesion, appropriate setting time, high compressive and flexural strength, low bleeding, uniform appearance, no precipitation and strong scratch resistance. In addition, the present invention Waterproof mortar has good construction performance under different external ambient temperatures.

Description

technical field [0001] The invention relates to the technical field of polymer cement-based materials, in particular to a waterproof mortar and a preparation method thereof. Background technique [0002] At present, with the development of polymer cement-based materials, polymer cement waterproof mortar has been widely used in many projects. Good and many other advantages, with the gradual application of various recycled materials, the research on the product formulation of related polymer cement waterproof mortars is also gradually deepening, but at present, various polymer cement waterproof mortars using recycled materials still have compression resistance in the market. The problems of reduced flexural strength and viscosity, high bleeding and long setting time limit the further application of polymer cement waterproof mortars in polymer cement-based materials. SUMMARY OF THE INVENTION [0003] Based on this, it is necessary to provide a waterproof mortar, which aims t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/14C04B111/27
CPCC04B28/14C04B2111/27C04B2201/50C04B24/2641C04B24/2623C04B24/00C04B24/023C04B24/42C04B7/02C04B7/32C04B18/141C04B14/22C04B14/28C04B2103/302C04B24/085C04B24/383C04B24/38C04B12/04C04B24/10C04B14/4656C04B16/0633C04B2103/0068C04B22/16C04B22/126C04B24/06
Inventor 陈周鹏邱岳涛胡俊华王永定苏伟东温宾煌
Owner FUJIAN KZJ NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com