Visible-light-responsive photocatalytic antibacterial healing-promoting hydrogel and preparation method thereof
A healing hydrogel and photocatalytic technology, applied in medical science, bandages, etc., can solve the problems of tissue damage, no reduction in infection, etc., achieve the effect of simple method, reduce bacterial infection, and promote wound healing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0034]Example 1:
[0035]It is weighed 20 mg collagen in a 2 ml of 1% acetic acid solution, and thoroughly stirred it to dissolve, and then the pH was adjacent to neutral sodium hydroxide solution, and the collagen solution was obtained. It is weighted 40 mg of alginate sodium alginate in 2 ml of deionized water, thoroughly stirring to dissolve, and sodium alginate solution. Under stirring, the alginate solution is added to the collagen solution, thoroughly stirred, and the collagen-alginate solution is obtained. The graphite phase breened carbon nanchi was dispersed in deionized water, and 30 min was tested for 30 min, and a uniform 0.6 mg / ml graphite phase nitrocarbon nano-dispersion was dispersed, and 1 ml of carbon nitride nano sheet dispersion and collagen-alginate Solution mixing (graphite phase nitrocarbon nanofin is used as 1% of collagen and the total mass of sodium alginate), stirring at normal temperature for 2 h, centrifugation, inserted into the mold, stand, add 6ml 1 wt...
Example Embodiment
[0036]Example 2:
[0037]It is weighed 20 mg collagen in a 2 ml of 1% acetic acid solution, and thoroughly stirred it to dissolve, and then the pH was adjacent to neutral sodium hydroxide solution, and the collagen solution was obtained. It is weighted 40 mg of alginate sodium alginate in 2 ml of deionized water, thoroughly stirring to dissolve, and sodium alginate solution. Under stirring, the alginate solution is added to the collagen solution, thoroughly stirred, and the collagen-alginate solution is obtained. The graphite phase-propelled carbon nanchi was dispersed in deionized water, and 30 min was tested for 30 min. Solution mixing (graphite phase nitrocarbon nanofer is used as 2% of collagen and the total mass of sodium alginate), stirring at normal temperature for 2 h, centrifugation, pour into the mold, stand, add 6ml 1 wt% CaCl2The solution crosslinked for 1 h, and then washed three-time visible light response to the photocatalytic antibacterial initiaturized hydrophilic gel ...
Example Embodiment
[0038]Example 3:
[0039]It is weighed 20 mg collagen in a 2 ml of 1% acetic acid solution, and thoroughly stirred it to dissolve, and then the pH was adjacent to neutral sodium hydroxide solution, and the collagen solution was obtained. It is weighted 40 mg of alginate sodium alginate in 2 ml of deionized water, thoroughly stirring to dissolve, and sodium alginate solution. Under stirring, the alginate solution is added to the collagen solution, thoroughly stirred, and the collagen-alginate solution is obtained. The graphite phase breened carbon nanchi was dispersed in deionized water, and 30 min was tested for 30 min. Solution mixing (graphite phase breened carbon nanofer is used as 3% of collagen and the total mass of sodium alginate), stirring at normal temperature for 2 h, centrifugation, inserted into the mold, stand, add 6 ml 1 wt% CaCl2The solution crosslinked for 1 h, and then washed three-time visible light response to the photocatalytic antibacterial initiaturized hydrophili...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap